RESUMO
OBJECTIVE: Obtaining strong resin bonds to computer-aided design and computer-aided manufacturing (CAD-CAM) resin-based composites with dispersed fillers (CCRBCs) poses a challenge. Therefore, this study aimed to assess the effect of three universal adhesives and a two-component silane coupling agent on the shear bond strength to three (CCRBCs). MATERIALS AND METHODS: Eight hundred and sixty-four specimens of Brilliant Crios, Lava Ultimate, and Tetric CAD were polished or grit blasted, bonded with Adhese Universal DC, One Coat 7 Universal (OC7), and Scotchbond Universal Plus Adhesive (SBU) with or without a silane primer. Shear bond strength was measured after 24 h and 10,000 thermocycles. Linear regressions were performed (α = 0.05). RESULTS: After thermocycling, bond strengths were similar for the universal adhesives on polished Brilliant Crios and Lava Ultimate (p ≥ 0.408). Grit blasted Tetric CAD showed no significant differences (p ≥ 0.096). The silane primer had minimal impact on grit blasted Tetric CAD (p ≥ 0.384). The silane primer increased the bond strength of OC7 to Brilliant Crios (p = 0.001) but decreased the adhesion of SBU to Brilliant Crios and Lava Ultimate (p ≤ 0.018). CONCLUSIONS: Bond strength of universal adhesives varied with CCRBC type. The two-component silane coupling agent showed mixed effects on adhesive performance. CLINICAL SIGNIFICANCE: Selecting universal adhesives from the same CCRBC product line does not always guarantee superior bond strength. The efficacy of silane coupling agents differs based on the bonding substrate.
Assuntos
Colagem Dentária , Silanos , Silanos/química , Cimentos Dentários , Propriedades de Superfície , Materiais Dentários , Cimentos de Resina/química , Desenho Assistido por Computador , Teste de MateriaisRESUMO
Background/purpose: Intraoral repair usually takes the convenience of the patient's daily life as the starting point, taking into account the bonding strength, operational feasibility, and safety. This study aimed to evaluate the survival of composite resin by simulating cavity fracture repair in porcelain-fused-to-metal (PFM) crowns and referring to the G.V. Black classification of caries as ceramic- and metal-site exposure. Materials and methods: Mechanical sandblast experimental and a nonsandblast control groups comprised 120 samples, and interfacial locking was enhanced through acid etching, bonding, and light-curing composite resin restoration. Classes of VI buccal (B), III mesial (M), and IV mesiobuccal (MB) types, were investigated. Load tests were performed on two sets, with one set at room temperature for 24 h and the other via thermal cycling at 5 °C/50 °C 720 times. Loading was gradually applied to the samples until a maximum of 450 N was reached. Results: Results showed that 24 h survival rates of B-, M - , and MB-repaired PFM crowns were 88%, 84%, and 88%, respectively. The repaired PFM survival rates for B, M, and MB were 52%, 44%, and 28%, respectively, after thermal cycling and loading tests. Multiple logistic regression and chi-square test (α = 0.05) showed that the regression results of factors affecting survival assessment were only significant between groups after thermal fatigue (P < 0.05). Survival rate of repairing metal-site in the MB model was significantly higher than that of ceramic-sites repairing in non-blasted samples. For the MB cavity model, sandblasting can significantly improve the survival rate of the repair of ceramic parts in the MB model (P < 0.05). Conclusion: Our results suggest that sandblasting can be further considered, especially for MB cavity fractures when ceramic-site restorations are required.
RESUMO
Resumo OBJETIVO: Avaliar a resistência ao cisalhamento e o Índice de Remanescente Adesivo (IRA) de bráquetes metálicos colados com três diferentes fotopolimerizadores LED de alta potência, quando comparados ao LED convencional. MATERIAIS E MÉTODOS: 80 incisivos bovinos foram divididos aleatoriamente em 4 grupos (n=20), nos quais foram realizadas colagens dos bráquetes utilizando-se os seguintes LEDs de alta potência por 3s: Grupo 1 LEDX T 2400, Orthometric; Grupo 2 Flashmax P4 PRO Ortho, Rock Moutain Orthodontics; Grupo 3 VALO CORDLESS, Ultradent e Grupo 4 LED convencional por 40s (controle) POLY-WIRELESS, Kavo. O teste de resistência ao cisalhamento foi realizado utilizando-se uma máquina de ensaio universal (AME-2kN, Oswaldo Filizola, São Paulo, Brasil) com velocidade de 0,5mm/min e célula de carga de 50N. A determinação da diferença estatística entre os grupos em relação ao cisalhamento foi realizada usando-se a análise de variância (ANOVA). Para avaliação do IRA, foi aplicado o teste Kruskal-Wallis. RESULTADOS: O grupo 2 apresentou resistência ao cisalhamento significativamente superior aos demais LEDs de alta potência e foi similar ao LED convencional. Em relação ao IRA, houve diferença estatisticamente significante entre os grupos e o único que não diferiu do grupo controle foi o 2, enquanto os demais LEDs de alta potência (Grupos 1 e 3) apresentaram mais falhas adesivas entre a resina e o esmalte. CONCLUSÃO: Houve diferença entre os três tipos de fotopolimerizadores LED de terceira geração, sendo que maior resistência ao cisalhamento e menos falhas adesivas foram observadas no LED que apresentou maior potência (AU)
Abstract OBJECTIVE: To evaluate shear strength and Adhesive Remnant Index (ARI) of metallic brackets bonded to three types of high-power LED light curing, when compared to conventional LED. MATERIALS AND METHODS: 80 bovine incisors were divided into 4 groups (n = 20), in which brackets were bonded using the following high-power LEDs for 3s: Group 1 LEDX T 2400, Orthometric; Group 2 Flashmax P4 PRO Ortho, Rock Mountain Orthodontics; Group 3 VALO CORDLESS, Ultradent; and Group 4 conventional LED for 40s (control) POLY-WIRELESS, Kavo. The shear strength test was performed using a universal test machine (AME-2kN, Oswaldo Filizola, São Paulo, Brasil) with 0.5 mm/min speed and 50N load cell. The determination of statistical difference between the groups in relation to shear strength was performed using analysis of variance (ANOVA). The Kruskal-Wallis test was used to assess the IRA. RESULTS: Group 2 showed shear strength significantly higher than other high-power LEDs and was similar to conventional LED. Regarding ARI, there was a statistically significant difference between the groups and the only one that did not differ from the control group was 2, while the other high-power LEDs (Groups 1 and 3) had more adhesive failures between the resin and the enamel. CONCLUSION: There was a difference between the three types of third generation LED light curing agents, with greater shear strength and less adhesive failures observed in the LED that presented higher power. (AU)
Assuntos
Braquetes Ortodônticos , Resistência ao Cisalhamento , Cura Luminosa de Adesivos DentáriosRESUMO
PURPOSE: To evaluate the effect of irradiation with an optical-fiber device on the bond strength of hollow and partially opaque intraradicular posts. MATERIALS AND METHODS: An optical-fiber accessory tip was attached to a light-curing unit to emit light through the central hollow of an experimental fiberglass post. The samples were divided into 4 groups (n = 80) according to the protocol (Variolink N [light cured] or Multilink N [dual-curing luting material]) and the light-curing mode (performed conventionally or with the optical fiber): GF: light-curing luting material; GFF: light-curing luting material and optical fiber; GD: dual-curing luting material; GDF: dual-curing luting material and optical fiber. The samples were tested immediately or after aging. Push-out bond strength, failure mode, degree of conversion (DC, assessed at the peak of 1750 cm-1), and stress distribution by finite element analysis were performed. Quantitative data were analyzed using 3-way ANOVA (luting material x light curing x depth) and 2-way ANOVA (aging x luting material), followed by Tukey's test. RESULTS: Bond strength was significantly affected by the luting material protocol (p < 0.001), depth (p = 0.010), and light curing mode (p = 0.031). The GFF group revealed higher bond strength in the middle and apical portions. The most frequent failure modes were adhesive in the apical portion for the GFF and GDF groups. The DC was higher for GF and GFF groups. CONCLUSION: Using the optical-fiber device led to superior bond strength results when a dual-curing luting material was used.
Assuntos
Colagem Dentária , Técnica para Retentor Intrarradicular , Colagem Dentária/métodos , Dentina , Teste de Materiais , Fibras Ópticas , Cimentos de Resina/química , Propriedades de SuperfícieRESUMO
To examine the effect of mold enclosure and chisel design on macro shear fatigue bond strengths of dental adhesive systems. The fatigue bond strength testing was conducted with two commercially available dental adhesive systems, (1) OptiBond eXTRa and (2) Scotchbond Universal, for bonding a resin composite (Filtek Supreme Ultra) to both enamel and dentin using a mold enclosure and a non-mold enclosure with a knife-edge and two sized notched-edge chisel assemblies for loading. As a loading reference for the fatigue testing, macro shear bond strengths of the adhesive systems to enamel and dentin were conducted using a mold enclosure and a knife-edge chisel assembly. The shear bond strengths with the mold enclosure using knife-edge chisel assembly did not exhibit a significant difference between the adhesive systems for either enamel or dentin. The fatigue bond strengths of bonded specimens demonstrated significant differences when comparing the mold enclosure and non-mold enclosure, but not between knife-edge and notched-edge chisel assemblies. The fatigue bond strengths of dental adhesive systems demonstrated significantly higher values when using mold-enclosed bonded specimens than a non-mold enclosure, regardless of type of chisel assembly.
Assuntos
Colagem Dentária , Adesivos Dentinários , Resinas Compostas/química , Cimentos Dentários , Dentina/química , Adesivos Dentinários/química , Teste de Materiais , Cimentos de Resina/química , Resistência ao CisalhamentoRESUMO
Introduction: Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective: An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method: Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result: For the customization factor, Tukey's test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion: The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.
Introdução: Dentes com extensa perda de estrutura podem comprometer a retenção das restaurações ao remanescente dental, onde pinos intraradiculares são indicados. Objetivo: Avaliou-se in vitro a união de pinos de fibra de vidro à dentina radicular em função de diferentes modos de reanatomização, fotopolimerizadores e regionalização radicular. Material e método: Noventa (n=10) raízes bovinas uniradiculares foram usadas num estudo fatorial 3 x 3 x 3 com parcelas subdivididas: Reanatomização do pino, variando a presença e tipo de resina (Sem reanatomização, Resina Convencional e Resina Bulkfill); Fotopolimerizador (Valo, Radii-cal, Rainbow); e Terço radicular (cervical, médio e apical). Resultado: O teste de Tukey (5%) evidenciou para o Fator Reanatomização superioridade dos grupos BulkFill (8.16MPa) e Z350 (7.40MPa) ao grupo Controle (4.92MPa), sem diferirem entre si. Todos os fotopolimerizadores diferiram entre si, com superioridade de Valo (9.36MPa), Radii (6.96MPa) intermediário, e inferioridade de Raiwbow (4.17MPa). O terço radicular cervical (7.81MPa) foi superior e o apical inferior (5.80MPa), com o terço médio (6.88MPa) intermediário e sem diferir dos demais. Conclusão: Conclui-se que a reanatomização de pinos de fibra de vidro aumenta a resistência de união à dentina radicular, independentemente da resina utilizada, havendo prejuízo no terço apical e quando são empregados fotopolimerizadores com menor intensidade luminosa.
Assuntos
Técnicas In Vitro , Bovinos , Técnica para Retentor Intrarradicular , Cimentos de Resina , Dentina , Cura Luminosa de Adesivos Dentários , Fotoiniciadores DentáriosRESUMO
Aim: This study evaluated the water sorption and solubility of a light-cured resin cement, under four thicknesses and four opacities of a lithium disilicate ceramic, also considering three light-emitting diode (LED) units. Methods: A total of 288 specimens of a resin cement (AllCem Veneer Trans FGM) were prepared, 96 samples were light-cured by each of the three light curing units (Valo Ultradent / Radii-Cal SDI / Bluephase II Ivoclar Vivadent), divided into 16 experimental conditions, according to the opacities of the ceramic: High Opacity (HO), Medium Opacity (MO), Low Translucency (LT), High Translucency (HT), and thicknesses (0.3, 0.8, 1.5, and 2.0 mm) (n = 6). The specimens were weighed at three different times: Mass M1 (after making the specimens), M2 (after 7 days of storage in water), and M3 (after dissection cycle), for calculating water sorption and solubility. Results: The higher thickness of the ceramic (2.0 mm) significantly increased the values of water sorption (44.0± 4.0) and solubility (7.8±0.6), compared to lower thicknesses. Also, the ceramic of higher opacity (HO) generated the highest values of sorption and solubility when compared to the other opacities, regardless of the thickness tested (ANOVA-3 factors / Tukey's test, α = 0.05). There was no influence of light curing units. Conclusion: Higher thicknesses and opacities of the ceramic increased the water sorption and solubility of the tested light-cured resin cement
Assuntos
Cerâmica , Cimentação , Cimentos de Resina , Cura Luminosa de Adesivos DentáriosRESUMO
BACKGROUND: Only a few controversial studies have assessed the repair bond strength of a fresh composite to aged composite. Moreover, no studies exist on repair bond strength of fresh composites to bleached composites. Therefore, this preliminary study was conducted to assess repair shear bond strength (SBS) of three composites bonded to nonbleached and at-home and in-office bleached composites. MATERIALS AND METHODS: In this experimental in vitro study, 108 disks (36 specimens per composite) of hybrid, microhybrid, and nanofilled composites were divided into three subgroups of three bleaching treatments: no bleaching (control), at-home bleaching, and in-office bleaching. Composite disks were incubated for 4 weeks in artificial saliva (also dipped in tea and coffee for 3 h a day). They were then thermocycled (5000 cycles). Afterward, the control group remained unbleached, while the other groups were bleached according to office and home bleaching methods. They were repaired with the same composite type. Their repair SBS and mode of failure were measured and analyzed using two-way ANOVA, Tukey, one-sample t-test, and Chi-square tests (α = 0.05, ß = 0.2). RESULTS: The mean (standard deviation) SBS values of hybrid, microhybrid, and nanofilled composites were 20.71 ± 5.99, 21.06 ± 6.68, and 9.46 ± 4.32 MPa, respectively. The mean SBS values of the bleaching techniques "home bleaching, office bleaching, and no bleaching (control)" were, respectively, 16.35 ± 7.13, 16.39 ± 8.07, and 18.49 ± 8.35 MPa. There was a significant difference among composites (two-way ANOVA P = 0.000) but not among nonbleaching/bleaching methods (P = 0.176). Their interaction was significant (P = 0.017). The difference between hybrid and microhybrid was not significant. Nevertheless, nanofilled had significantly poorer results compared to both hybrid and microhybrid composites (Tukey P = 0.000). Both hybrid and microhybrid were capable of producing satisfactory clinical repair bond strengths (above 20 MPa) regardless of bleaching or lack of it. Nanofilled composite failed to provide proper repair SBS values, even in the control (no-bleaching) group. By moving from Z100 or from Z250 to Z350, modes of failure shifted from mostly cohesive to mostly adhesive (P < 0.05). CONCLUSION: Bleaching of an aged composite might not affect the repair bond strength. Hybrid and microhybrid composites can provide clinically acceptable repair bond strengths, regardless of bleaching. Nonetheless, nanofilled composite is inferior to them and cannot provide appropriate repair bond strengths (regardless of bleaching).
RESUMO
The literature has shown that there is no consensus regarding the best resin composite photoactivation protocol. This study evaluated the efficiency of the conventional, soft-start, pulse-delay and exponential protocols for photoactivation of resin composites in reducing the shrinkage stress and temperature variation during the photopolymerisation. The photoactivation processes were performed using a photocuring unit and a smartphone app developed to control the irradiance according each photoactivation protocol. These photoactivation methods were evaluated applying photoactivation energies recommended by the resins manufactures. Three brands of resin composites were analysed: Z-250, Charisma and Ultrafill. The cure effectiveness was evaluated through depth of cure experiments. All results were statistically evaluated using one-way and multi-factor analysis of variance (ANOVA). The use of exponential and pulse-delay methods resulted in a significant reduction of the shrinkage stress for all evaluated resins; however, the pulse-delay method required too long a photoactivation time. The increases on the temperature were lower when the exponential photoactivation was applied; however, the temperature variation for all photoactivation protocols was not enough to cause damage in the restoration area. The evaluation of the depth of cure showed that all photoactivation protocols resulted in cured resins with equivalent hardness, indicating that the choice of an alternative photoactivation protocol did not harm the polymerisation. In this way, the results showed the exponential protocol as the best photoactivation technique for practical applications.
RESUMO
OBJECTIVE: This study evaluated the effect of beam homogeneity on the microtensile bond strength (µTBS) of two adhesive resins to dentin. METHODS: One polywave light-emitting-diode (LED) LCU (Bluephase Style, Ivoclar Vivadent AG) was used with two different light guides: a regular tip (RT, 1010 mW/cm2 emittance) and a homogenizer tip (HT, 946 mW/cm2 emittance). The emission spectra and beam profiles were measured from both light guides. Extracted third molars were prepared for µTBS evaluation using two adhesive systems: Excite F (EXF) and Adhese Universal (ADU). Bond strength was calculated for each specimen (n = 10) at locations that correlated with the output of the two LED chips emitting blue (455 nm) and the one chip that emitted violet light (409 nm) after 24-hs and after one-year water-storage. The µTBS was analyzed using a four-way analysis of variance (factors: adhesive system, light guide, LED wavelength, and storage time) and post-hoc Tukey test (α = 0.05). RESULTS: EXF always delivered a higher µTBS than ADU (p < 0.0001), with the µTBS of ADU being about 20% lower than EXF. The light guide (p = 0.0259) and storage time (p = 0.0009) significantly influenced the µTBS. The LED wavelengths had no influence on the µTBS (p > 0.05). SIGNIFICANCE: Homogeneity of the emitted light beam was associated with higher 24-h µTBS to dentin, regardless of the adhesive tested. Also, differences in the composition of adhesives can affect their compatibility with restorative composites and their ability to maintain bonding over one year.
Assuntos
Colagem Dentária , Adesivos Dentinários , Adesivos , Resinas Compostas , Cimentos Dentários , Dentina , Teste de Materiais , Cimentos de Resina , Resistência à TraçãoRESUMO
Abstract Fixed orthodontic appliances may lead to biofilm accumulation around them that may increase caries risk. This study aimed to evaluate the influence of quaternary ammonium methacrylates (QAMs) on the physicochemical properties, cytotoxicity, and antibacterial activity of adhesive resins for orthodontic purposes. Methodology: A base resin was prepared with a comonomer blend and photoinitiator/co-initiator system. Two different QAMs were added to the base adhesive: dimethylaminododecyl methacrylate at 5 wt.% (DMADDM) or dimethylaminohexadecyl methacrylate (DMAHDM) at 10 wt.%. The base adhesive, without QAMs, (GC) and the commercial Transbond™ XT Primer 3M (GT) were used as control. The resins were tested immediately and after six months of aging in the water regarding the antibacterial activity and shear bond strength (SBS). The antibacterial activity was tested against Streptococcus mutans via metabolic activity assay (MTT test). The groups were also tested for the degree of conversion (DC) and cytotoxicity against keratinocytes. Results: The resins containing QAM showed antibacterial activity compared to the commercial material by immediately reducing the metabolic activity by about 60%. However, the antibacterial activity decreased after aging (p<0.05). None of the groups presented any differences for SBS (p>0.05) and DC (p>0.05). The incorporation of DMADDM and DMAHDM significantly reduced the keratinocyte viability compared to the GT and GC groups (p<0.05). Conclusion: Both adhesives with QAMs showed a significant reduction in bacterial metabolic activity, but this effect decreased after water aging. Lower cell viability was observed for the group with the longer alkyl chain-QAM, without significant differences for the bonding ability and degree of conversion. The addition of QAMs in adhesives may affect the keratinocytes viability, and the aging effects maybe decrease the bacterial activity of QAM-doped materials.
Assuntos
Braquetes Ortodônticos , Streptococcus mutans , Teste de Materiais , Biofilmes , Cimentos de Resina , Cimentos Dentários , Metacrilatos , AntibacterianosRESUMO
Objective: The objective of this study was to characterize and correlate the absorption spectra of three photoinitiators [camphorquinone (CQ), diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) and phenylbis (2,4,6-trimethylbenzoyl)-phosphine oxide (BAPO)], using second or third-generation light curing units (LCU), and to evaluate the degree of conversion and the physical properties of an experimental resin adhesive. Material and methods: Second-generation (Radii-cal® and Emitter D®) and third-generation (Valo® Cordless and Bluephase N®) LCU were assessed regarding spectrum and irradiance rate of emitted light. Also, the photoinitiators (CQ, TPO and BAPO) were characterized by a light absorption spectrum assessed by UV-Vis spectroscopy, degree of conversion and yellowing effect. Statistical analyzes considered two-way ANOVA and post-hoc Tukey test. Results: BAPO presented higher reactivity compared to TPO. Regarding degree of conversion of the photoinitiators activated by different light-curing units, the Emitter D® device promoted a high degree of conversion. BAPO presented the highest yellowing effect values. Conclusions: The emission and absorption characteristics of the photoinitiators were different. The polymerization reaction activated by the second-generation light-curing unit was reduced when using an experimental resin with photoinitiator TPO, and the third-generation light-curing unit showed a higher polymerization potential regardless of the photoinitiator. (AU)
Objetivo: Caracterizar e correlacionar os espectros de absorção de três fotoiniciadores [canforoquinona (CQ), difenil 2,4,6-trimetilbenzil óxido de fosfina (TPO) e óxido de di (2,4,6-trimetilbenzil) difenil fosfina (BAPO)], com unidades de fotoativação (LCU) de segunda ou terceira geração, e avaliar o grau de conversão e as propriedades físicas de um adesivo experimental. Material e métodos: LCU de segunda geração (Radii-cal® e Emitter D®) e terceira geração (Valo® Cordless e Bluephase N®) foram avaliadas quanto ao espectro e taxa de irradiância da luz emitida. Além disso, os fotoiniciadores (CQ, TPO e BAPO) foram caracterizados por um espectro de absorção de luz avaliado por espectroscopia UV-Vis, avaliado o grau de conversão dos adesivos e efeito de amarelamento. A análise estatística empregada foi ANOVA duas vias e teste post-hoc de Tukey. Resultados: BAPO apresentou maior reatividade comparado ao TPO. Em relação ao grau de conversão dos fotoiniciadores ativados por diferentes aparelhos fotopolimerizadores, o dispositivo Emitter D® promoveu um alto grau de conversão. BAPO apresentou os maiores valores de efeito de amarelamento. Conclusões: As características de emissão e absorção dos fotoiniciadores foram diferentes. A reação de polimerização ativada pelas unidades de fotopolimerização de segunda geração foi reduzida com o uso de uma resina experimental com fotoiniciador TPO. As unidades de fotopolimerização de terceira geração apresentaram maior potencial de polimerização independentemente do fotoiniciador. (AU)
Assuntos
Cura Luminosa de Adesivos Dentários , Lâmpadas de Polimerização Dentária , Fotoiniciadores DentáriosRESUMO
BACKGROUND: Light curing of resin composite is associated with a thermal rise that may have harmful effect on the health of the vital pulp. In addition, desirable polymerization is important to achieve mechanical properties and clinical function. The purpose of this in-vitro study was to compare the thermal rise under normal dentin during photopolymerization and degree of conversion (DC) of bulk fill and conventional resin composite using continuous high- and soft-start mode. MATERIALS AND METHODS: In this in-vitro study, Cl I cavities with a dimension of 4 mm × 4 mm × 4 mm and remaining dentin thickness of 1 mm were prepared on 56 extracted human molars. The temperature rise during the light curing of conventional resin composite (Tetric N Ceram, Ivoclar Vivadent) by incremental filling technique and bulk-fill resin composite (Tetric N Ceram Bulk Fill, Ivoclar Vivadent) by bulk-filling technique were measured with a K-type thermocouple wire. DC of both resin composites was measured using Fourier-transform infrared spectroscopy. Data were analyzed using one-way ANOVA, Tamhane and Duncan post hoc, two-way ANOVA at the significance level of α = 0.05. RESULTS: Photopolymerization temperature rise due to soft start mode and the first layer of conventional composite was higher than continuous high mode and bulk-filling technique, respectively (P < 0.001). DC of conventional resin composite was higher than bulk-fill composite (P < 0.001). CONCLUSION: Soft-start mode produced higher thermal rise than continuous high mode and conventional resin composite showed higher DC than bulk-fill composite.
RESUMO
PURPOSE: During bracket bonding, patients often report about thermosensitivity. The reason could be that modern light emitting diode (LED) light curing units run with intensities up to 3200â¯mW/cm2. In this in vitro pilot study with nonpulpal circulation approaches, the temperatures in the pulpal cavity were measured. METHODS: The study included 60 extracted teeth divided into four equal groups: lower and upper incisors, premolars and molars. Starting at 37⯰C (body temperature) as the reference, the temperature increase was measured for the first series on each tooth without a bracket, without and with a recommended hygienic barrier case for the LED light curing unit, and exposition to light once versus twice. The distance between the tooth and light curing unit was 3â¯mm. In the second test series, a metal bracket was also bonded to each tooth. In the third series, the light exposition distance was increased to 4â¯mm. RESULTS: In all three test series, significant intrapulpal temperature increase was found: The highest temperatures were recorded after exposure to light once without the hygienic barrier case. In the first test series, this approach showed temperatures even higher than 42.5⯰C in the lower incisors (average 42.99⯱ 2.23⯰C) and premolars (average 42.94⯱ 2.15⯰C). CONCLUSIONS: Significant increases in the temperature of the pulpal cavity (up to 42.5⯰C) may occur during bonding brackets according to the manufacturer's recommendation with an LED light curing unit with in vitro nonpulpal circulation approaches. Therefore it could be reasonable to critically question the recommendation of the manufacturer.
Assuntos
Colagem Dentária , Braquetes Ortodônticos , Lâmpadas de Polimerização Dentária , Cavidade Pulpar , Humanos , Projetos Piloto , TemperaturaRESUMO
The aim of the present study was to formulate dental adhesives with different concentrations of LiNbO3 and to evaluate their physicochemical and antibacterial properties. A dental adhesive was formulated using methacrylate monomers and photoinitiators and used as a control filler-free group. Subsequently, three experimental adhesives doped with LiNbO3 at different concentrations (1 wt.%, 2 wt.%, and 5 wt.%) were also formulated. All the experimental adhesives were assessed to evaluate the degree of conversion (DC), softening in solvent, immediate and long-term microtensile bond-strength (µ-TBS), radiopacity, ultimate tensile strength, and antibacterial activity. The incorporation of 1 wt.% of LiNbO3 had no negative effect on the DC of the adhesive resin compared to the control group (p > 0.05). We observed a decrease in the percentage of softening in solvent in the group LiNbO3 at 1 wt.% (p < 0.05). The addition of LiNbO3 increased the radiopacity at a concentration above 2 wt.%, and there was also an increase in cohesive strength (p < 0.05). The immediate µ-TBS increased for LiNbO3 at 5 wt.% (p < 0.05), and there was no statistical difference for the other groups compared to the control (p > 0.05). After six months, the group with 5 wt.% still presented the highest µ-TBS (p < 0.05). The adhesives showed no antimicrobial activity (p > 0.05). LiNbO3 was successfully incorporated in dental adhesives, increasing the radiopacity and their resistance to degradation. Although LiNbO3 offered no antibacterial properties, the reliability of LiNbO3 incorporation in the adhesive encourages new tests to better investigate the antimicrobial action of LiNbO3 through temperature variation.
RESUMO
In order to evaluate the influence of 38% silver diamine fluoride (SDF) application on enamel and dentin bond stability of universal adhesives in self-etch mode, a 38% SDF and three universal adhesives were used in this study. Initial shear bond strength (ISBS), fatigue bond strength (FBS), and shear bond strength of survivors (SBSS) to enamel and dentin of universal adhesives in self-etch mode, with and without SDF application, were determined. SDF was applied to the polished enamel or dentin surface for 1 min, water-rinsed and air-dried for comparison with controls. The universal adhesives were applied to the prepared samples and composite resin was bonded using a mold-enclosed method. Enamel bond stability of universal adhesives with SDF (ISBS: 14.7-20.4 MPa; FBS: 5.5-7.4 MPa and SBSS: 14.4-21.5 MPa) was significantly weaker than those without SDF (ISBS: 28.0-29.2 MPa; FBS: 12.1-15.6 MPa and SBSS: 28.4-34.4 MPa). Dentin bond stability with SDF (ISBS: 14.8-20.9 MPa; FBS: 7.1-8.2 MPa and SBSS: 17.3-21.8 MPa) was also significantly weaker than without SDF (ISBS: 19.3-36.1 MPa; FBS: 11.0-13.7 MPa and SBSS: 22.2-34.6 MPa). The results suggest that SDF application on enamel and dentin reduces the bond stability of universal adhesives in self-etch mode.
Assuntos
Colagem Dentária , Adesivos Dentinários , Cimentos Dentários , Esmalte Dentário , Dentina , Fluoretos Tópicos , Teste de Materiais , Compostos de Amônio Quaternário , Cimentos de Resina , Resistência ao Cisalhamento , Compostos de PrataRESUMO
The insufficient radiopacity of dental adhesives applied under composite restorations makes the radiographic diagnosis of recurrent caries challenging. Consequently, the misdiagnosis may lead to unnecessary replacement of restorations. The aims of this study were to formulate experimental dental adhesives containing cerium dioxide (CeO2) and investigate the effects of different loadings of CeO2 on their radiopacity and degree of conversion for the first time. CeO2 was characterized by X-ray diffraction analysis, Fourier transforms infrared spectroscopy, and laser diffraction for particle size analysis. Experimental dental adhesives were formulated with CeO2 as the inorganic filler with loadings ranging from 0.36 to 5.76 vol.%. The unfilled adhesive was used as a control. The studied adhesives were evaluated for dispersion of CeO2 in the polymerized samples, degree of conversion, and radiopacity. CeO2 presented a monoclinic crystalline phase, peaks related to Ce-O bonding, and an average particle size of around 16 µm. CeO2 was dispersed in the adhesive, and the addition of these particles increased the adhesives' radiopacity (p < 0.05). There was a significant decrease in the degree of conversion with CeO2 loadings higher than 1.44 vol.%. However, all materials showed a similar degree of conversion in comparison to commercially available adhesives. CeO2 particles were investigated for the first time as a promising compound to improve the radiopacity of the dental adhesives.
RESUMO
In this study, dentin bond fatigue resistance and interfacial science characteristics of universal adhesives through etch-and-rinse and self-etch modes were investigated. Resin composite was bonded to human dentin with four universal adhesives, namely, Adhese Universal, All-Bond Universal, G-Premio Bond, and Scotchbond Universal Adhesive. The initial bond strengths, bond fatigue strengths, and interfacial science characteristics of the universal adhesives with dentin through etch-and-rinse and self-etch modes were determined. Bond fatigue resistance (initial bond strength and bond fatigue strength) of universal adhesives in etch-and-rinse mode showed no significant difference in contrast to that in self-etch mode and was material-dependent regardless of the etching mode. Although phosphoric acid conditioning of dentin did not have a strong impact on the bond fatigue resistance, surface free energy and parameters of dentin were significantly decreased by etching and by application of universal adhesives regardless of etching mode. Changes in γS and γSh for when universal adhesive was applied to etched and ground dentin were significantly different depending on the adhesive. The results suggest that bonding performance of universal adhesives was effective in both etching modes; however, bonding mechanisms may be different for each.
Assuntos
Colagem Dentária , Adesivos Dentinários , Adesivos , Cimentos Dentários , Dentina , Humanos , Teste de Materiais , Cimentos de Resina , Propriedades de SuperfícieRESUMO
Objective: To evaluate the ultimate tensile strength (UTS) of total and self- etch adhesives irradiated at different distances. Materials and Methods: Sixty cylindrical specimens of 0.78mm diameter and 10 mm length were prepared of two types of adhesive systems total etch Excite DSC (EX Ivoclar Vivadent, Schaan, Liechtenstein) and one-step self-etch Clearfil S3 Bond (S3, Kuraray Medical Inc., Tokyo, Japan). Specimens of each adhesive were divided into three groups according to the light irradiation distance (0, 2, 4mm) (n=10). Each specimen was attached to universal testing machine (Digital Force Gauge, IMADA CO., LTD, Japan) and loaded at cross head speed of 1mm/min until failure. Data were analyzed using two-way ANOVA and Independent Student t-test at p< 0.05. Results: Mean UTS for total etch (24.63, 18.19, 17.26 Mpa) and for self-etch (12.68, 8.53, 7.58Mpa) at (0, 2, 4mm) distances. Specimens irradiated directly show significantly the highest UTS while those irradiated at 4mm show the lowest values (p<0.05). Excite DSC total etch adhesive have higher UTS than Clearfil S3 self-etch adhesive regardless of irradiation distance (p<0.05).Conclusions: The UTS of the evaluated adhesives was light irradiation distance and adhesive system dependant.
Assuntos
Humanos , Resistência à Tração/efeitos da radiação , Colagem Dentária , Adesivos Dentinários , Radiação , Cimentos Dentários , Análise do Estresse DentárioRESUMO
OBJECTIVE: This study evaluated the effects of curing modes on surface microhardness of visible light-cured resin-modified glass ionomer cements (VLC RMGIC) and a giomer after different storage periods in comparison to auto-cured resin-modified glass ionomer cements (AC RMGIC). MATERIALS AND METHODS: The following materials were used: VLC RMIC: Fuji II LC Improved, Photac Fil Quick Aplicap, AC RMGIC: Fuji Plus, Fuji VIII and Giomer: Beautifil II. The measurements of microhardness were performed using a Vickers test (100 g loads were applied for 10 s) in the following time intervals: immediately after the recommended cure and after 1, 7 and 14 days of immersion in distilled water. Five samples (d=4 mm, h=2 mm) were prepared for each combination of curing mode and tested material. RESULTS: After 14 days, an improvement of microhardness was evident in all tested materials. The full factorial ANOVA identified a highly significant (p<0.001) effect of the factors "material", "time" and "curing mode ("low", "soft", "high") for the light-cured materials Beautifil II, Fuji II LC and Photac Fil Quick. There was a statistically significant difference in the microhardness between different material types (Beautifil IIËFuji II LCËPhotac Fil QuickËFuji PlusËFuji VIII) and curing modes (low Ësoft Ëhigh). CONCLUSIONS: Material type had the greatest impact on microhardness, followed by the factor of time, while curing modes showed a considerably smaller influence on microhardness of the light-cured materials.