Construction of Magnesium Phosphate Chemical Conversion Coatings with Different Microstructures on Titanium to Enhance Osteogenesis and Angiogenesis.

Titanium (Ti) and its alloys are widely used as hard tissue substitutes in dentistry and orthopedics, but their low bioactivity leads to undesirable osseointegration defects in the early osteogenic phase. Surface modification is an important approach to overcome these problems. In the present study, novel magnesium phosphate (MgP) coatings with controllable structures were fabricated on the surface of Ti using the phosphate chemical conversion (PCC) method. The effects of the microstructure on the physicochemical and biological properties of the coatings on Ti were researched. The results indicated that accelerators in PCC solution were important factors affecting the microstructure and properties of the MgP coatings. In addition, the coated Ti exhibited excellent hydrophilicity, high bonding strength, and good corrosion resistance. Moreover, the biological results showed that the MgP coatings could improve the spread, proliferation, and osteogenic differentiation of mouse osteoblast cells (MC3T3-E1) and vascular differentiation of human umbilical vein endothelial cells (HUVECs), indicating that the coated Ti samples had a great effect on promoting osteogenesis and angiogenesis. Overall, this study provided a new research idea for the surface modification of conventional Ti to enhance osteogenesis and angiogenesis in different bone types for potential biomedical applications.

The Influence of pH Value on the Microstructure and Properties of Strontium Phosphate Chemical Conversion Coatings on Titanium.

Strontium (Sr) is a trace element in the human body that can promote bone formation and inhibit bone absorption. A conversion coating of strontium phosphate (Sr-P) on the surface of titanium (Ti) can improve its biological properties and has many potential applications in the fields of dentistry and orthopedics. In the present study, Sr-P coatings with SrHPO4 and Sr3(PO4)2 crystals on Ti are prepared by a phosphate chemical conversion (PCC) treatment and the effect of pH values on the properties of the Sr-P coatings is researched. The results prove that the phase composition, morphology, and corrosion resistance of the coated Ti vary according to the pH values of the PCC solution. The morphology of the conversion deposition on Ti changes from plat-like to cluster-like and then to homogeneous microcrystals as the pH value changes from 2.50 to 3.25. Only discrete SrHPO4 crystals are generated on the substrate at lower pH values, while relatively stable Sr3(PO4)2 and SrHPO4 crystals grow and subsequently form an integrated coating on the Ti as the pH exceeds 2.50. The cross-sectional morphologies and bonding strength of different coatings are also researched. The corrosion resistance of coated Ti improves compared with that of bare Ti because of the Sr-P coatings with a Sr3(PO4)2 phase. In addition, it is indicated that the Sr-P coatings on Ti can improve the adhesion and differentiation of BMSCs.

Effect of Reaction Temperature on the Microstructure and Properties of Magnesium Phosphate Chemical Conversion Coatings on Titanium.

Magnesium phosphate (MgP) has garnered growing interest in hard tissue replacement processes due to having similar biological characteristics to calcium phosphate (CaP). In this study, an MgP coating with the newberyite (MgHPO4·3H2O) was prepared on the surface of pure titanium (Ti) using the phosphate chemical conversion (PCC) method. The influence of reaction temperature on the phase composition, microstructure, and properties of coatings was systematically researched with the use of an X-ray diffractometer (XRD), a scanning electron microscope (SEM), a laser scanning confocal microscope (LSCM), a contact angle goniometer, and a tensile testing machine. The formation mechanism of MgP coating on Ti was also explored. In addition, the corrosion resistance of the coatings on Ti was researched by assessing the electrochemical behavior in 0.9% NaCl solution using an electrochemical workstation. The results showed that temperature did not obviously affect the phase composition of the MgP coatings, but affected the growth and nucleation of newberyite crystals. In addition, an increase in reaction temperature had a great impact on properties including surface roughness, thickness, bonding strength, and corrosion resistance. Higher reaction temperatures resulted in more continuous MgP, larger grain size, higher density, and better corrosion resistance.

Calcium-Zinc Phosphate Chemical Conversion Coating Facilitates the Osteointegration of Biodegradable Zinc Alloy Implants by Orchestrating Macrophage Phenotype.

Zinc (Zn) alloys provide a new generation for orthopedic applications due to their essential physiological effects and promising degradation properties. However, excessive release of Zn ions (Zn2+ ) during degradation and the severe inflammatory microenvironment are not conducive to osseointegration, which is determined by the characteristics of the implant surface. Therefore, it is essential to modulate the release rate of Zn alloys by surface modification technology and endow them with anti-inflammatory and osteogenic effects. In this study, two kinds of phosphate chemical conversion (PCC) coatings with different compositions and morphological structures are prepared, namely Zn-P (with disk-like crystals) and Ca-Zn-P (with lamellar crystals). Although all the PCC-coated Zn implants have low cytotoxicity, Ca-Zn-P show better osteoimmunomodulation effects in several aspects: the induction of the M2-phenotype macrophage polarization and thus promotion of osteogenesis in vitro; the regulation of the bone immune microenvironment which is conducive to tissue regeneration and osseointegration in vivo; and the release of ions (through PI3K/AKT and Wnt signaling pathways) and the morphological structures (through RhoGTPase signaling pathways) act as possible mechanisms of M2 polarization. The Ca-Zn-P coating can be considered to provide new insights into bone immunomodulation and osseointegration.

Effect of Substrates Performance on the Microstructure and Properties of Phosphate Chemical Conversion Coatings on Metal Surfaces.

Phosphate chemical conversion (PCC) technology has attracted extensive attention for its ability to regulate the surface properties of biomedical metals. However, titanium (Ti)-based alloys exhibit inertia because of the native passive layer, whereas zinc (Zn)-based alloys show high activity in acidic PCC solutions. The substrate performance affects the chemical reaction in the phosphating solution, which further leads to diversity in coating properties. In this work, the zinc-phosphate (ZnP) coatings are prepared on Ti alloy (TA) and Zn alloy (ZA) substrates using the PCC method, respectively. The coatings prepared herein are detected by a scanning electron microscope (SEM), X-ray diffractometer (XRD), laser scanning confocal microscope (LSCM), universal testing machine, contact angle goniometer, and electrochemical workstation system. The results show that the substrate performance has little effect on the phase composition but can significantly affect the crystal microstructure, thickness, and bonding strength of the coatings. In addition, the ZnP coatings improve the surface roughness of the substrates and show good hydrophilicity and electrochemical corrosion resistance. The formation mechanism of the ZnP coating is revealed using potential-time curves, indicating that the metal-solution interfacial reaction plays a dominant role in the deposition process.