Effect of surface sealant on the color stability and whiteness index of single-shade resin composites after staining and bleaching.

Objectives: The aim of the current study was to evaluate the effect of polishing systems and surface sealant on the color stability and whiteness index of single-shade resin composites after staining and bleaching. Materials and Methods: Three single-shade (Omnichroma, Charisma Diamond One, Zenchroma) and one multi-shade (Filtek Z250) materials were tested. From each resin composite, 40 specimens were prepared. The specimens were divided into 4 subgroups (n = 10) according to the surface treatments: 1-step polishing, 1-step + Biscover LV, 2-step polishing, and 2-step polishing + Biscover LV. Color differences (ΔE00) were calculated after being immersed in the coffee solution for 12 days. After the staining, the specimens were immersed in a whitening mouthrinse (Crest-3D White) for 12 hours. Whiteness index differences (∆WID = WID after staining - WID after bleaching) values were recorded. The generalized linear model was used for analysis (p < 0.05). Results: The lowest and highest ΔE00 values were found for Zenchroma and Charisma Diamond One respectively. Sealed groups indicated higher ΔE00 values than nonsealed groups with significant differences (p = 0.008). The lowest and highest ΔWID values were found for Zenchroma and Charisma Diamond One respectively. Sealed groups indicated lower ΔWID values than nonsealed groups with significant differences (p = 0.022). Conclusions: The use of surface sealant increased the discoloration and showed less whiteness change in resin materials. When the 1-step was compared with the 2-step polishing, the effects on the color stability and whiteness index values of the resin materials were similar.

Improving Self-Healing Dental-Restorative Materials with Functionalized and Reinforced Microcapsules.

Dental resin composites are widely used in clinical settings but often face longevity issues due to the development and accumulation of microcracks, which eventually lead to larger cracks and restoration failure. The incorporation of microcapsules into these resins has been explored to introduce self-healing capability, potentially extending the lifespan of the restorations. This study aims to enhance the performance of self-healing dental resins by optimizing the microcapsules-resin matrix physicochemical interactions. Poly(urea-formaldehyde) (PUF) microcapsules were reinforced with melamine and subsequently subjected to surface functionalization with 3-aminopropyltriethoxysilane (APTES) and (3-mercaptopropyl)trimethoxysilane (MPTMS). Additionally, microcapsules were functionalized with a bilayer approach, incorporating tetraethyl orthosilicate (TEOS) with either APTES or MPTMS. X-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA) confirmed an increased Si:C ratio from 0.006 to 0.165. The functionalization process did not adversely affect the structure of the microcapsules or their healing agent volume. Compared to PUF controls, the functionalized microcapsules demonstrated enhanced healing efficiency, with TEOS/MPTMS-functionalized microcapsules showing the highest performance, showing a toughness recovery of up to 35%. This work introduces a novel approach to functionalization of microcapsules by employing advanced silanizing agents such as APTES and MPTMS, and pioneering bilayer functionalization protocols through their combination with TEOS.

Enhancing Esthetics in Direct Dental Resin Composite: Investigating Surface Roughness and Color Stability.

Dental restorations must replicate the natural appearance of teeth while ensuring biocompatibility and durability. This study evaluated the surface characteristics and color stability of three dental composites-Herculite Ultra XRV, G-ænial A'CHORD, and Omnichroma-exposed to acidic beverages (red wine, black coffee, and Coca-Cola). Sixty disk-shaped specimens were prepared, polished, and immersed in these beverages. Surface roughness was assessed using profilometry and SEM analysis, hydrophobicity via contact angle analysis, and surface charge through streaming potential measurements. Color stability was evaluated using a spectrophotometer, and the pH levels of the solutions were recorded. Results showed that Herculite Ultra XRV had the highest mean contact angle (79.46° ± 6.52), indicating superior hydrophobicity, while Omnichroma had the lowest (64.94° ± 3.08), indicating more hydrophilicity. Significant color changes were observed, especially in black coffee, with ∆E values indicating notable discoloration. The acidic pH of the solutions increased surface roughness and color changes. Statistical analyses confirmed significant increases in surface roughness and color change for all composites, with the nanohybrid resin composite showing the greatest variability. These findings highlight the need for dental restorative materials with enhanced resistance to acidic environments to improve the longevity and esthetics of dental treatments.

Exceptional bone remodeling over composite restoration in the management of external root resorption: A case report.

A 65-year-old Caucasian male was referred to an endodontic specialist practice in a private clinic in December 2019 for the management of an asymptomatic, radiolucent lesion located at the cervical level of the distal root of his right lower first molar, noticed during a routine periapical radiograph. After an accurate evaluation with cone-beam computed tomography (CBCT), the subgingival lesion was diagnosed as a supracrestal external cervical resorption (ECR), with a circumferential spread ⩽90°, confined to dentine without pulp involvement. The lesion was treated with the following sequence: (1) a full flap accessed the ECR, (2) the granulomatous tissue was removed from the root area, (3) the cavity was refreshed and filled with a well-refined and polished resin composite, (4) the flap was sutured at the cemento-enamel junction. A mandibular CBCT scan was performed before treatment, right after treatment, and 3 years postoperatively. Compared to the 3-year posttreatment CBCT scan, the immediate posttreatment one, revealed the absence of bone loss and an unexpected coronal bone remodeling with new bone formation over the treated lesion.

Microscopic and Color Changes in Direct Dental Restorative Composite Resins upon Immersion in Beverages: Characterization by Scanning Electron Microscopy (SEM) and Energy-Dispersive X-ray Spectroscopy (EDS).

This study aimed to evaluate the staining sensitivity and surface changes in recent composite resins (Herculite Ultra XRV (Kerr, Bolzano, Italy), G-ænial A'CHORD (GC Corp, Tokyo, Japan), and Omnichroma (Yamaguchi, Japan)) when exposed to common beverages such as coffee, red wine, and Coca-Cola. A total of 60 disk-shaped specimens were prepared from three different resin composites (n = 20 each). The specimens were exposed to coffee, red wine, and Coca-Cola for 10 days. Color measurements were taken using a spectrophotometer, and surface morphology and elemental composition were analyzed using SEM and EDS. The SEM and EDS analyses revealed significant changes in the surface morphology and elemental composition of the composites after immersion. Coffee and wine caused significant surface degradation, whereas Coca-Cola resulted in the greatest degree of surface and elemental variations. Color changes (ΔE = 4 ± 0.52) were most notable in Coca-Cola for Herculite Ultra XRV (Kerr, Italy), in red wine for G-ænial A'CHORD (GC Corp, Japan) (ΔE = 12.51 ± 0.38), and in coffee for Omnichroma (Yamaguchi, Japan) (ΔE = 10.85 ± 1.03). The tested beverages significantly affected both the surface condition and the chemical composition of the resin at the surface level. These findings highlight the importance of understanding the effects of common dietary beverages on dental composites.

Novel lignin α-O-4 derived hydrogen donors in CQ-based photoinitiating systems for dental resins.

The purpose of this work is to explore the properties of the lignin-derived amine-free photoinitiating systems (PISs) during the curing process. Four novel hydrogen donors (HD1, HD2, HD3, and HD4) derived from lignin α-O-4 structural were designed and synthesized by simple methods, and their low C-H bond dissociation energies on methylene were determined by molecular orbitals theory. Four experimental groups using CQ (camphorquinone)/HD PIs formulated with Bis-GMA/TEGDMA (70 w%/30 w%) were compared to CQ/EDB (ethyl 4-dimethylamino benzoate) system. The photopolymerization profiles and double bond conversion rate was tracked by FTIR experiments; the color bleaching ability of the samples and color aging test assay were performed using color indexes measurements; The cytotoxicity of the samples was also compared to EDB related systems. All of the experimental groups with new HDs were compared to the control group with EDB by statistical analysis. Compared to CQ/EDB system, new lignin-derived hydrogen donors combined with CQ showed comparable or even better performances in polymerization initiation to form resin samples, under a blue dental LED in air. Excellent color bleaching property was observed with the new HDs. Aging tests and cytotoxicity examination of the resin were performed, indicating the new lignin compounds to be efficient hydrogen donors for amine-free CQ-based photo-initiating system. Novel lignin α-O-4 derived hydrogen donors are promising for further usage in light-curing materials.

Preparation of Al-doped mesoporous silica spheres (Al-MSSs) for the improvement of mechanical properties and aging resistance of dental resin composites.

OBJECTIVE: The purpose of this study was to synthesize Al-doped mesoporous silica spheres (Al-MSSs) and evaluate the effect of them as functional fillers on the mechanical properties and aging resistance of dental resin composites. METHODS: Al-MSSs were prepared by a two-step method. The effect of Al-MSSs on the performance of the composites was evaluated using neat resin matrix, commercial composites 3M Z350XT and samples containing mesoporous silica spheres (MSSs) and nonporous silica spheres (NSSs) as control. The neat resin matrix consisted of resin monomer (Bisphenol A glycerolate dimethacrylate/triethylene glycol dimethacrylate, 49.5/49.5, wt%) and photoinitiator (camphor quinone/Ethyl-4-dimethylaminobenzoate, 0.2/0.8, wt%). The mechanical properties (flexural strength, flexural modulus, compressive strength and microhardness) of them were evaluated by a universal testing machine and microhardness tester. The mechanical stabilities of the prepared composites in wet environment were evaluated by immersing them in deionized water at 37 °C. In addition, we evaluated the effect of Al-MSSs on other properties of the dental resin composites such as polymerization shrinkage, degree of conversion, curing depth, contact angle, water sorption and solubility according to ISO 4049: 2019. RESULTS: The synthesized Al-MSSs possessed good dispersibility with an average particle size of about 505 ± 16 nm. The mechanical properties of resin composites gradually increased with the increase of the loading amounts of inorganic fillers. The reinforcing effect of Al-MSSs was similar to that of MSSs and better than that of the NSSs groups at the same filler loading. After aging in deionized water at 37 °C for 30 days, the mechanical properties of all resin composites decreased. However, the decrease percentage of the composites filled with Al-MSSs was significantly lower than the other groups, indicating that the stability of the dental composites in wet environments was significantly improved by the Al-MSSs fillers. Furthermore, Al-MSSs had no obvious influence on the biocompatibility and other properties of dental resins. SIGNIFICANCE: The prepared Al-MSSs could effectively improve the mechanical properties and aging resistance without sacrificing other physic-chemical properties of dental resin composites.

Optimization of functionally graded solid-network TPMS meta-biomaterials.

The current study enhances the performance of solid-network triply periodic minimal surface (TPMS) cellular materials through using cell size grading along with the Taguchi method. Cell size grading is a novel technique used to control the size of pores and the surface area without changing the relative density. In this context, experimental compression testing was conducted on six distinct geometries of cell size graded TPMS structures (Diamond, Fischer-Koch S, Gyroid, IWP, Primitive, and Schoen-F-RD) manufactured with dental resin using a masked stereolithography (MSLA) printer. The findings indicated that mean total energy absorption was greater for smaller initial cell sizes (4 and 6 mm) compared to larger sizes (12 mm). Consistent patterns were also observed with respect to final cell sizes. Upon examination of the stress-strain relationships between D and I-WP, it is evident that D exhibits a higher initial peak stress point. However, subsequent to a significant decline, it exhibits a tremendous degree of volatility before recovering. Conversely, I-WP demonstrated greater stability throughout the experiments, with a notably greater maximum stress effect. A significant influence was observed from the initial cell size on stress, with larger sizes leading to a reduction in absorbed energy. The acquired results serve as an essential basis for the identification of optimized designs that may be implemented to enhance the structures' durability.

Evaluating mechanical and surface properties of zirconia-containing composites: 3D printing, subtractive, and layering techniques.

This study assessed the monotonic and fatigue flexural strength (FS), elastic modulus (E), and surface characteristics of a 3D printed zirconia-containing resin composite compared to subtractive and conventional layering methods. Specimens, including discs (n = 15; Ø = 15 mm × 1.2 mm) and bars (n = 15; 14 × 4 × 1.2 mm), were prepared and categorized into three groups: 3D printing (3D printing - PriZma 3D Bio Crown, Makertech), Subtractive (Lava Ultimate blocks, 3M), and Layering (Filtek Z350 XT, 3M). Monotonic tests were performed on the discs using a piston-on-three-balls setup, while fatigue tests employed similar parameters with a frequency of 10 Hz, initial stress at 20 MPa, and stress increments every 5000 cycles. The E was determined through three-point-bending test using bars. Surface roughness, fractographic, and topographic analyses were conducted. Statistical analyses included One-way ANOVA for monotonic FS and roughness, Kruskal-Wallis for E, and Kaplan-Meier with post-hoc Mantel-Cox and Weibull analysis for fatigue strength. Results revealed higher monotonic strength in the Subtractive group compared to 3D printing (p = 0.02) and Layering (p = 0.04), while 3D Printing and Layering exhibited similarities (p = 0.88). Fatigue data indicated significant differences across all groups (3D Printing < Layering < Subtractive; p = 0.00 and p = 0.04, respectively). Mechanical reliability was comparable across groups. 3D printing and Subtractive demonstrated similar E, both surpassing Layering. Moreover, 3D printing exhibited higher surface roughness than Subtractive and Layering (p < 0.05). Fractographic analysis indicated that fractures initiated at surface defects located in the area subjected to tensile stress concentration. A porous surface was observed in the 3D Printing group and a more compact surface in Subtractive and Layering methods. This study distinguishes the unique properties of 3D printed resin when compared to conventional layering and subtractive methods for resin-based materials. 3D printed shows comparable monotonic strength to layering but lags behind in fatigue strength, with subtractive resin demonstrating superior performance. Both 3D printed and subtractive exhibit similar elastic moduli, surpassing layering. However, 3D printed resin displays higher surface roughness compared to subtractive and layering methods. The study suggests a need for improvement in the mechanical performance of 3D printed material.

Ionic Liquid-Based Silane for SiO2 Nanoparticles: A Versatile Coupling Agent for Dental Resins.

The current longevity of dental resins intraorally is limited by susceptibility to acidic attacks from bacterial metabolic byproducts and vulnerability to enzymatic or hydrolytic degradation. Here, we demonstrate synthesizing an ionic liquid-based antibiofilm silane effective against Streptococcus mutans, a major caries pathogen. Furthermore, we incorporate this silane into dental resins, creating antibiofilm- and degradation-resistant materials applicable across resin types. FTIR, UV-vis, and NMR spectroscopy confirmed the synthesis of the expected ionic liquid-based silane. The characterization of SiO2 after the silanization indicated the presence of the silane and how it interacted with the oxide. All groups achieved a degree of conversion similar to that found for commercial resin composites immediately and after two months of storage in water. The minimum of 2.5 wt % of silane led to lower softening in solvent than the control group (GCTRL) (p < 0.05). While the flexural strength indicated a lower value from 1 wt % of silane compared to GCTRL (p < 0.05), the ultimate tensile strength did not indicate differences among groups (p > 0.05). There was no difference within groups between the immediate and long-term tests of flexural strength (p > 0.05) or ultimate tensile strength (p > 0.05). The addition of at least 5 wt % of silane reduced the viability of S. mutans compared to GCTRL (p < 0.05). The fluorescence microscopy analysis suggested that the higher the silane concentration, the higher the amount of bacteria with membrane defects. There was no difference among groups in the cytotoxicity test (p > 0.05). Therefore, the developed dental resins displayed biocompatibility, proper degree of conversion, improved resistance against softening in solvent, and stability after 6 months of storage in water. This material could be further developed to produce polymeric antimicrobial layers for different surfaces, supporting various potential avenues in developing novel biomaterials with enhanced therapeutic characteristics using ionic liquid-based materials.

A Review on the Current State of Microcapsule-Based Self-Healing Dental Composites.

Resin-based dental composites, commonly used in dentistry, offer several advantages including minimally invasive application, esthetically pleasing appearance, and good physical and mechanical properties. However, these dental composites can be susceptible to microcracks due to various factors in the complex oral environment. These microcracks can potentially lead to clinical restoration failure. Conventional materials and methods are inadequate for detecting and repairing these microcracks in situ. Consequently, incorporating self-healing properties into dental composites has become a necessity. Recent years have witnessed rapid advancements in self-healing polymer materials, drawing inspiration from biological bionics. Microcapsule-based self-healing dental composites (SHDCs) represent some of the most prevalent types of self-healing materials utilized in this domain. In this article, we undertake a comprehensive review of the most recent literature, highlighting key insights and findings related to microcapsule-based SHDCs. Our discussion centers particularly on the preparation techniques, application methods, and the promising future of self-healing microcapsules in the field of dentistry.

Impact of bisphenol A and analogues eluted from resin-based dental materials on cellular and molecular processes: An insight on underlying toxicity mechanisms.

Dental resin systems, used for artificial replacement of teeth and their surrounding structures, have gained popularity due to the Food and Drug Administration's (FDA) recommendation to reduce dental amalgam use in high-risk populations and medical circumstances. Bisphenol A (BPA), an endocrine-disrupting chemical, is an essential monomer within dental resin in the form of various analogues and derivatives. Leaching of monomers from resins results in toxicity, affecting hormone metabolism and causing long-term health risks. Understanding cellular-level toxicity profiles of bisphenol derivatives is crucial for conducting toxicity studies in in vivo models. This review provides insights into the unique expression patterns of BPA and its analogues among different cell types and their underlying toxicity mechanisms. Lack of a consistent cell line for toxic effects necessitates exploring various cell lines. Among the individual monomers, BisGMA was found to be the most toxic; however, BisDMA and BADGE generates BPA endogenously and found to elicit severe adverse reactions. In correlating in vitro data with in vivo findings, further research is necessary to classify the elutes as human carcinogens or xenoestrogens. Though the basic mechanisms underlying toxicity were believed to be the production of intracellular reactive oxygen species and a corresponding decline in glutathione levels, several underlying mechanisms were identified to stimulate cellular responses at low concentrations. The review calls for further research to assess the synergistic interactions of co-monomers and other components in dental resins. The review emphasizes the clinical relevance of these findings, highlighting the necessity for safer dental materials and underscoring the potential health risks associated with current dental resin systems.

Dental biomaterials redefined: molecular docking and dynamics-driven dental resin composite optimization.

BACKGROUND: Dental resin-based composites are widely recognized for their aesthetic appeal and adhesive properties, which make them integral to modern restorative dentistry. Despite their advantages, adhesion and biomechanical performance challenges persist, necessitating innovative strategies for improvement. This study addressed the challenges associated with adhesion and biomechanical properties in dental resin-based composites by employing molecular docking and dynamics simulation. METHODS: Molecular docking assesses the binding energies and provides valuable insights into the interactions between monomers, fillers, and coupling agents. This investigation prioritizes SiO2 and TRIS, considering their consistent influence. Molecular dynamics simulations, executed with the Forcite module and COMPASS II force field, extend the analysis to the mechanical properties of dental composite complexes. The simulations encompassed energy minimization, controlled NVT and NPT ensemble simulations, and equilibration stages. Notably, the molecular dynamics simulations spanned a duration of 50 ns. RESULTS: SiO2 and TRIS consistently emerged as influential components, showcasing their versatility in promoting solid interactions. A correlation matrix underscores the significant roles of van der Waals and desolvation energies in determining the overall binding energy. Molecular dynamics simulations provide in-depth insights into the mechanical properties of dental composite complexes. HEMA-SiO2-TRIS excelled in stiffness, BisGMA-SiO2-TRIS prevailed in terms of flexural strength, and EBPADMA-SiO2-TRIS offered a balanced combination of mechanical properties. CONCLUSION: These findings provide valuable insights into optimizing dental composites tailored to diverse clinical requirements. While EBPADMA-SiO2-TRIS demonstrates distinct strengths, this study emphasizes the need for further research. Future investigations should validate the computational findings experimentally and assess the material's response to dynamic environmental factors.

Antibacterial Properties of an Experimental Dental Resin Loaded with Gold Nanoshells for Photothermal Therapy Applications.

This study explored the chemical and antibacterial properties of a dental resin loaded with gold nanoshells (AuNPs) in conjunction with photothermal therapy (PTT) as a novel method against Streptococcus mutans (S. mutans) to prevent secondary caries. First, a 20-h minimum inhibitory concentration (MIC) assay was performed on solutions of AuNPs with planktonic S. mutans under an LED device and laser at 660 nm. Next, resin blends containing 0, 1 × 1010, or 2 × 1010 AuNPs/mL were fabricated, and the degree of conversion (DC) was measured using an FTIR spectroscopy. Lastly, a colony forming unit (CFU) count was performed following 24 h growth of S. mutans on 6 mm diameter resin disks with different light treatments of an LED device and a laser at 660 nm. The MIC results only showed a reduction in S. mutans at AuNP concentrations less than 3.12 µg/mL under a laser illumination level of 95.5 J/cm2 compared to the dark treatment (p < 0.010 for each). CFU and DC results showed no significant dependence on any light treatment studied. The AuNPs expressed antibacterial effects following PPT against planktonic S. mutans but not in a polymerized dental adhesive resin. Future studies should focus on different shapes, structure, and concentrations of AuNPs loaded in a resin blend.

Experimental characterization and finite element investigation of SiO2 nanoparticles reinforced dental resin composite.

In this study, a commercial dental resin was reinforced by SiO2 nanoparticles (NPs) with different concentrations to enhance its mechanical functionality. The material characterization and finite element analysis (FEA) have been performed to evaluate the mechanical properties. Wedge indentation and 3-point bending tests were conducted to assess the mechanical behavior of the prepared nanocomposites. The results revealed that the optimal content of NPs was achieved at 1% SiO2, resulting in a 35% increase in the indentation reaction force. Therefore, the sample containing 1% SiO2 NPs was considered for further tests. The morphology of selected sample was examined using field emission scanning electron microscopy (FE-SEM), revealing the homogeneous dispersion of SiO2 NPs with minimal agglomeration. X-ray diffraction (XRD) was employed to investigate the crystalline structure of the selected sample, indicating no change in the dental resin state upon adding SiO2 NPs. In the second part of the study, a novel approach called iterative FEA, supported by the experiment wedge indentation test, was used to determine the mechanical properties of the 1% SiO2-dental resin. Subsequently, the accurately determined material properties were assigned to a dental crown model to virtually investigate its behavior under oblique loading. The virtual test results demonstrated that most microcracks initiated from the top of the crown and extended through its thickness.

Color discrepancy of single-shade composites at different distances from the interface measured using cell phone images.

Objectives: This study aimed to evaluate the impact of substrate color and interface distance on the color adjustment of 2 single-shade composites, Vittra APS Unique and Charisma Diamond One. Materials and Methods: Dual disc-shaped specimens were created using Vittra APS Unique or Charisma Diamond One as the center composite, surrounded by shaded composites (A1 or A3). Color measurements were taken with a spectrophotometer against a gray background, recording the color coordinates in the CIELAB color space. Illumination with a light-correcting device and image acquisition using a polarizing filter-equipped cell phone were performed on specimens over the same background. Image processing software was used to measure the color coordinates in the center and periphery of the inner composite and in the outer composite. The color data were then converted to CIELAB coordinates and adjusted using data from the spectrophotometer. Color differences (ΔE00) between the center/periphery of single-shade and outer composites were calculated, along with color changes in single-shade composites caused by different outer composites. Color differences for the inner composites surrounded by A1 and A3 were also calculated. Data were analyzed using repeated-measures analysis of variance (α = 0.05). Results: The results showed that color discrepancies were lowest near the interface and when the outer composite was whiter (A1). Additionally, Charisma Diamond One exhibited better color adjustment ability than Vittra APS Unique. Conclusions: Color discrepancies between the investigated single-shade composites diminished towards the interface with the surrounding composite, particularly when the latter exhibited a lighter shade.

Urchin-like multiscale structured fluorinated hydroxyapatite as versatile filler for caries restoration dental resin composites.

Caries is one of the most prevalent human diseases, resulting from demineralization of tooth hard tissue caused by acids produced from bacteria, and can progress to pulpal inflammation. Filling restoration with dental resin composites (DRCs) is currently the most common treatment for caries. However, existing DRCs suffer from low fracture strength and lack comprehensive anti-caries bioactivity including remineralization, pulp protection, and anti-cariogenic bacteria effects. In this study, inspired by plant roots' ability to stabilize and improve soil, fluorinated urchin-like hydroxyapatite (FUHA) with a three-dimensional whisker structure and bioactive components of calcium, phosphorus, and fluorine was designed and synthesized by a dynamic self-assembly method. Furthermore, versatile FUHA particles with different loading fractions were used as functional fillers to fabricate methacrylate-based DRCs, where the urchin-like hydroxyapatite (UHA) filled DRCs and commercial DRCs (Z350XT and BEAUTIFIL II) served as the control groups. The results demonstrated that FUHA with 50 wt% loading in resin matrix endowed DRC (F5) with excellent physicochemical properties, dentin remineralization property, cell viability, promotion of dental pulp stem cells mineralization, and antibacterial properties. Meanwhile, F5 also presented good clinical handling and aesthetic characteristics. Therefore, structure/functional-integrated FUHA filled DRCs have potential as a promising strategy for tooth restoration and anti-caries bioactivity.

Effect of various post-curing light intensities, times, and energy levels on the color of 3D-printed resin crowns.

Background/purpose: Current 3D-printing technology has been widely used for creating dental resin restorations. This study aimed to evaluate the effect of light intensity, time, and energy post-curing on the surface color of 3D-printed resin crowns. However, the influences of post-curing parameters on the restoration after printing still need to be explored. Therefore, this project investigates the effect of post-cure conditions on resin color. Materials and methods: Specimens from single-crown (SC) and pontic (PO) specimens underwent post-curing at various light intensities (105, 210, 420, 630, and 860 mW/cm2) for 5, 10, and 15 min. Specimens were observed at three predetermined points and measured using a commercial spectrophotometer that utilizes the CIE Lab∗ color space. Subsequently, samples were analyzed for color differences (ΔE). Results: ΔE color differences in evaluated samples were influenced by the light intensity, time, and energy post-curing. SC samples showed a significant color difference (P < 0.05), with the lowest value at 5 min of 16 (860 mW/cm2), while 10 and 15 min had a difference of 4 (210 mW/cm2). PO samples exhibited a significant decrease in the color difference (P < 0.05) at 5 and 10 min of 16 (860 mW/cm2), and at 15 min of 12 (630 mW/cm2). Conclusion: The results of this study indicate that exposing a resin crown to a high light intensity results in color stability and allows shorter post-curing times.

POSS hybrid bioactive glass dental composite resin materials: Synthesis and analysis.

INTRODUCTION: This study create a dental composite by hybirding polyhedral oligo-sesquioxide nano monomers and bioactive glass BG 45S5. METHODS: Make an experimental composite resin material with a 60 % filler content overall by substituting 20 % of the filler with BG 45S5. The experimental resins are grouped and named P0, P2, P4, P6 and P8 based on the reactive nanomonomer methacrylic acid-based multifaceted oligomeric sesquisiloxane (POSS) added by 2 %-8 % in the resin matrix portion of each group. Utilize a universal testing machine to analyze and compare the mechanical properties of these, then perform Fourier infrared spectrum analysis, double bond conversion analysis, and scanning electron microscope analysis. Based on this, after soaking the experimental materials artificial saliva solution or lactic acid solution for a while, the pH changes of the solution, the release of Ca2+ and PO43- ions, and the precipitation of apatite on the resin material's surface were tested and analyzed. Cell viability tests were used to assess sample cell viability and quantify the cytotoxicity of biological cells. The independent sample t-test was used to examine the group comparisons, and a difference was considered statistically significant at P<0.05. RESULTS: Outstanding mechanical and the double bond conversion are demonstrated by the nanocomposites when the POSS concentration hits 4 wt%. Agglomeration will cause the performance to deteriorate if the concentration beyond this threshold. In the P4 group, the double bond conversion, CS, and FS rose by a large margin, respectively, in comparison to the blank control group P0. Thankfully, the data demonstrate that adding POSS increases adhesive ability when compared to the blank group P0, however, there is no discernible difference between the other experimental groups. The acid neutralization capacity of the P4 group is essentially the same as that of the control group (P0). Ca2+ and PO43- ions are released in significant amounts following treatment with lactic acid solution, although this tendency is clearly less pronounced in artificial saliva. SEM and EDX data indicate that when the experimental resin is soaked in lactic acid solution and artificial saliva, apatite precipitation will happen on its surface. The results of the cell viability test indicated that there was no statistically significant difference between the experimental groups, and the viability of the cells increased after 24hours and 48 hours. CONCLUSIONS: POSS was included into the composite resin along with 20% bioactive glass as a filler. When the proportion of POSS is less than 4%, the indices of composite resin materials rise in a dose-dependent way. When this value is surpassed, performance begins to deteriorate. The inclusion of POSS has no influence on the biological activity of the composites, which means that the hybrid composite resin is capable of acid neutralization, ion release, and apatite precipitation. CLINICAL SIGNIFICANCE: The experimental composite resin can be used as an intelligent material in clinical treatment. It has the clinical application potential of preventing demineralization of tooth hard tissue, promoting remineralization, and improving edge sealing through apatite precipitation.

Effect of silanization of poly (urea-formaldehyde) microcapsules on the flexural strength and self-healing efficiency of an experimental self-healing dental resin composite (An in-vitro study).

OBJECTIVES: This study investigated the impact of using γ-methacryloxypropyl trimethoxy silane (MPS) for surface silanization of poly (urea-formaldehyde) (PUF) microcapsules which enclose a healing liquid of "triethylene glycol dimethacrylate (TEGDMA) and N,N dihydroxyethyl-p-toluidine (DHEPT)" on some mechanical properties of an experimental dental composite as well as its self-healing efficiency. METHODS: Synthesis of PUF microcapsules was done via in situ polymerization, followed by silanization with MPS silane. Silanized and non-silanized microcapsules were incorporated into a composite containing 30% polymer matrix and 70% fillers at different weight percentages (0%, 5%, 7.5% and 10%). The composite strength and elastic modulus were evaluated by Flexural testing. Fracture toughness KIc and self-healing efficiency were assessed by utilizing the "single edge notched beam" method. RESULTS: Flexural strength of all groups containing silanized microcapsules was non-significantly different from control group without microcapsules. However, in contrast to control group, all groups containing non-silanized microcapsules displayed considerably decreased flexural strength. Adding silanized and non-silanized microcapsules didn't show a significant change in the KIc-virgin. The silanized microcapsules' groups achieved a self-healing efficiency of about 49-77% recovery in KIc-virgin compared to 38-69% for their non-silanized counterparts. SIGNIFICANCE: In order to increase the interfacial adhesion with the polymer matrix, improve the mechanical properties, and increase the efficiency of self-healing of dental resin composite, PUF microcapsules were silanized for the first time in the dental field using MPS silane. This innovative silanized microcapsule-containing self-healing composite may hold promise for repairing the damage caused by restorative cracks and extending their service life.