Stable Ultrathin Ag Electrodes by Tailoring the Surface of Plastic Substrates for Flexible Organic Light-Emitting Devices.

Flexible transparent metal electrodes (FTMEs) have significant application potentials in the fields of flexible optoelectronic devices due to their outstanding optical transmittance and electrical conductivity. However, obtaining excellent optoelectrical properties and mechanical flexibility of FTMEs is challenging because ultrathin metal layers usually follow an island growth mode. In this paper, flexible transparent ultrathin Ag electrodes with high mechanical stability and good optoelectrical properties were exploited by tailoring the surface properties of plastic substrates with ultraviolet-ozone (UVO) treatment for regulating the nucleation and growth kinetics of Ag films. The composite transparent electrodes of Ag (9 nm)/MoO3 (20 nm) fabricated on the UVO-treated polyethylene terephthalate (PET) substrates possess a low sheet resistance of ∼7.9 Ω/sq, a high optical transmittance of ∼87.2% at 550 nm, a long-period environmental stability of 30 days (∼65 °C, ∼80% humidity), and excellent mechanical flexibility of 100,000 bending cycles at a bending radius of 1.5 mm. These properties are derived from the surface treatment of PET substrates by UVO, which increases substrate surface energy and produces chemical nucleation sites of the phenolic hydroxyl groups. The phenolic hydroxyl groups generated on the PET surface not only provided efficient nucleation sites for subsequent Ag film growth but also formed C-O-Ag bonds between the substrate surface and the Ag layer, which act as "anchor chains" to fix firmly the Ag atoms on the substrate surface. As a universal applicability strategy, the composite electrodes on the UVO-treated polyethylene naphthalate (PEN) and norland optical adhesive 63 (NOA63) substrates also possess excellent optoelectrical properties and mechanical flexibility. Based on the ultrathin Ag composite electrodes, the flexible white organic light-emitting devices with PET, PEN, and NOA63 as substrates present the maximum current efficiencies of 53.0, 77.0, and 65.2 cd/A, respectively.

Improved Metal Oxide Electrode for CIGS Solar Cells: The Application of an AgOX Wetting Layer.

Oxide/metal/oxide (OMO) layer stacks are used to replace transparent conductive oxides as front contact of thin-film solar cells. These multilayer structures not only reduce the overall thickness of the contact, but can be used for colouring of the cells utilizing interference effects. However, sheet resistance and parasitic absorption, both of which depend heavily on the metal layer, should be further reduced to reach higher efficiencies in the solar cells. In this publication, AgOX wetting layers were applied to OMO electrodes to improve the performance of Cu(In,Ga)Se2 (CIGS) thin-film solar cells. We show that an AgOX wetting layer is an effective measure to increase transmission and conductivity of the multilayer electrode. With the presented approach, we were able to improve the short-circuit current density by 18% from 28.8 to 33.9 mA/cm2 with a metal (Ag) film thickness as low as 6 nm. Our results highlight that OMO electrodes can be an effective replacement for conventional transparent conductive oxides like aluminium-doped zinc oxide on thin-film solar cells.

Ultrathin Silver Film Electrodes with Ultralow Optical and Electrical Losses for Flexible Organic Photovoltaics.

Improving the wetting ability of Ag on chemically heterogeneous oxides is technically important to fabricate ultrathin, continuous films that would facilitate the minimization of optical and electrical losses to develop qualified transparent Ag film electrodes in the state-of-the-art optoelectronic devices. This goal has yet to be attained, however, because conventional techniques to improve wetting of Ag based on heterogeneous metallic wetting layers are restricted by serious optical losses from wetting layers. Herein, we report on a simple and effective technique based on the partial oxidation of Ag nanoclusters in the early stages of Ag growth. This promotes the rapid evolution of the subsequently deposited pure Ag into a completely continuous layer on the ZnO substrate, as verified by experimental and numerical evidence. The improvement in the Ag wetting ability allows the development of a highly transparent, ultrathin (6 nm) Ag continuous film, exhibiting an average optical transmittance of 94% in the spectral range 400-800 nm and a sheet resistance of 12.5 Ω sq-1, which would be well-suited for application to an efficient front window electrode for flexible solar cell devices fabricated on polymer substrates.