In situ melt electrospun polycaprolactone/Fe3O4 nanofibers for magnetic hyperthermia.

Magnetic fibrous membrane used to generate heat under the alternating magnetic field (AMF) has attracted wide attention due to their application in magnetic hyperthermia. However, there is not magnetic fibrous membrane prepared by melt electrospinning (e-spinning) which is a solvent-free, bio-friendly technology. In this work, polycaprolactone (PCL)/Fe3O4 fiber membrane was prepared by melt e-spinning and using homemade self-powered portable melt e-spinning apparatus. The hand-held melt e-spinning apparatus has a weight of about 450 g and a precise size of 24 cm in length, 6 cm in thickness and 13 cm in height, which is more portable for widely using in the medical field. The PCL/Fe3O4 composite fibers with diameters of 4-17 µm, are very uniform. In addition, the magnetic composite fiber membrane has excellent heating efficiency and thermal cycling characteristics. The results indicated that self-powered portable melt e-spinning apparatus and PCL/Fe3O4 fiber membrane may provide an attractive way for hyperthermia therapy.

Flexible TiO2/PVDF/g-C3N4 Nanocomposite with Excellent Light Photocatalytic Performance.

As the world faces water shortage and pollution crises, the development of novel visible light photocatalysts to purify water resources is urgently needed. Over the past decades, most of the reported photocatalysts have been in powder or granular forms, creating separation and recycling difficulties. To overcome these challenges, a flexible and recyclable heterostructured TiO2/polyvinylidene fluoride/graphitic carbon nitride (TiO2/PVDF/g-C3N4) composite was developed by combining electrospinning, sintering and hydrothermal methods. In the composite, PVDF was used as a support template for removing and separating the photocatalyst from solution. Compared with pure TiO2, the TiO2/PVDF/g-C3N4 composite exhibited the extended light capture range of TiO2 into the visible light region. The photogenerated carriers were efficiently transferred and separated at the contact interface between TiO2 and g-C3N4 under visible light irradiation, which consequently increased the photocatalytic activity of the photocatalyst. In addition, the flexible composites exhibited excellent self-cleaning properties, and the dye on the photocatalysts was completely degraded by the as-prepared materials. Based on the intrinsic low cost, recyclability, absorption of visible light, facile synthesis, self-cleaning properties and good photocatalytic performances of the composite, the photocatalyst is expected to be used for water treatment.