RESUMO
OBJECTIVES: To evaluate the mechanical properties of root canal dentin treated with sodium hypochlorite (NaOCl) in combination with hydroxyethylidene diphosphonic acid (HEDP) or ethylenediaminetetraacetic acid (EDTA). METHODS: For testing fracture resistance, 45 single-rooted teeth were instrumented and irrigated with NaOCl/HEDP, NaOCl/EDTA, or distilled water. Fifteen untreated teeth served as control. After obturation, specimens from the experimental groups were thermocycled, dynamically-loaded, and then statically-loaded in a universal testing machine until failure. For flexural strength analysis, 15 teeth were instrumented and irrigated with NaOCl/HEDP or NaOCl/EDTA. Root segments were sectioned into dentin bars and tested for flexural strength using a universal testing machine. For microhardness evaluation, 20 teeth were instrumented and irrigated with NaOCl/HEDP or NaOCl/EDTA. Dentin disks from the coronal-third of each root segment were prepared, one before and one after irrigation, for microhardness testing with a Knoop hardness tester. RESULTS: The highest fracture resistance was recorded in the untreated group, and the lowest in the EDTA group. Although the HEDP group had higher fracture resistance than the EDTA group, the distilled water group demonstrated even greater fracture resistance than the HEDP group. Specimens treated with HEDP had significantly higher flexural strength and microhardness values when compared with those treated with EDTA. CONCLUSION: The fracture resistance, flexural strength, and microhardness of root canal dentin were higher when root canals were irrigated with NaOCl/HEDP, when compared with NaOCl/EDTA. CLINICAL SIGNIFICANCE: Irrigating root canals with NaOCl combined with HEDP significantly improves the mechanical integrity of root canal dentin compared to the use of NaOCl with EDTA.
Assuntos
Quelantes , Dentina , Ácido Edético , Dureza , Teste de Materiais , Irrigantes do Canal Radicular , Hipoclorito de Sódio , Dentina/efeitos dos fármacos , Hipoclorito de Sódio/farmacologia , Humanos , Ácido Edético/farmacologia , Irrigantes do Canal Radicular/farmacologia , Quelantes/farmacologia , Estresse Mecânico , Ácido Etidrônico/farmacologia , Cavidade Pulpar/efeitos dos fármacos , Resistência à Flexão , Análise do Estresse Dentário , Preparo de Canal Radicular/métodos , Fraturas dos Dentes/prevenção & controle , Raiz Dentária/efeitos dos fármacos , Maleabilidade , Temperatura , Obturação do Canal Radicular/métodosRESUMO
Background: This study assessed the impact of chelating agents, 17% ethylenediaminetetraacetic acid (EDTA), 10% citric acid (CA), and 18% etidronic acid (HEDP), on root dentin mineral content. Scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) was applied to analyze changes, and the push-out bond strength test was used to measure dentin adhesion of Well-Root ST, a bioceramic root canal sealer. Methods: A total of 80 extracted single-rooted lower premolar teeth were included in this study and randomly divided into four groups (n=20): group 1 (17% EDTA), group 2 (10% CA), group 3 (18% HEDP), and group 4 (distilled water, control). After irrigation and drying, SEM-EDS was applied to analyze eight samples from each group at coronal, middle, and apical root regions for mineral content and SEM images. The remaining 12 samples underwent a push-out bond strength test using Well-Root ST sealer and gutta-percha. Kruskal-Wallis and Dunn's tests were used for statistical analyses. Results: Statistically significant differences were found between groups (P<0.05). SEM-EDS showed significant differences in C, O, Ca, P, and Ca/P content, with no significant differences in Na and Mg. Push-out bond strength was significantly higher in the 17% EDTA, 10% CA, and 18% HEDP groups compared to the control group, with no significant differences between chelating agents. Conclusion: Chelating agents altered root dentin mineral content and improved the adhesive properties of the bioceramic sealer. These findings highlight the importance of considering the selection and use of chelating agents in the clinical practice for root canal treatment.
RESUMO
This study aimed to compare the effect of silver diamine fluoride (SDF) and fluoride varnish (NaF) on the Vickers microhardness (VHN) of enamel and dentin after radiotherapy and pH-cycling. Human premolars were cut longitudinally, embedded and serially polished. The VHN of enamel/dentin and irradiated enamel/dentin were evaluated. The irradiated specimens were treated with either NaF or SDF, subjected to pH-cycling then VHN test for 4 days. Consequently, they were subjected to energy-dispersive X-ray (EDX) analysis. Radiation adversely affect enamel VHN (p<0.05), whereas dentin VHN was not affected (p>0.05). After pH-cycling, a significant decrease in dentin VHN was observed on day 2 for all groups, whereas enamel VHN was significantly decreased in the control group on day 4. SDF-treated enamel demonstrated higher VHN than that of NaF on day 3. Caries prevention effect of SDF and NaF were observed on enamel, where SDF was proved to be superior to NaF.
Assuntos
Cárie Dentária , Esmalte Dentário , Fluoretos Tópicos , Dureza , Compostos de Amônio Quaternário , Compostos de Prata , Fluoreto de Sódio , Humanos , Cárie Dentária/prevenção & controle , Compostos de Amônio Quaternário/farmacologia , Esmalte Dentário/efeitos dos fármacos , Esmalte Dentário/efeitos da radiação , Dentina/efeitos dos fármacos , Dentina/efeitos da radiação , Cariostáticos , Dente Pré-Molar , Técnicas In Vitro , Concentração de Íons de Hidrogênio , Espectrometria por Raios X , Raiz Dentária/efeitos dos fármacos , Raiz Dentária/efeitos da radiaçãoRESUMO
OBJECTIVES: To assess the growth of a multispecies biofilm on root canal dentin under different radiotherapy regimens. MATERIALS AND METHODS: Sixty-three human root dentin cylinders were distributed into six groups. In three groups, no biofilm was formed (n = 3): NoRT) non-irradiated dentin; RT55) 55 Gy; and RT70) 70 Gy. In the other three groups (n = 18), a 21-day multispecies biofilm (Enterococcus faecalis, Streptococcus mutans, and Candida albicans) was formed in the canal: NoRT + Bio) non-irradiated + biofilm; RT55 + Bio) 55 Gy + biofilm; and RT70 + Bio) 70 Gy + biofilm. The biofilm was quantified (CFUs/mL). Biofilm microstructure was assessed under SEM. Microbial penetration into dentinal tubules was assessed under CLSM. For the biofilm biomass and dentin microhardness pre- and after biofilm growth assessments, 45 bovine dentin specimens were distributed into three groups (n = 15): NoRT) non-irradiated + biofilm; RT55 + Bio) 55 Gy + biofilm; and RT70 + Bio) 70 Gy + biofilm. RESULTS: Irradiated specimens (70 Gy) had higher quantity of microorganisms than non-irradiated (p = .010). There was gradual increase in biofilm biomass from non-irradiated to 55 Gy and 70 Gy (p < .001). Irradiated specimens had greater reduction in microhardness after biofilm growth. Irradiated dentin led to the growth of a more complex and irregular biofilm. There was microbial penetration into the dentinal tubules, regardless of the radiation regimen. CONCLUSION: Radiotherapy increased the number of microorganisms and biofilm biomass and reduced dentin microhardness. Microbial penetration into dentinal tubules was noticeable. CLINICAL RELEVANCE: Cumulative and potentially irreversible side effects of radiotherapy affect biofilm growth on root dentin. These changes could compromise the success of endodontic treatment in oncological patients undergoing head and neck radiotherapy.
Assuntos
Biofilmes , Candida albicans , Cavidade Pulpar , Dentina , Enterococcus faecalis , Streptococcus mutans , Biofilmes/efeitos da radiação , Dentina/microbiologia , Dentina/efeitos da radiação , Humanos , Cavidade Pulpar/microbiologia , Cavidade Pulpar/efeitos da radiação , Candida albicans/efeitos da radiação , Animais , Enterococcus faecalis/efeitos da radiação , Streptococcus mutans/efeitos da radiação , Bovinos , Microscopia Eletrônica de Varredura , Dureza , Microscopia Confocal , Dosagem RadioterapêuticaRESUMO
The aim of this study was to evaluate the effect of different irrigating solutions as well as their combination and activation modes on root canal dentin microhardness. The protocol was registered in PROSPERO and PRISMA guidelines were followed. The structured question was as follows: "Which type of irrigating solution used in endodontic treatment causes more change in dentin microhardness?" The literature was screened via PubMed, Google Scholar, Scopus, and Science Direct. The last search was carried out in February 2023 with English language restriction. Two reviewers independently performed screening and evaluation of articles. A total of 470 articles were retrieved from all the databases, whereas only 114 articles were selected for full-text analysis. After applying eligibility criteria, 44 studies were evaluated and included in this review. The results showed that with increased contact time with irrigants, dentin microhardness decreases. Increased contact time with sodium hypochlorite (NaOCl) was associated with more reduction in dentin microhardness compared with other irrigants. Other irrigants, with the exception of distilled water, including EDTA, citric acid, herbal irrigants, glycolic acid, phytic acid, etc., in this study significantly decreased dentin microhardness. The maximum reduction in dentin microhardness was seen with 2.5% NaOCl after 15 min of contact time. The use of irrigating solutions alters the chemical composition of dentin, thereby decreasing its microhardness, which affects the clinical performance of endodontically treated teeth.
RESUMO
Human dentition is unique to individuals and helps in identification of individuals in forensic odontology. This study proposes to study the manually ground sections of single rooted teeth using digital methods for dental age estimation. To assess the dentinal translucency from the scanned digital images of manually ground section of teeth using commercially available image edition software. Corroborating the root dentinal translucency length and region of interest (ROI) of translucency zone in pixels (as a marker of dental age) with the chronological age of the subject, as stratified by different age groups. Twenty single-rooted extracted teeth from 20 patients each from 6 groups divided as per age. Manual sectioning of the teeth followed by scanning the sections was done. Root area in pixels and ROI of translucency zone were measured. From the observed values, translucency length percentage (TLP) and percentage of ROI in pixels (TPP) was calculated and tabulated. Pearson's correlation coefficients were obtained for age with TLP and TPP. Positive correlation existed between age and TLP and also between age and TPP. With the obtained data, multilinear regression equations for specific age groups based on 10-year intervals were derived. By a step-down analysis method, age was estimated with an average error of around ±7.9 years. This study gives a novel method for age-estimation that can be applied in real-time forensic sciences.
RESUMO
BACKGROUND: Silver nanoparticle was developed to overcome the drawback of silver diamine fluoride. However, evidence is limited, especially in root caries. The aim of this study was to evaluate the remineralization effect of silver nanoparticles on root caries. MATERIALS AND METHODS: Fifty-five root human dentin slices size 5 × 5 mm2 from patients aged over 60 years old were immersed in demineralized solution to create artificial caries. Specimens were allocated into five groups according to the remineralizing agents: silver diamine fluoride (SDF), silver nanoparticles solution (AgNPs), silver nanoparticle solution followed by sodium fluoride varnish (AgNPs+NaF), sodium fluoride varnish (NaF), and tap water. After 8 days of pH-cycling challenge, the microhardness test, lesion depth evaluation, dentin surface morphology, and elemental analysis were performed. Data was analysed using F-test One-way ANOVA followed by Tukey's post hoc test and paired T-test. RESULTS: All test groups demonstrated a significantly higher microhardness value and lower lesion depth compared with the control group. AgNPs+NaF and NaF-treated groups showed lower efficacy than SDF. Crystal precipitation was presented in all groups composed of silver. CONCLUSION: Addition of fluoride varnish did not benefit for silver nanoparticles in preventing further demineralization. SDF provides the highest effectiveness in elderly root carious dentin.
Assuntos
Cárie Dentária , Nanopartículas Metálicas , Cárie Radicular , Humanos , Pessoa de Meia-Idade , Idoso , Pré-Escolar , Fluoreto de Sódio/farmacologia , Fluoreto de Sódio/uso terapêutico , Fluoretos Tópicos/farmacologia , Fluoretos Tópicos/uso terapêutico , Cárie Radicular/tratamento farmacológico , Nanopartículas Metálicas/uso terapêutico , Suscetibilidade à Cárie Dentária , Prata/farmacologia , Prata/uso terapêutico , Compostos de Prata/farmacologia , Compostos de Amônio Quaternário/farmacologia , Compostos de Amônio Quaternário/uso terapêutico , Compostos de Amônio Quaternário/química , Cárie Dentária/prevenção & controle , Dentina , Sódio/farmacologia , Cariostáticos/farmacologia , Cariostáticos/uso terapêuticoRESUMO
AIM: This study is aimed to evaluate the combined effect of sodium hypochlorite at varied concentrations and temperatures on radicular dentin microhardness along with its surface structural changes using an FTIR spectrometer. MATERIALS AND METHODS: Mandibular premolars were cleaned and shaped up to F3 Protaper gold rotary files, after which they were subjected to five experimental conditions - group I - neutral saline as negative control, group II - 3% NaOCl solution, group III - 5% NaOCl solution, group IV - 3% intracanal-heated NaOCl solution, and group V - 5% intracanal-heated NaOCl solution. Following this, the microhardness of radicular dentin at 100 µm and 300 µm from the canal lumen and Fourier-transform infrared (FTIR) spectroscopic analysis were performed. RESULTS: The results showed that intracanal-heated sodium hypochlorite group reduced root dentin microhardness at 300 µm than its nonheated counterpart. No difference in microhardness values was observed between 3% intracanal-heated and room-temperature sodium hypochlorite groups at 100 µm. Reduction in amide/phosphate ratio was noted in all the groups treated with sodium hypochlorite irrespective of temperature and concentration. CONCLUSION: Thus, considering that the level of alteration in physical and structural changes of root dentin with or without heating is insignificant, intracanal-heated low-concentration sodium hypochlorite solutions could be used as an alternative to high-concentration sodium hypochlorite. CLINICAL SIGNIFICANCE: Intracanal-heated low-concentration sodium hypochlorite enables the clinicians to achieve maximum disinfection while keeping the structural and physical properties of the dentin similar to room-temperature sodium hypochlorite.
Assuntos
Cavidade Pulpar , Hipoclorito de Sódio , Hipoclorito de Sódio/farmacologia , Sódio/farmacologia , Irrigantes do Canal Radicular/farmacologia , Dentina , Ácido EdéticoRESUMO
Nutritional supplements have been recommended to cope with malnutrition in elderly persons. In Chile, the Supplementary Nutrition Program for the Elderly (PACAM, for its Spanish acronym) consists in a monthly distribution of a low-fat-milk-based drink that contains 8% sucrose. The aim of this study was to determine whether older persons consuming the milk-based drink have a higher caries experience when compared to those not receiving the supplement. A cross-sectional study was conducted in the Maule Region in Chile. The representative sample comprised two groups: (a) PACAM consumers (CS) (n = 60) and (b) nonconsumers (NCS) (n = 60). Participants received intraoral examination and coronal (DMFT/DMFS) and root caries (RCI index) experience were recorded. Additionally, questionnaires regarding acceptability and consumption habits of PACAM and a 24-h diet recall were applied. The influence of predictors was calculated using binary logistic regression for a dichotomized DMFS and Poisson Regression for root caries lesions. A p value <0.05 was considered significant. No differences were detected in food consumption patterns between study groups (p > 0.05). CS participants had increased dairy product consumption. Higher DMFS mean value was observed in the CS (85.35 ± 39.0) compared with NCS (77.28 ± 28.9) (p = 0.043). The multivariate analysis showed nonconsumers of the milk-based product (ß = -0.41, p = 0.02) are less likely to have root surfaces affected by caries. Additionally, CS show higher RCI, compared to nonconsumers (ß = -0.17, p = 0.02). Daily consumption of a PACAM's milk-based drink supplement seems to increase coronal and root caries risk. Based on these results, composition modification of milk-based drinks with added sucrose appears mandatory.
Assuntos
Cárie Dentária , Cárie Radicular , Humanos , Idoso , Idoso de 80 Anos ou mais , Animais , Leite , Cárie Radicular/epidemiologia , Cárie Radicular/prevenção & controle , Estudos Transversais , Suscetibilidade à Cárie Dentária , Cárie Dentária/epidemiologia , Cárie Dentária/prevenção & controle , SacaroseRESUMO
PURPOSE: To synthesise and characterise nanosilver sodium fluoride (NSSF) and assess the effect of applying this formulation in vitro on artificially demineralised root dentin lesions, compared with the application of silver diamine fluoride (SDF), sodium fluoride (NAF) or no treatment, in terms of mechanical, chemical and ultrastructural properties. MATERIALS AND METHODS: NSSF was prepared using 0.5 wt% chitosan solution. On 40 extracted human molars, the buccal aspect of the cervical thirds of roots were prepared and divided into 4 groups of 10 each: control (no treatment), NSSF, SDF and NaF (n = 10). The specimens were examined using scanning electron microscopy (SEM), atomic force microscopy (AFM), and x-ray photoelectron spectroscopy (XPS). Fourier transform infrared spectroscopy (FTIR), surface and cross-sectional microhardness and nano-indentation tests were performed to determine the mineral and carbonate content, microhardness, and nanohardness, respectively. Statistical analysis was performed to determine the differences between the different treatment groups for the set parameters using parametric and non-parametric tests. Tukey's and Dunnet's T3 post-hoc tests were further used for multiple comparisons between groups (α = 0.05). RESULTS: The control group (no treatment) was found to have statistically significantly lower mean scores for surface and cross-sectional microhardness compared with all other test groups (NaF, NSSF and SDF) (p < 0.05). Spearman's rank correlation test showed statistically insignificant differences between the mineral-to-matrix ratio (M:M) and carbonate content of all groups (p < 0.05). CONCLUSIONS: Treatment of root lesions with NSSF yielded comparable results to SDF and NaF under in-vitro conditions.
Assuntos
Dentina , Fluoreto de Sódio , Humanos , Fluoreto de Sódio/farmacologia , Microscopia Eletrônica de VarreduraRESUMO
This study aimed to use an in-air micro-particle-induced X-ray/gamma emission (in-air µPIXE/PIGE) system to evaluate tooth-bound fluoride (T-F) in dentin following the application of fluoride-containing tooth-coating materials. Three fluoride-containing coating materials (PRG Barrier Coat, Clinpro XT varnish, and Fuji IX EXTRA) and a control were applied to the root dentin surface of human molars (n = 6, total 48 samples). Samples were stored in a remineralizing solution (pH 7.0) for 7 or 28 days and then sectioned into two adjacent slices. One slice of each sample was immersed in 1M potassium hydroxide (KOH) solution for 24 h and rinsed with water for 5 min for the T-F analysis. The other slice did not undergo KOH treatment and was used to analyze the total fluoride content (W-F). The fluoride and calcium distributions were measured in all the slices using an in-air µPIXE/PIGE. Additionally, the amount of fluoride released from each material was measured. Clinpro XT varnish demonstrated the highest fluoride release among all the materials and tended to show high W-F and T-F and lower T-F/W-F ratios. Our study demonstrates that a high fluoride-releasing material shows high fluoride distribution into the tooth structure and low conversion from fluoride uptake by tooth-bound fluoride.
RESUMO
OBJECTIVES: To evaluate effects of a novel auxiliary irrigation strategy, proanthocyanidin (PA) + carboxymethyl chitosan/amorphous calcium phosphate (CMC/ACP) nanocomplexes, on maintaining the organic-inorganic structural integrity and hence optimizing the adhesion strength of root dentin. MATERIALS AND METHODS: Dentin specimens (n = 150) were prepared and subjected to the classical irrigating strategy with or without PA and CMC/ACP. The ultrastructure and biomechanical behaviour of dentin were characterized by scanning electron microscopy and atomic force microscope, respectively. Forty single root-canal premolars were employed for push-out bond strength testing. Besides, the antibacterial effects against Enterococcus faecalis were evaluated with confocal laser scanning microscopy. Statistical differences were verified with one-way ANOVA and Tukey's post-tests. RESULTS: The organic-inorganic structural integrity of root dentin was repaired with the synergetic use of PA and CMC/ACP. Correspondingly, the bond stability between the root canal wall and the AH-Plus sealer was significantly reinforced (P < 0.05). Meanwhile, the tissue biomechanical properties and antibacterial behaviour were enhanced compared to that of control group (P < 0.05). CONCLUSIONS: The synergistic utilization of PA and CMC/ACP can preserve the structural integrity of root dentin, contributing to optimizing the sealing effects of root canal. Moreover, the novel irrigation strategy demonstrated a favourable antimicrobial activity. CLINICAL RELEVANCE: The combination of PA and CMC/ACP can serve as a promising auxiliary irrigation strategy to optimize the outcomes of chemical preparation, enhance the sealing effects of root canal and hence improve the success rate of treatment.
Assuntos
Colagem Dentária , Materiais Restauradores do Canal Radicular , Dentina/química , Tratamento do Canal Radicular , Raiz Dentária , Microscopia Eletrônica de Varredura , Materiais Restauradores do Canal Radicular/química , Cavidade Pulpar , Teste de Materiais , Resinas Epóxi/química , Preparo de Canal Radicular , Irrigantes do Canal Radicular/farmacologia , Irrigantes do Canal Radicular/químicaRESUMO
Complete eradication of bacterial infection from the root canal with minimum or no effect on the microhardness of the dentin is desirable for the success of endodontic treatment. The effect of nanoparticle based intracanal medicaments on the root dentine microhardness was assessed. The medicaments used were combination of calcium hydroxide - silver nanoparticles, Combination of graphene oxide - silver nanoparticles, Calcium hydroxide and a control group. Vickers hardness value were evaluated and compared at coronal, middle and apical third level. Graphene oxide - silver nanoparticles based intracanal medicament showed least effect on the microhardness of the root dentin compared to calcium hydroxide and calcium hydroxide combined with silver nanoparticle based intracanal medicaments.
RESUMO
PURPOSE: This study investigated the effects of mechanical and chemical pretreatment of polyetherketoneketone (PEKK) on shear bond strength (SBS) to root dentin using two types of resin cement. MATERIALS AND METHODS: A total of 100 PEKK specimens were prepared and polished. Sixty specimens were mechanically treated by sandblasting (50-µm Al2O3 for 10 s at 0.2-0.25 MPa), and the remaining 40 were untreated. Self-adhesive resin cement and conventional resin cement were used. PEKK specimens bonded to root dentin using self-adhesive resin cement were classified into three groups by pretreatment method: (1) untreated PEKK, (2) mechanical pretreatment (sandblasted PEKK), and (3) both mechanical and chemical pretreatment (PEKK sandblasting as well as application of Scotchbond Universal; 3M Oral Care). Conventional resin cement was pretreated following the same steps (1-3) as those followed for self-adhesive specimens. Each group included 10 specimens. PEKK specimens after surface treatments were examined using SEM. SBS tests were performed using a universal testing machine, and data were statistically analyzed using one-way ANOVA and Tukey's multiple comparison test (p < 0.05). RESULTS: No significant difference was observed between cements with and without sandblasting. However, self-adhesive specimens with both mechanical and chemical pretreatments demonstrated higher SBS than other cements with or without pretreatment. CONCLUSION: Mechanical pretreatment by sandblasting did not improve the PEKK-root dentin SBS. However, combined mechanical (sandblasting) and chemical pretreatment (ScotchBond Universal) significantly improved the SBS between the PEKK and root dentin.
Assuntos
Colagem Dentária , Cimentos de Resina , Cimentos de Resina/química , Cimentos Dentários/química , Análise do Estresse Dentário , DentinaRESUMO
Background: Sequential chemical application for irrigating a root canal during chemomechanical debridement can affect the dentin microstructure. Understanding the effects of various irrigants on chemical properties of dentin can elucidate their effects on physical properties and thereby explain the higher incidence of structural failure in endodontically treated teeth. This in vitro research aimed to compare and evaluate the effects of three different irrigating solutions on the chemical structure of root canal dentin in extracted human teeth. Methods: Forty-eight extracted single-rooted mandibular premolar teeth were sectioned at the cemento−enamel junction by a diamond disc and were then randomly assigned to four groups of twelve samples each. The groups were irrigated using 5.25% NaOCl, ozonated olive oil, silver citrate, or distilled water. Dentin sections measuring 1.5 mm were obtained from the root portion and each section and were analyzed using Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and electron-dispersive spectroscopy (EDS). FTIR and EDS values are reported as means ± standard deviations. Data were analyzed using an ANOVA and a post hoc Bonferroni test (p < 0.05). Results: A comparison of the FTIR and EDS values among the groups using ANOVA revealed statistically significant differences in the organic and inorganic peak values among the groups. An intergroup comparison between NaOCl with silver citrate and ozonated olive oil revealed significant reductions in the carbonate and phosphate peak values in the NaOCl group (p < 0.05). The EDS values tabulated for the carbon, oxygen, phosphorous, and calcium peak levels showed significant differences between the groups using an ANOVA. An SEM analysis was conducted under 1500× magnification, which revealed smear layer removal in the silver citrate group. Conclusions: The silver citrate solution and the ozonated olive oil caused less changes in the organic and mineral contents of dentin than sodium hypochlorite.
RESUMO
Aim: The aim of the current study was to evaluate the radicular dentin defect during retreatment employed diverse NiTi hand and rotary retreatment file systems. Materials and Methods: Eighty mandibular premolars with a single root and root canal that were recently extracted were gathered and stored. The premolars were subject to decoronation at cementoenamel junction (CEJ) beneath irrigation with water to attain a uniform radicular length of 16 mm. Gutta-percha cones were covered with sealer and introduced into the root canal up to the working length. Eighty teeth were allocated at random into four groups with each group consisting of 20 samples. Group I: Control, Group II: EdgeFile XR retreatment rotary files, Group III: ProTaper Universal retreatment files, and Group IV: MTwo retreatment files. Under constant water cooling, the roots were cut flat with a diamond disc at apical third (3 mm), middle third (6 mm), and cervical third (9 mm) points. Stereomicroscope was employed to visualize the sections below × 20 magnification. Results: A statistically significant difference was noted among the groups with respect to the formation of radicular dentinal defects at 3 mm (P < 0.01) and 6 mm (P < 0.001), while the sections at 9 mm did not exhibit any statistically significant difference (P > 0.598). Conclusion: Despite the limitations in this study, it was concluded that all the evaluated file systems efficiently eliminated root canal filling during the retreatment. In addition, it was noted that the EdgeFile XR group exhibited fewer root dentin defects in comparison with the MTwo and ProTaper Universal group of files.
RESUMO
Background: Irrigation is a crucial aspect of root canal treatment, and it is imperative to employ chelating agents to eliminate the smear layer during biomechanical preparation. They in turn react with mineral content of dentin, leading to decreased strength and increased susceptibility to fracture. Aims: This study aimed to assess and compare mineral loss and microhardness from primary root canal dentin following the usage of different irrigating solutions and determine the least detrimental irrigant among the tested solutions. Materials and Methods: Sixty-six primary anterior teeth were divided into three groups with 22 in each- Group I: 17% ethylenediaminetetraacetic acid (EDTA) Group II: 0.2% Nano chitosan Group III: Pomegranate extract. The decoronated teeth were split longitudinally. Half of it was directly subjected to Vickers test, and the other half was immersed in a magnetic stirrer bath containing test solution to record the mineral loss from solution. Postmicrohardness values were recorded on the specimen and compared with initial values. Statistical Analysis Used: Statistical analysis was done using SPSS software (Version 20, SPSS, IBM, Armonk, NY, U. S. A). Results: Descriptive statistics were calculated, and the groups were compared using analysis of variance test and post hoc Tukey test. Pomegranate extract showed least effect on mineral content and microhardness compared to 17% EDTA and 0.2% nano chitosan. P ≤ 0.05 was considered statistically significant. Conclusion: Pomegranate aril extract showed better results with selected parameters.
Assuntos
Quitosana , Punica granatum , Quelantes/farmacologia , Quitosana/farmacologia , Dentina , Ácido Edético/farmacologia , Humanos , Irrigantes do Canal RadicularRESUMO
The aim of this study was to investigate the influence of moisture content in frozen and embalmed human cadavers on the detection of dentinal microcracks using micro-computed tomography (micro-CT). The group of embalmed specimens included three mandibular and two maxillary segments each containing one tooth. The group of frozen cadavers consisted of two frozen mandibular bone-blocks with two teeth and one mandibular segment containing one tooth. The final number of teeth for each preservation method was n = 5. All specimens were scanned with eight different moisture conditions: 48 h wet, 2 h dry, 48 h wet, 24 h dry, 48 h wet, 1 wk dry, 48 h wet, 1 wk dry. Micro-CT images were screened for the presence of dentinal microcracks. Statistical analysis was performed by nonparametric analysis of variance (α = 5%). Only few microcracks were observed in wet and in 2 h dried bone-blocks with no significant differences (p = 0.63 and p = 0.23, respectively). There was a significant and steady increase of microcracks within the groups of dried specimens as follows: 2 h dry < 24 h dry < first wk dry < second wk dry (all p < 0.008). Preservation method had no significant influence on the visibility of microcracks (p = 0.98). Identification of dentinal microcracks on micro-CT images is influenced by moisture content of cadaveric bone-blocks irrespective of the preservation method.
Assuntos
Preparo de Canal Radicular , Fraturas dos Dentes , Cadáver , Dentina/diagnóstico por imagem , Humanos , Microtomografia por Raio-XRESUMO
Introducción: este trabajo buscó determinar la exactitud y precisión de los métodos dentales para estimar la edad, basados en la transparencia de la dentina radicular. Materiales y métodos: estudio transversal de tipo comparativo en el que se evaluaron 90 dientes unirradiculares de una muestra peruana de 90 cadáveres adultos masculinos. En cada diente se midió la altura de la periodontosis, altura radicular y longitud de la transparencia de la dentina radicular. Con estas medidas se hallaron las edades dentales de acuerdo con los métodos de Prince-Ubelaker, Ubelaker-Parra y Vilcapoma, y se compararon los resultados entre sí y con la edad cronológica (edad real). Debido a la normalidad de los datos y a su homocedasticidad, se utilizó la prueba de Pearson, el Anova de un factor para muestras relacionadas y la prueba de Tukey. La exactitud se evaluó mediante las diferencias entre las edades cronológicas y las estimadas por cada método, y la precisión se obtuvo del análisis de confiabilidad y repetibilidad, mediante diagramas de Bland-Altman. El nivel de significancia fue 0.05. Resultados: las exactitudes y precisiones fueron de 0.15-0.14, 2.18-2.07, 3.5-3.11 y 9.92-9.82 para los métodos de Vilcapoma, Ubelaker-Parra, Prince-Ubelaker para masculinos blancos y Prince-Ubelaker para para masculinos negros, respectivamente. Conclusiones: el método de Vilcapoma tuvo mayor exactitud y precisión para estimar la edad.
Objective: To determine the accuracy and precision of dental methods for age estimation based on transparency of root dentin. Materials and Methods: Transversal study of comparative type where 90 uniradicular teeth of a Peruvian sample of 90 male adult corpses were evaluated. In each tooth was mea-sured: height of periodontosis, root height and height of transparency of root dentin. With these mea-surements the dental ages were found according to the methods of Prince-Ubelaker, Ubelaker-Parra and Vilcapoma, comparing the results with each other and with the chronological age (real age). Due to the normality of the data and its homocedasticity, the Pearson test, the one-factor Anova for related samples and the Tukey test were used. Accuracy was evaluated by differences between chronological and esti-mated ages for each method and accuracy was obtained from reliability and repeatability analysis using Bland-Altman diagrams. The significance level was 0.05. Results: Accuracy and precision were 0.15-0.14, 2.18-2.07, 3.5-3.11 and 9.92-9.82 for the Vilcapoma, Ubelaker-Parra, Prince-Ubelaker for white males and Prince-Ubelaker for black males, respectively. Conclusions: The Vilcapoma method had greater accuracy and precision in estimating age.
Objetivo: determinar a precisão e a exatidão dos métodos odontológicos para a estimativa da idade com base na transparência da dentina radicular. Materiais e métodos: estudo transversal comparativo onde foram avaliados 90 dentes uniradiculares de uma amostra peruana de 90 cadáveres masculinos adultos. Cada dente foi medido para: altura da periodontose, altura da raiz e comprimento da transparência da dentina radicular. Com estas medidas foram encontradas as idades dentárias de acordo com os métodos de Prince-Ubelaker, Ubelaker-Parra e Vilcapoma, comparando os resultados entre si e com a idade cro-nológica (idade real). Devido à normalidade dos dados e sua homocedasticidade, foram utilizados o teste Pearson, a anova de um fator para amostras relacionadas e o teste Tukey. A exatidão foi avaliada pelas diferenças entre as idades cronológicas e as estimadas por cada método e a exatidão foi obtida a partir da análise de confiabilidade e repetibilidade usando diagramas de Bland-Altman. O nível de significância foi de 0,05. Resultados: precisão e exatidão foram 0,15-0,14, 2,18-2,07, 3,5-3,11 e 9,92-9,82 para os métodos Vilcapoma, Ubelaker-Parra, Prince-Ubelaker para os homens brancos e Prince-Ubelaker para os homens negros, respectivamente. Conclusões: o método Vilcapoma foi mais preciso e exato na estimativa da idade.
Assuntos
Humanos , Adulto , Dente , Saúde , Análise de Variância , Dentina , Homens , MétodosRESUMO
Abstract This in vitro study evaluated the anti-erosive effect of an experimental varnish containing 5% stannous chloride (SnCl₂) associated with different concentrations of NaF (NaF-free, 2.5% NaF, or 5.2% NaF) on bovine enamel and root dentin. One hundred samples were pre-eroded (0.3% citric acid, pH 2.6, 10 min) and randomized into five groups (n=10 for each substrate): Negative control - milli-Q water; NaF-free - Experimental varnish SnCl₂-free and NaF-free; 2.5 NaF - Experimental varnish 5% SnCl₂ associated with 2.5% NaF; 5.2 NaF: Experimental varnish 5% SnCl₂ associated with 5.2% NaF and positive control - Commercial varnish containing 5% NaF (Duraphat). After the varnishes were applied, the erosive and abrasive challenges were carried out for five days. Loss of tooth structure (TSL) was determined by optical profilometry, and the loss of calcium (ΔCa2+) using atomic absorption spectroscopy. Dentin analysis was also performed by SEM. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The experimental 2.5 NaF and 5.2 NaF groups showed greater effectiveness in preventing TSL when compared to the other groups (p <0.05), regardless of the substrate. In addition, these groups showed lower loss in Ca2+ content when compared to the other groups (p <0.05), for enamel and dentin. Dentin showed greater TSL and ΔCa2+ loss when compared to enamel in all treatments (p <0.05). The 5.2% and 2.5% NaF-containing experimental varnishes showed promising results in both, the prevention of TSL and the loss of Ca2+, regardless of the substrate studied.
Resumo Este estudo in vitro avaliou o efeito anti-erosivo de um verniz experimental contendo 5% de cloreto estanoso (SnCl₂) associado a diferentes concentrações de NaF (sem NaF, 2,5% NaF ou 5,2% NaF) sobre esmalte e dentina radicular bovinos. Cem amostras foram pré-erodidas (ácido cítrico 0,3%, pH 2,6, 10 min) e randomizadas em cinco grupos (n=10 para cada substrato): Controle negativo - água milli-Q; Sem NaF - Verniz experimental sem SnCl2 e sem NaF; 2,5 NaF - Verniz experimental 5% SnCl2 associado a 2,5% NaF; 5,2 NaF: Verniz experimental 5% SnCl2 associado a 5,2% NaF e controle positivo - Verniz comercial contendo 5% NaF (Duraphat). Após a aplicação dos vernizes, os desafios erosivos e abrasivos foram realizados por cinco dias. A perda de estrutura dentária (PED) foi determinada por perfilometria óptica e a perda de cálcio (ΔCa2+) por espectroscopia de absorção atômica. A análise da dentina também foi realizada por MEV. Um teste ANOVA/Bonferroni de uma via foi realizado para analisar os dados (α=0,05). Os grupos experimentais 2,5 NaF e 5,2 NaF apresentaram maior eficácia na prevenção de PED quando comparados aos demais grupos (p<0,05), independentemente do substrato. Além disso, esses grupos apresentaram menor perda no teor de Ca2+ quando comparados aos demais grupos (p<0,05), para esmalte e dentina. A dentina apresentou maior PED e de ΔCa2+ quando comparada ao esmalte em todos os tratamentos (p<0,05). Os vernizes experimentais contendo NaF 5,2% e 2,5% apresentaram resultados promissores tanto na prevenção de PED quanto na perda de Ca2+, independente do substrato estudado.