Catalysis of the Oxygen-Evolution Reaction in 1.0 M Sulfuric Acid by Manganese Antimonate Films Synthesized via Chemical Vapor Deposition.

Manganese antimonate (MnySb1-yOx) electrocatalysts for the oxygen-evolution reaction (OER) were synthesized via chemical vapor deposition. Mn-rich rutile Mn0.63Sb0.37Ox catalysts on fluorine-doped tin oxide (FTO) supports drove the OER for 168 h (7 days) at 10 mA cm-2 with a time-averaged overpotential of 687 ± 9 mV and with >97% Faradaic efficiency. Time-dependent anolyte composition analysis revealed the steady dissolution of Mn and Sb. Extended durability analysis confirmed that Mn-rich MnySb1-yOx materials are more active but dissolve at a faster rate than previously reported Sb-rich MnySb1-yOx alloys.

Probing the Degradation Chemistry and Enhanced Stability of 2D Organolead Halide Perovskites.

Recent work on quasi-2D Ruddlesden-Popper phase organolead halide perovskites has shown that they possess many interesting optical and physical properties. Most notably, they are significantly more stable when exposed to moisture when compared to the typical 3D perovskite methylammonium lead iodide (MAPI); direct evidence for the chemical source of this stability remains elusive, however. Here, we present a detailed study of the superior moisture stability of a quasi-2D Ruddlesden-Popper perovskite, n-butylammonium methylammonium lead iodide (nBA-MAPI), compared to that of MAPI, and examine a simple, yet efficient, methodology to improve the stability of MAPI devices through the application of a thin layer of nBA-MAPI to the surface. By employing a variety of analytical techniques (photoluminescence, time-of-flight secondary ion mass spectrometry, cyclic voltammetry, X-ray diffraction) we determine that the improved stability of Ruddlesden-Popper perovskites is a consequence of a unique degradation pathway which produces a passivating surface layer, composed of increasingly stable phases of the 2D perovskite, via disproportionation. Our work establishes that this protective material isolates the bulk of the perovskite from a newly identified hydration layer which is found to accumulate at the C60/perovskite interface of full devices, slowing further hydrolysis reactions that would damage the device. As MAPI devices degrade quickly without any protection, a surface treatment of nBA-MAPI is an efficient way to delay device deterioration by creating an artificial 2D surface layer that similarly inhibits interaction with the hydration layer.