Heterogeneous Multi-Phase Grains Improving the Strength-Ductility Balance in Warm-Rolled Fe-18Mn-3Ti Steel.

The thermal properties, microstructure, and mechanical properties of Fe-18Mn-3Ti (wt%) were investigated, focusing on the effects of different heat-treatment processes. Results revealed that the 450 °C warm-rolling sample (450 WR) exhibited promising mechanical properties. Specifically, this sample displayed a yield strength of 988 MPa, an ultimate tensile strength of 1052 MPa, and total elongation of 15.49%. Consequently, a favorable strength-ductility balance was achieved. The strain-hardening ability surpassed that of the cold rolling sample (CR). Microstructure analysis indicated the simultaneous occurrence of dynamic equilibrium between grain deformation and re-crystallization because of the co-influence of thermal and strain in the warm rolling process. This desirable mechanical property was attributed to the presence of a multi-phase (α-martensite, austenite, and ε-martensite) and heterogeneous microstructure. The improvement of ultimate tensile strength was based on grain refinement, grain co-deformation, and the transformation-induced plasticity (TRIP) effect in the early stage of plastic deformation (stage Ⅰ). The improvement of ultimate elongation (TEL) was ascribed to the TRIP effect in the middle stage of plastic deformation (stage Ⅱ).

A Cable-Stayed Honeycomb Superstructure to Improve the Stability of Li-Rich Materials via Inhibiting Interlaminar Lattice Strain.

In layered Li-rich materials, over stoichiometric Li forms an ordered occupation of LiTM6 in transition metal (TM) layer, showing a honeycomb superstructure along [001] direction. At the atomic scale, the instability of the superstructure at high voltage is the root cause of problems such as capacity/voltage decay of Li-rich materials. Here a Li-rich material with a high Li/Ni disorder is reported, these interlayer Ni atoms locate above the honeycomb superstructure and share adjacent O coordination with honeycomb TM. These Ni─O bonds act as cable-stayed bridge to the honeycomb plane, and improve the high-voltage stability. The cable-stayed honeycomb superstructure is confirmed by in situ X-ray diffraction to have a unique cell evolution mechanism that it can alleviate interlaminar lattice strain by promoting in-plane expansion along a-axis and inhibiting c-axis stretching. Electrochemical tests also demonstrate significantly improved long cycle performance after 500 cycles (86% for Li-rich/Li half cell and 82% for Li-rich/Si-C full cell) and reduced irreversible oxygen release. This work proves the feasibility of achieving outstanding stability of lithium-rich materials through superstructure regulation and provides new insights for the development of the next-generation high-energy-density cathodes.

Exploring the Underlying Correlation between the Structure and Ionic Conductivity in Halide Spinel Solid-State Electrolytes with Neutron Diffraction.

The development of cutting-edge solid-state electrolytes (SSEs) entails a deep understanding of the underlying correlation between the structure and ionic conductivity. Generally, the structure of SSEs encompasses several interconnected crystal parameters, and their collective influence on Li+ transport can be challenging to discern. Here, we systematically investigate the structure-function relationship of halide spinel LixMgCl2+x (2 ≥ x ≥ 1) SSEs. A nonmonotonic trend in the ionic conductivity of LixMgCl2+x SSEs has been observed, with the maximum value of 8.69 × 10-6 S cm-1 achieved at x = 1.4. The Rietveld refinement analysis, based on neutron diffraction data, has revealed that the crystal parameters including cell parameters, Li+ vacancies, Debye-Waller factor, and Li-Cl bond length assume diverse roles in influencing ionic conductivity of LixMgCl2+x at different stages within the range of x values. Besides, mechanistic analysis demonstrates Li+ transport along three-dimensional pathways, which primarily governs the contribution to ionic conductivity of LixMgCl2+x SSEs. This study has shed light on the collective influence of crystal parameters on Li+ transport behaviors, providing valuable insights into the intricate relationship between the structure and ionic conductivity of SSEs.

Porous Single-crystalline Centimeter-sized α-Al2 O3 Monoliths for Selective and Durable Non-oxidative Dehydrogenation of Ethane.

Alpha alumina (α-Al2 O3 ) are inert materials with outstanding thermal, chemical and mechanical stability. Herein, we fabricate porous single-crystalline (PSC) α-Al2 O3 monoliths at centimeter scale to endow them with high catalytic activity while maintaining their stability. We reduce PSC α-Al2 O3 monoliths to create oxygen vacancies in lattice and stabilize them by the ordered lattice to construct unsaturated Al-O coordination structures for enhancing the catalytic activity. The generation of oxygen vacancy at 18e wyckoff position contributes to the unsaturated Al-O coordination. As a case study, we demonstrate the outstanding performance with conversion (≈34 %) and selectivity (≈95 %) toward non-oxidative dehydrogenation of ethane to ethylene at 700 °C. We achieve the outstanding performance without obvious degradation even after a continuous operation over 1000 hours at 700 °C.

A neutron beam monitor based on ceramic gas electron multiplier with high spatial resolution for low flux measurements.

Neutron scattering instruments play an important role in studying the inner structure of materials. A neutron beam monitor is a detector commonly used in a neutron scattering instrument. The detection efficiency for most neutron beam monitors is quite low (10-4-10-6). However, in some experiments with a low neutron flux, such as small angle neutron scattering (SANS) and inelastic neutron scattering experiments, a neutron beam monitor with a higher detection efficiency (∼1% for thermal neutrons) is required to reduce the duration of the experiment. To meet this requirement, a ceramic gas electron multiplier-based neutron beam monitor equipped with a 1 µm 10B4C neutron converter was developed in this study. Its performance was determined both experimentally and in simulations. The detection efficiency in the wavelength range of 1.8-5.5 Å was measured experimentally and was confirmed by the simulation results. An algorithm based on event selection and position reconstruction was developed to improve the spatial resolution to about 1 mm full-width-half-maximum. The wavelength spectrum was measured in beamline 20 (BL20) and agreed well with the results obtained using a commercial monitor. The maximum counting rate was 1.3 MHz. The non-uniformity over the whole 100 × 100 mm2 active area was determined to be 1.4%. Due to the excellent performance of this monitor, it has been used in several neutron instruments, such as the SANS and the High-Energy Direct-Geometry Inelastic Spectrometer instruments in the China spallation neutron source.