Impact of optical fiber-based photo-activation on dental composite polymerization.

OBJECTIVES: The study aimed to introduce a novel two-step optical fiber-based photo-activation of dental resin-based composites (RBCs) for reducing polymerization shrinkage stress (PSS). METHODS: Proposed protocol design - in the first step, two flexible plastic optical fibers connected to a dental light curing unit (LCU), were used as light guides inserted into the filling to initiate low-irradiance polymerization from within; in the second step, fibers were extracted and remaining voids were filled with RBC, followed by conventional high-irradiance curing to finalize polymerization. Three bulk-fill RBCs were tested (Beautifil-Bulk Restorative, Filtek Bulk-fill Posterior, Tetric PowerFill) using tooth cavity models. Three non-invasive examination techniques were employed: Digital Holographic Interferometry, Infrared Thermography, and Raman spectroscopy for monitoring model deformation, RBC temperature change, and degree of conversion (DC), respectively. A control group (for each examined RBC) underwent conventional photo-activation. RESULTS: The experimental protocol significantly reduced model deformation by 15 - 35 %, accompanied by an 18 - 54 % reduction in RBC temperature change, emphasizing the impact of thermal shrinkage on PSS. Real-time measurements of deformation and temperature provided indirect insights into reaction dynamics and illuminated potential mechanisms underlying PSS reduction. After a 24-hour dark-storage period, DC outcomes comparable to conventional curing were observed, affirming the clinical applicability of the method. CONCLUSIONS: Protocol involving the use of two 1.5 mm fibers in the first step (300 mW/cm2 x 10 s), followed by a second conventional curing step (1000 mW/cm2 x 10 s), is recommended to achieve the desired PSS reduction, while maintaining adequate DC and ensuring efficient clinical application. CLINICAL SIGNIFICANCE: Obtained PSS reduction offers promise in potentially improving the performance of composite restorations. Additionally, leveraging the flexibility of optical fibers improves light guide approach for restorations on posterior teeth. Meanwhile, implementation in clinical practice is easily achievable by coupling the fibers with commercial dental LCUs using the provided plastic adapter.

Polymerization Shrinkage of Short Fiber Reinforced Dental Composite Using a Confocal Laser Analysis.

The purpose of this study was to investigate the polymerization shrinkage of short fiber reinforced composite (SFRC) using a multicolor confocal displacement laser that can measure the polymerization shrinkage with high accuracy. The three types of SFRCs used in this study were XD (Ever X Flow Dentin), XB (Ever X Flow Bulk), and XP (EverX Posterior). In addition, CF (Clearfil majesty ES Flow) with hybrid type filler was used as a control. The measured values of the final polymerization shrinkage rate and amount of polymerization shrinkage rate when the polymerization shrinkage rate became constant (less than 0.1 µm/s) were approximated for all SFRCs. XP had a large aspect ratio of glass fiber filler and showed a significant difference from XD with a small aspect ratio (p < 0.05). There was no significant difference in the measured value of time when the polymerization contraction reached a constant speed (0.1 µm/s or less) for all SFRCs (p > 0.05). There was no significant difference in the measured values of polymerization shrinkage rate after the polymerization shrinkage reached a constant rate for all SFRCs (p > 0.05). These results show that glass fiber with large aspect ratio can alleviate polymerization shrinkage stress. The polymerization behavior of SFRC was found to be dependent on the amount of glass fiber filler, aspect ratio, and orientation.