RESUMO
The structure of porous silica particles can be reorganized without alteration of the particle size and shape by the process of pseudomorphic transformation. Partial pseudomorphic transformation leads to ordered mesoporous silica with bimodal pore size distributions and bottleneck pores. Compared to the classical pathways of mesoporous silica synthesis, pseudomorphic transformation implies less compromise between pore structure and particle shape, while enabling the preparation of complex pore architectures.
RESUMO
In this work a comprehensive study on a new active packaging obtained by a hybrid organic-inorganic coating with antimicrobial properties was carried out. The packaging system based on polylactic acid was realised by sol-gel processing, employing tetraethoxysilane as a precursor of the inorganic phase and polyvinyl alcohol as the organic component, and incorporating natamycin as the active agent. Films with different organic-inorganic ratios (in a range between 1:19 and 1:4) were prepared, and the amount of antimycotic entrapped was found to be modulated by the sol composition, and was between 0.18 and 0.25mg/dm(2). FTIR microspectroscopic measurements were used to characterise the prepared coatings. The antifungal properties of the films were investigated against mould growth on the surface of commercial semi-soft cheese. The release of natamycin from the films to ethanol 50% (v/v) was studied by means of HPLC UV-DAD. The maximal level released was about 0.105 mg/dm(2), which is far below the value allowed by legislation.