Development of ZTA (80% Al2O3/20% ZrO2) pre-sintered blocks for milling in CAD/CAM systems.

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% Al2O3 and 20% ZrO2 was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C. After cooling and holder gluing, a stereolithography (STL) file was designed and uploaded to manufacture disk-shaped specimens projected to comply with ISO 6872:2015. Seventy specimens were produced through machining of the blocks, samples were sintered at 1600 °C and two-sided polished. Half of the samples were subjected to accelerated autoclave hydrothermal aging (20h at 134 °C and 2.2 bar). Immediate and aged samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Optical and mechanical properties were assessed by reflectance tests and by biaxial flexural strength test, Vickers indentation and fracture toughness, respectively. Samples produced by machining presented high density and smooth surfaces at SEM evaluation with few microstructural defects. XRD evaluation depicted characteristic peaks of alpha alumina and tetragonal zirconia and autoclave aging had no effect on the crystalline spectra of the composite. Optical and mechanical evaluations demonstrated a high masking ability for the composite and a characteristic strength of 464 MPa and Weibull modulus of 17, with no significant alterations after aging. The milled composite exhibited a hardness of 17.61 GPa and fracture toughness of 5.63 MPa m1/2, which remained unaltered after aging. The synthesis of ZTA blocks for CAD-CAM was successful and allowed for the milling of disk-shaped specimens using the grinding method of the CAD-CAM system. ZTA composite properties were unaffected by hydrothermal autoclave aging and present a promising alternative for the manufacture of infrastructures of fixed dental prostheses.

Reliability and Failure Mode of Ti-Base Abutments Supported by Narrow/Wide Implant Systems.

To assess the reliability and failure modes of Ti-base abutments supported by narrow and wide-diameter implant systems. Narrow (Ø3.5 × 10 mm) and wide (Ø5 × 10 mm) implant systems of two different manufacturers with internal conical connections (16°) and their respective Ti-base abutments (3.5 and 4.5 mm) were evaluated. Ti-base abutments were torqued to the implants, standardized metallic maxillary incisor crowns were cemented, and step stress accelerated life testing of eighteen assemblies per group was performed in three loading profiles: mild, moderate, and aggressive until fracture or suspension. Reliability for missions of 100,000 cycles at 100 and 150 N was calculated, and fractographic analysis was performed. For missions at 100 N for 100,000 cycles, both narrow and wide implant systems exhibited a high probability of survival (≥99%, CI: 94-100%) without significant differences. At 150 N, wide-diameter implants presented higher reliability (≥99%, CI: 99-100%) compared to narrow implants (86%, CI: 61-95%), with no significant differences among manufacturers. Failure mode predominantly involved Ti-base abutment fractures at the abutment platform. Ti-base abutments supported by narrow and wide implant systems presented high reliability for physiologic masticatory forces, whereas for high load-bearing applications, wide-diameter implants presented increased reliability. Failures were confined to abutment fractures.

Hydrothermal aging affects the three-dimensional fit and fatigue lifetime of zirconia abutments.

OBJECTIVE: Evaluate the effect of aging using two different methods on the three-dimensional fit of zirconia abutments at the implant-abutment connection and estimate the probability of survival of anterior crowns supported by straight and 17-degree angled abutments. MATERIALS AND METHODS: Two different zirconia abutment designs, straight and 17-degree angled abutments (n = 63/group), were evaluated in the current study. The abutments were randomly allocated into three experimental groups according to laboratory aging condition (134°C, 2.2 bar, 20 h): (i) control, (ii) autoclave aging, and (iii) hydrothermal reactor aging. Crystalline content was determined by X-Ray diffraction (XRD) and Raman spectroscopy, and microstructure was analyzed using field-emission gun scanning electron microscope (FEG-SEM). Implant-abutment volume misfit was determined in the straight abutments by micro-computed tomography using the silicone replica technique. For fatigue testing, abutments were torqued to the implants and connected to standardized maxillary incisor zirconia crowns. The assemblies were subjected to step-stress accelerated life testing (SSALT) in water until fracture or suspension. The use level probability Weibull curves and probability of survival for a mission of 50,000 cycles at 50, 100, 150 and 200 N were calculated and plotted. Fractured samples were analyzed using a stereomicroscope and scanning electron microscope. RESULTS: The crystalline spectra depicted a zirconia system primarily composed of the tetragonal phase. Laboratory aging yielded a 20%- and 37%-increase in the monoclinic content for abutments aged in autoclave and hydrothermal reactor relative to control, respectively. A fully crystalline matrix with a regular grain size was observed in the FEG-SEM for control abutments, with a considerable presence of intergranular defects. While autoclave aging triggered no significant alteration to the microstructure, defect population was reduced after hydrothermal reactor aging. Control abutments presented a significantly higher volume misfit (2.128 ± 0.54 mm3) relative to aged abutments using autoclave (1.244 ± 0.48 mm3) or hydrothermal reactor (1.441 ± 0.41 mm3). The beta (ß) values indicated that failures were predominantly controlled by material strength rather than fatigue damage accumulation for all groups, except for straight control abutments. Irrespective of aging, the probability of survival of straight and angled zirconia abutments was up to 95% (95-100%) at 50 and 100 N. A 50N-increase in the load resulted in wider range of survival estimate, with straight autoclave abutments percentage significantly lower probability of survival (77%) than angled hydrothermal reactor abutments (99%). At 200N, angled hydrothermal reactor (97%) or autoclave (82%) aged abutments demonstrated the highest probability of survival, angled control (71%) and straight hydrothermal reactor (69%) abutments intermediate values, and straight autoclave (23%) and control (7%) abutments the lowest estimate. The failure mode predominantly involved abutment and/or abutment screw fracture for both straight and angled abutments. CONCLUSIONS: Hydrothermal aging significantly influenced volume misfit, as well as the probability of survival of zirconia abutments at higher loads for both angled and straight abutments.