A Novel Synthesized 1D Nanobelt-like Cobalt Phosphate Electrode Material for Excellent Supercapacitor Applications.

In the present report, we synthesized highly porous 1D nanobelt-like cobalt phosphate (Co2P2O7) materials using a hydrothermal method for supercapacitor (SC) applications. The physicochemical and electrochemical properties of the synthesized 1D nanobelt-like Co2P2O7 were investigated using X-ray diffraction (XRD), X-ray photoelectron (XPS) spectroscopy, and scanning electron microscopy (SEM). The surface morphology results indicated that the deposition temperatures affected the growth of the 1D nanobelts. The SEM revealed a significant change in morphological results of Co2P2O7 material prepared at 150 °C deposition temperature. The 1D Co2P2O7 nanobelt-like nanostructures provided higher electrochemical properties, because the resulting empty space promotes faster ion transfer and improves cycling stability. Moreover, the electrochemical performance indicates that the 1D nanobelt-like Co2P2O7 electrode deposited at 150 °C deposition temperature shows the maximum specific capacitance (Cs). The Co2P2O7 electrode prepared at a deposition temperature 150 °C provided maximum Cs of 1766 F g-1 at a lower scan rate of 5 mV s-1 in a 1 M KOH electrolyte. In addition, an asymmetric hybrid Co2P2O7//AC supercapacitor device exhibited the highest Cs of 266 F g-1, with an excellent energy density of 83.16 Wh kg-1, and a power density of 9.35 kW kg-1. Additionally, cycling stability results indicate that the 1D nanobelt-like Co2P2O7 material is a better option for the electrochemical energy storage application.

Co2P2O7 Microplate/Bacterial Cellulose-Derived Carbon Nanofiber Composites with Enhanced Electrochemical Performance.

Nanocrystalline Co2P2O7 and carbon nanofiber (Co2P2O7/CNFs) composites with enhanced electrochemical performance were obtained by calcination after a hydrothermal process with NH4CoPO4∙H2O/bacterial cellulose precursors under an argon atmosphere. SEM images showed that the CNFs were highly dispersed on the surfaces of Co2P2O7 microplates. The diagonal size of the Co2P2O7 plates ranged from 5 to 25 µm with thicknesses on a nanometer scale. Notably, with the optimal calcining temperature, the Co2P2O7/CNFs@600 material has higher specific micropore and mesopore surface areas than other samples, and a maximal specific capacitance of 209.9 F g-1, at a current density of 0.5 A g-1. Interestingly, CNF composite electrodes can enhance electrochemical properties, and contribute to better electrical conductivity and electron transfer. EIS measurements showed that the charge-transfer resistance (Rct) of the CNF composite electrodes decreased with increasing calcination temperature. Furthermore, the Co2P2O7/CNF electrodes exhibited higher energy and power densities than Co2P2O7 electrodes.