Optimizing Flame Retardancy and Durability of Melamine-Formaldehyde/Solid-Urban-Waste Composite Panels.

In our previous study, an innovative method for sterilization, inertization, and valorization of the organic fraction of municipal solid waste (OFMSW), to be recycled in the production of composite panels, was developed. In this follow-up work, the effects of fire retardants on fire performance, durability, and the mechanical properties of the composite panels based on OFMSW and melamine-formaldehyde resin were investigated. The performance of panels without fire retardants (control panels) was compared to panels containing either mono-ammonium phosphate (PFR) or aluminium trihydrate (ATH) at a mass fraction of 1% and 10% (modified panels). As shown by cone calorimetry, the total heat released was already low (about 31 MJ/m2 at 50 kW/m2) in the control panels, further decreased in the modified panels with the addition of fire retardants, and reached the lowest value (about 1.4 MJ/m2) with 10% mass fraction of PFR. Hence, the addition of fire retardants had a beneficial effect on the response to fire of the panels; however, it also reduced the mechanical properties of the panels as measured by flexural tests. The deterioration of the mechanical properties was particularly obvious in panels containing 10% mass fraction of fire retardants, and they were further degraded by artificial accelerated weathering, carried out by boiling tests. Ultimately, the panels containing PFR at a mass fraction of 1% offered the best balance of fire resistance, durability, and mechanical performance within the formulations investigated in this study.

Performance and Failure Mechanism of Fire Barriers in Full-Scale Chair Mock-ups.

The effectiveness and the failure mechanism of fire barriers in residential upholstered furniture were investigated by full-scale flaming tests on upholstered chair mock-ups. Six commercial fire barriers were tested in this study. Fire barriers were screened for (1) the presence of elements that are typically used in fire retardants and, (2) the presence of targeted fire retardants. For each fire barrier, triplicate flammability tests were run on chair mock-ups where polyurethane foam and polyester fiber fill were used as the padding materials, and each chair component was fully wrapped with the fire barrier of choice and a polypropylene cover fabric. The ignition source was an 18 kW square propane burner, impinging on the top surface of the seat cushion for 80 s. Results showed all six fire barriers reduced the peak heat release rate (as much as ≈ 64 %) and delayed its occurrence (up to ≈ 19 min) as compared to the control chair mock-ups. The heat release rate remained at a relatively low plateau level until liquid products (generated by either melting or pyrolysis of the padding material) percolated through the fire barrier at the bottom of the seat cushion and ignited, while the fire barrier was presumably intact. The flaming liquid products dripped and quickly formed a pool fire under the chair and the peak heat release rate occurred shortly thereafter. Ultimately, the ignition of the percolating liquid products at the bottom of the seat cushion was identified as the mechanism triggering the failure of the fire barrier.

A novel application of silicone-based flame-retardant adhesive in plywood.

A silicone-based elastomer filled with vinyl-silane treated aluminum hydroxide was used to replace conventional polyurethane-based adhesive to provide a flame-retardant adhesive for plywood. The shear strength and fire performance of such a silicone-based (SI) adhesive glued plywood (SI/plywood) were investigated and compared to those of the polyurethane-based (PU) adhesive glued plywood (PU/plywood). The shear strength of the SI/plywood [(0.92 ± 0.09) MPa] was about 63% lower than that of the PU/plywood at room temperature, but it was less sensitive to water (62% reduction for the PU/plywood and 30% reduction for the SI/plywood after hot-water immersion at 63 °C for 3 h). The fire performance of plywood was assessed by a simulated match-flame ignition test (Mydrin test), lateral ignition and flame spread test, cone calorimetry, and thermocouple measurements. With a higher burn-though resistance and thermal barrier efficiency, and lower flame spread and heat release rate, the SI/plywood exhibited a superior fire-resistance and reaction-to-fire performance and improved fire-resistance as compared to the PU/plywood. The SI adhesive generated an inorganic protective layer on the sample surface that visibly suppressed glowing and smoldering of the plywood during combustion. The SI adhesive was also combined and reinforced with cellulosic fabric (CF) or glass fabric (GF) to prepare composite plywood (SI/CF/plywood and SI/GF/plywood) with improved fire performance. The cone calorimetry and thermocouple measurements indicated that the use of CF or GF in SI/CF/plywood and SI/GF/plywood, respectively, suppressed the delamination and cracking of the composite plywood and promoted the formation of an effective thermal barrier during smoldering and flaming combustion. Particularly, the SI/GF/plywood exhibited the most effective fire barrier with no crack formation, and the lowest heat release rate among the plywood types investigated in this study.

Effect of Ammonium Polyphosphate to Aluminum Hydroxide Mass Ratio on the Properties of Wood-Flour/Polypropylene Composites.

Two halogen-free inorganic flame retardants, ammonium polyphosphate (APP) and aluminum hydroxide (ATH) were added to wood-flour/polypropylene composites (WPCs) at different APP to ATH mass ratios (APP/ATH ratios), with a constant total loading of 30 wt % (30% by mass). Water soaking tests indicated a low hygroscopicity and/or solubility of ATH as compared to APP. Mechanical property tests showed that the flexural properties were not significantly affected by the APP/ATH ratio, while the impact strength appeared to increase with the increasing ATH/APP ratio. Cone calorimetry indicated that APP appeared to be more effective than ATH in reducing the peak of heat release rate (PHRR). However, when compared to the neat WPCs, total smoke release decreased with the addition of ATH but increased with the addition of APP. Noticeably, WPCs containing the combination of 20 wt % APP and 10 wt % ATH (WPC/APP-20/ATH-10) showed the lowest PHRR and total heat release in all of the formulations. WPCs combustion residues were analyzed by scanning electron microscopy, laser Raman spectroscopy, and Fourier transform infrared spectroscopy (FTIR). Thermogravimetric analysis coupled with FTIR spectroscopy was used to identify the organic volatiles that were produced during the thermal decomposition of WPCs. WPC/APP-20/ATH-10 showed the most compact carbonaceous residue with the highest degree of graphitization.

Smoldering and Flame Resistant Textiles via Conformal Barrier Formation.

A durable and flexible silicone-based backcoating (halogen free) is applied to the backside of an otherwise smoldering-prone and flammable fabric. When exposed to fire, cyclic siloxanes (produced by thermal decomposition of the backcoating) diffuse through the fabric in the gas phase. The following oxidation of the cyclic siloxanes forms a highly conformal and thermally stable coating that fully embeds all individual fibers and shields them from heat and oxidation. As a result, the combustion of the fabric is prevented. This is a novel fire retardant mechanism that discloses a powerful approach towards textiles and multifunctional flexible materials with combined smoldering/flaming ignition resistance and fire-barrier properties.

Revealing the interface in polymer nanocomposites.

The morphological characterization of polymer nanocomposites over multiple length scales is a fundamental challenge. Here, we report a technique for high-throughput monitoring of interface and dispersion in polymer nanocomposites based on Förster resonance energy transfer (FRET). Nanofibrillated cellulose (NFC), fluorescently labeled with 5-(4,6-dichlorotriazinyl)-aminofluorescein (FL) and dispersed into polyethylene (PE) doped with Coumarin 30 (C30), is used as a model system to assess the ability of FRET to evaluate the effect of processing on NFC dispersion in PE. The level of energy transfer and its standard deviation, measured by fluorescence spectroscopy and laser scanning confocal microscopy (LSCM), are exploited to monitor the extent of interface formation and composite homogeneity, respectively. FRET algorithms are used to generate color-coded images for a real-space observation of energy transfer efficiency. These images reveal interface formation at a nanoscale while probing a macroscale area that is large enough to be representative of the entire sample. The unique ability of this technique to simultaneously provide orientation/spatial information at a macroscale and nanoscale features, encoded in the FRET signal, provides a new powerful tool for structure-property-processing investigation in polymer nanocomposites.

Flame retardant behavior of polyelectrolyte-clay thin film assemblies on cotton fabric.

Cotton fabric was treated with flame-retardant coatings composed of branched polyethylenimine (BPEI) and sodium montmorillonite (MMT) clay, prepared via layer-by-layer (LbL) assembly. Four coating recipes were created by exposing fabric to aqueous solutions of BPEI (pH 7 or 10) and MMT (0.2 or 1 wt %). BPEI pH 10 produces the thickest films, while 1 wt % MMT gives the highest clay loading. Each coating recipe was evaluated at 5 and 20 bilayers. Thermogravimetric analysis showed that coated fabrics left as much as 13% char after heating to 500 degrees C, nearly 2 orders of magnitude more than uncoated fabric, with less than 4 wt % coming from the coating itself. These coatings also reduced afterglow time in vertical flame tests. Postburn residues of coated fabrics were examined with SEM and revealed that the weave structure and fiber shape in all coated fabrics were preserved. The BPEI pH 7/1 wt % MMT recipe was most effective. Microcombustion calorimeter testing showed that all coated fabrics reduced the total heat release and heat release capacity of the fabric. Fiber count and strength of uncoated and coated fabric are similar. These results demonstrate that LbL assembly is a relatively simple method for imparting flame-retardant behavior to cotton fabric. This work lays the foundation for using these types of thin film assemblies to make a variety of complex substrates (foam, fabrics, etc.) flame resistant.