Effect of combining aminomethacrylate and fluoride against erosive and abrasive challenges on enamel and dentin.

This study evaluated the effect of solutions containing aminomethacrylate copolymer (AA) and sodium fluoride (F; 225 ppm F-) or fluoride plus stannous chloride (FSn; 225 ppm F-, 800 ppm Sn2+) against enamel and dentin erosion/abrasion. Solutions F, FSn, AA, F+AA, FSn+AA, and deionized water as negative control were tested. Bovine enamel and dentin specimens (n = 13/solution/substrate) underwent a set of erosion-abrasion cycles (0.3% citric acid [5 min, 4×/day], human saliva [1 h, 4×/day], brushing [15 s, 2×/day], and treatments [2 min, 2×/day]) for each of five days. Initial enamel erosion was evaluated using Knoop microhardness after the first and second acid challenge on day 1, and surface loss with profilometry after day 5. KOH-soluble fluoride was assessed. Data were analyzed with ANOVA/Tukey tests. The combination of fluoride and AA resulted in higher protection against enamel erosion, whereas this was not the case for the combination of AA and FSn. All treatments protected against enamel and dentin loss. The lowest surface loss values were observed with F+AA and FSn+AA. The polymer did not significantly influence the KOH-soluble fluoride formation on enamel/dentin specimens. The aminomethacrylate copolymer effectively enhanced the efficacy of sodium fluoride against initial erosion and improved the control of enamel and dentin wear of F and FSn solutions.

Dentin erosive wear is reduced by fluoride varnishes containing nanosized sodium trimetaphosphate in vitro.

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Experimental toothpastes containing ß-TCP nanoparticles functionalized with fluoride and tin to prevent Erosive Tooth Wear.

OBJECTIVES: The present study aimed to synthesize toothpastes containing Beta- TriCalcium Phosphate (ß-TCP) nanoparticles, functionalized with fluoride and tin, and test their ability to reduce erosive tooth wear (ETW). METHODS: Toothpastes were synthesized with the following active ingredients: 1100 ppm of fluoride (as sodium fluoride, F-), 3500 ppm of tin (as stannous chloride, Sn2+), and 800 ppm of ß-TCP (Sizes a - 20 nm; and b - 100 nm). Enamel specimens were randomly assigned into the following groups (n = 10): 1. Commercial toothpaste; 2. Placebo; 3 F-; 4. F- + ß-TCPa; 5. F- + ß-TCPb; 6. F- + Sn2+; 7. F- + Sn2+ + ß-TCPa and 8. F- + Sn2+ + ß-TCPb. Specimens were subjected to erosion-abrasion cycling. Surface loss (in µm) was measured by optical profilometry. Toothpastes pH and available F- were also assessed. RESULTS: Brushing with placebo toothpaste resulted in higher surface loss than brushing with F- (p = 0.005) and F- + ß-TCPb (p = 0.007); however, there was no difference between F- and F- + ß-TCPb (p = 1.00). Commercial toothpaste showed no difference from Placebo (p = 0.279). The groups F-, F- + ß-TCPa, F- + ß-TCPb, F- + Sn2+, F- + Sn2+ + ß-TCPa and F- + Sn2+ + ß-TCPb were not different from the commercial toothpaste (p > 0.05). Overall, the addition of ß-TCP reduced the amount of available fluoride in the experimental toothpastes. The pH of toothpastes ranged from 4.97 to 6.49. CONCLUSIONS: Although toothpaste containing ß-TCP nanoparticles protected enamel against dental erosion-abrasion, this effect was not superior to the standard fluoride toothpaste (commercial). In addition, the functionalization of ß-TCP nanoparticles with fluoride and tin did not enhance their protective effect. CLINICAL SIGNIFICANCE: Although ß-TCP nanoparticles have some potential to control Erosive Tooth Wear, their incorporation into an experimental toothpaste appears to have a protective effect that is similar to a commercial fluoride toothpaste.

Stain removal, abrasion and anticaries properties of a novel low abrasion dentifrice containing micro-fibrillated cellulose: in vitro assessments.

OBJECTIVES: This laboratory study assessed the performance of a novel fluoride dentifrice containing micro-fibrillated cellulose (MFC) and entrapped silica. METHODS: Removal of extrinsic stains was assessed using the pellicle cleaning ratio (PCR) method, and radioactive dentin abrasivity (RDA) was measured, to calculate a cleaning efficiency index (CEI). Fluoride efficacy was evaluated using widely used remineralization and fluoride uptake methods. The test product (Protegera™) was compared to common dentifrices (Crest - Cavity Protection™ and ProHealth™, Sensodyne Pronamel™, Arm & Hammer™ Advanced Whitening, Crest ProHealth™, and Colgate Optic White™). RESULTS: The PCR for the MFC dentifrice (141) was comparable to three known marketed stain-removing dentifrices (Arm & Hammer™ Advanced Whitening, Crest ProHealth™, and Colgate Optic White™) but it had a significantly lower RDA (88 ± 6) than 5 other products. This gave it the highest CEI of the tested products (2.0). In a 10-day pH cycling study, the fluoride efficacy of the MFC product was comparable to Sensodyne Pronamel and Crest Cavity Protection. The MFC dentifrice was superior for promoting fluoride uptake into incipient enamel lesions compared to the USP reference dentifrice. CONCLUSION: The MFC dentifrice has low abrasion, but despite this, it is highly effective in removing stained pellicle. It also is an efficacious fluoride source when compared to relevant commercially available fluoride dentifrices with high dentin abrasivity. CLINICAL SIGNIFICANCE: The addition of micro-fibrillated cellulose to a fluoride dentifrice gives a low abrasive product that can effectively remove external stains, and serve as an effective fluoride source. This combination of benefits seems well suited to enamel protection and caries prevention.

Evaluation of Relative Dentin Abrasivity in Whitening Toothpastes Containing Acids.

INTRODUCTION AND AIMS: This study aimed to evaluate the relative dentin abrasivity of whitening toothpastes containing acids using the Radioactive Dentin Abrasivity - Profilometry Equivalent (RDA-PE). METHODS: A total of 100 bovine dentin specimens were prepared and assigned to the following groups (n = 10): 5 hydrogen peroxide (HP) whitening toothpastes (WTH1-WTH5) with or without acid (citric acid, ethylenedinitrilotetraacetic acid disodium, and phosphoric acid), 2 whitening toothpastes with silica and containing citric or phosphoric acid (WTS1 and WTS2), one conventional toothpaste (CT), and 2 reference slurries (RS). All specimens were brushed for 4,000 or 10,000 strokes using toothbrush and toothbrushing machine. The average dentin depth was measured using a noncontact profilometery, and the RDA-PE value was calculated based on the RS. The pH of the solution, average particle size, particle content, and particle hardness were measured. The RDA-PE data were analysed using one-way analysis of variance and Tukey's test, and the effects of the 4 measured factors on RDA-PE were investigated via multiple regression analysis. RESULTS: The RDA-PE values of the HP whitening toothpastes (mean value: 19-46) were significantly lower, whereas those of the silica whitening toothpastes (80 or 111) were similar to those of the RS after 4,000 strokes (100). The RDA-PE values of all whitening toothpastes were significantly lower than the RS values after 10,000 strokes (242). The HP whitening toothpastes were slightly acidic (pH ≤6) compared to the other solutions. The HP (2.9%-3.7%) and silica (8.9% or 9.9%) whitening toothpastes had significantly lower particle content than RS (16.6%). The particle content significantly influenced the RDA-PE values by multiple regression results. CONCLUSIONS: The RDA-PE values of whitening toothpastes varied. The particle content in the solution was a key factor affecting the RDA-PE value. CLINICAL RELEVANCE: Whitening toothpastes containing acids did not cause significant dentin abrasion.

Tooth surface loss: causes, management, and prevention.

OBJECTIVES: Tooth wear, also referred to as tooth surface loss, occurs due to causes other than caries. This involves the loss of hard tissues, namely enamel, dentin, and/or cementum. Types of tooth wear/tooth surface loss are abrasion, abfraction, attrition, and erosion. These multifactorial conditions can be caused by factors such as lifestyle, diet, or even habits, and may not be symptomatic. The focus of this article is to provide clinicians with detailed examples and explanations of the causes of tooth loss to aid in early diagnosis. Through early identification, the preventive measures outlined can be implemented to avoid excessive tooth wear. The provision of a treatment flowchart and general treatment recommendations aims to help clinicians determine when to restore these lesions and the most appropriate treatment measures for the four types of wear. METHOD AND MATERIALS: The PubMed (MEDLINE) search engine was used to gather information on teeth restricted to a 5-year period (26 August 2018 to 25 July 2022). Only English-language studies and reviews with the best balance of sensitivity and specificity were considered. A Boolean search of the PubMed dataset was implemented to combine a range of keywords: ("tooth wear" OR tooth attrition OR tooth erosion OR tooth abrasion OR tooth abfraction). Additional articles were selected through Google Scholar. RESULTS: By this process, many articles and studies were obtained, and the 48 most relevant published studies were chosen and used in the current review. CONCLUSION: Tooth wear affects an increasing number of individuals and can have detrimental effects physically, mentally, and emotionally. It is important to stress early diagnosis and management of tooth wear through monitoring, prevention, and treatment where indicated.

Effect of different brushing parameters on erosive tooth wear in primary bovine enamel and dentin.

This in-vitro study aimed to analyse the effect of brushing and different brushing parameters (kind of toothpaste, kind of toothbrush, brushing force) on erosive tooth wear of primary bovine enamel and dentin. Specimens were prepared from primary bovine enamel or dentin (each group n = 12) and cyclically eroded (6 × 60 s/d, citric acid, pH 2.4) and brushed with children's toothbrushes (2 × 15 s/d) over 5 days. The brushing parameters under investigation were: toothpaste (fluoridated, fluoride-free), toothbrush (manual; rotating-oscillating and sonic, each at two different activation modes) and brushing force (1 N, 2 N). Specimens that were only eroded and not brushed served as controls. Enamel and dentin wear was quantified using widefield confocal microscopy. Statistical analysis was performed using three- and one-way ANOVAs followed by Scheffe's (enamel) or Tamhane's (dentin) post-hoc tests (p < 0.05). Brushing with the fluoridated toothpaste was able to significantly reduce erosive wear in enamel (by 15 to 37%, 6 of 10 groups) and in dentin (by 58 to 72%, all groups), while brushing with the fluoride-free toothpaste was not different from the controls. Considering the kind of toothpaste and brushing force, slight differences between the toothbrushes were observed in enamel, but not in dentin. Within the same toothbrush and activation mode, almost no differences between 1 and 2 N brushing force were detected. In conclusion, erosive tooth wear on primary bovine dental hard tissue mainly depends on the kind of toothpaste, rather than on the kind of toothbrush and the brushing force.

Toothpaste containing TiF4 and chitosan against erosive tooth wear in situ.

OBJECTIVE: This study compared the protective effect of an experimental TiF4/Chitosan toothpaste with a commercial toothpaste on the prevention of erosive tooth wear (ETW) in situ. METHODS: Fifteen subjects took part in this crossover and double-blind study, in which they wore a palatal appliance containing 4 bovine enamel and 4 dentin in 3 phases (5 days each). Half of the samples were subjected to erosive challenges (90 s in 0.1 % citric acid, pH 2.5, 4 times/day), and the other half to erosive plus abrasive challenges (15 s plus 45 s of contact, 2 times/day). The phases corresponded to the application of the different toothpastes: 1) TiF4 (1400 ppm F-) plus Chitosan, 2) Elmex®, Erosion Protection (1400 ppm F-, Chitosan), and 3) Placebo (negative control). Tooth wear was measured using contact profilometry (µm) and submitted to two-way RM ANOVA/Tukey test (p < 0.05). RESULTS: No significant differences were detected between the experimental and commercial toothpastes, regardless of the challenge on both tissues. Both significantly reduce ETW compared to negative control (p < 0.0006). Tooth wear was increased by brushing only on eroded enamel (p < 0.01), but not on dentin (p = 0.6085). TiF4/Chitosan [erosion 2.98 ± 1.12 µm vs. erosion and abrasion 3.12 ± 1.33 µm] and Elmex® toothpastes [erosion 2.35 ± 0.93 µm vs. erosion and abrasion 2.98 ± 1.0 µm] minimized the impact of brushing compared to placebo on enamel [erosion 4.62 ± 1.48 µm vs. erosion and abrasion 5.15 ± 1.50 µm]. CONCLUSIONS: TiF4 plus chitosan toothpastes showed to be effective in minimizing the ETW as the commercial toothpaste is in situ. CLINICAL RELEVANCE: The experimental toothpaste has similar effect against ETW compared to the commercial toothpaste. Considering the increased ETW prevalence worldwide, this result supports clinical trials and a possible application of this experimental anti-erosive toothpaste in the future.

Characteristics of tin-containing fluoride toothpastes related to erosive tooth wear protection.

OBJECTIVES: To assess the effect of different tin-containing toothpastes on the control of erosive tooth wear in enamel and dentin. METHODS: Enamel and dentin slabs were randomly distributed into 7 experimental groups (n = 10/substrate): C-: negative control (Artificial saliva); AmF (regular fluoridated toothpaste without tin); Sn-1 (SnF2/NaF); Sn-2 (SnF2/NaF/SnCl2); Sn-3 (SnCl2/NaF); Sn-4 (SnF2/SnCl2); Sn-5 (SnCl2/AmF/NaF/chitosan). Specimens were submitted to 5-day erosion-abrasion cycling. Surface loss (SL) was determined with an optical profilometer. Tin deposition on the tooth surfaces and some characteristics of the toothpastes (pH, potentially available F-, %weight of solid particles, and RDA) were also assessed. Data were statistically analyzed (α = 0.05). RESULTS: For enamel, the Sn-2 presented the lowest SL, not differing significantly from AmF, C+, and Sn-3. The SL of these groups was significantly lower than the C-, except for Sn-3. Sn-1 and Sn-4 were also not significantly different from C-. For dentin, C- significantly showed the highest SL values, whilst, Sn-1 presented the lowest SL, not differing significantly from AmF, Sn-2, C+, and Sn-3. There was a significant positive association between enamel SL and the pH and tin deposition. Dentin SL was significantly negatively associated with the %weight of solid particles and RDA. CONCLUSIONS: Most of the tin-toothpastes were able to exhibit some protection against ETW. In this process, the toothpastes characteristics play a role, as lower enamel SL was significantly associated with lower pH values and tin deposition; and lower dentin SL was associated with higher %weight of solid particles and RDA of the toothpastes. CLINICAL SIGNIFICANCE: Tin-containing toothpastes can be used for erosive tooth wear protection, but our study showed that their effect depends on the pH, amount of tin deposition, % weight of solid particles and RDA of the toohpastes.

Description of a new laboratory evaluation method of interdental brush abrasion as a clinical hazard.

OBJECTIVES: To simulate the abrasive potential of an interdental brush when applied with toothpastes and prophylactic gels/solutions in a novel laboratory brushing simulation set-up. METHODS: A brushing device was customized to treat dentin samples mimicking a simplified interdental space with an interdental brush (ISO 2). The brushing, that is, 7200 strokes for 1 h, was performed with artificial saliva (control), a povidone-iodine solution, and slurries of chlorhexidine and fluoride gels as well as three toothpastes with different RDA values ranging from 29 to 100, respectively. The loss of dentin was profilometrically assessed and compared with ANOVA and Fishers LSD. RESULTS: While artificial saliva as control, the solution and the gel slurries showed no measurable dentin loss, toothpastes resulted in a measurable linear surface damage with respect to the actual intrinsic RDA values and ranged from 12.6 to 26.5 µm (p < 0.001). CONCLUSIONS: Any interdental cleaning product should be tailored and carefully instructed. Any over- and misuse should be avoided, which applies especially to the use of interdental brushes in combination with abrasive toothpastes.

Impact of toothbrush head configuration and dentifrice abrasivity on non-carious cervical lesions in-vitro.

OBJECTIVE: To investigate the effect of toothbrush head configuration and dentifrice slurry abrasivity on the development of simulated non-carious cervical lesions (NCCLs) in vitro. METHODS: Extracted premolars were randomly allocated into 15 groups (n = 16) generated by the association between toothbrush head configuration (flat-trimmed, rippled, cross-angled/multilevel/rubbers added, cross-angled/multilevel/flex head, feathered) and dentifrice slurry abrasivity (low/medium/high). Teeth were mounted on acrylic blocks and had their roots partially covered with acrylic resin, leaving 2-mm root surfaces exposed. Toothbrushing was performed for 35,000 and 65,000 double-strokes. Specimens were analyzed using non-contact profilometry for dental volume loss (mm3) and lesion morphology. Data was analyzed using ANOVA with pairwise comparisons and Kruskal-Wallis tests. RESULTS: The two-way interaction between toothbrush head configuration and slurry abrasivity was significant (p = 0.02). At 35,000 strokes, the flat-trimmed and cross-angled/multilevel/rubbers added toothbrushes caused the highest loss, when associated to the high-abrasive slurry (p<0.05); whereas cross-angled/multilevel/flex head showed the least loss, when associated to the low-abrasive (p<0.05). At 65,000, more dental loss was observed for all toothbrushes when associated to the high-abrasive slurry, with flat-trimmed causing the highest loss (p < 0.05). Lower dental loss rates were observed for cross-angled/multilevel/flex head associated to the low-abrasive slurry when compared to the other toothbrushes (p < 0.05), except to feathered (p = 0.14) and rippled (p = 0.08). Flat lesions (mean internal angle ± standard-deviation: 146.2°± 16.8) were mainly associated with low-abrasive slurry, while wedge-shaped lesions (85.8°± 18.8) were more frequent with medium- and high-abrasive slurries. CONCLUSION: The development, progression and morphology of simulated NCCLs were modulated by both toothbrush head configuration and dentifrice abrasivity. CLINICAL SIGNIFICANCE: Dental professionals should consider both the type of toothbrush and dentifrice abrasivity in the management plan of patients at risk of developing NCCLs.

A microscopia eletrônica de varredura pode ser usada para medir quantitativamente a rugosidade da dentina? / Can Scanning Electron Microscopy be used to quantitatively measure dentine roughness?

Objective: The aim of this study was to determine if SEM used with imaging software could be used to quantitatively determine the extent of dentine roughness due to tooth-brushing. Material and methods: Flat, polished dentine surfaces were subjected to 25,000 cycles of simulated tooth-brushing at 2 strokes per second with a load of 200 g. At the end of the brushing cycle, dentine surfaces were first assessed using profilometry and then subjected to SEM analysis. Ra (average roughness) readings were obtained for profilometric assessment. Using imaging software, the horizontal distance between adjacent characteristic grooves noted on micrographs was measured, ensuring that the middle of each crest of the associated groove was used as the reference point, the Crest-to-Crest distance (C-C distance). These two parameters were examined statistically for correlation. Results: When Spearman Rank tests were utilized the correlation between average Ra and crest to crest measurements was 0.709 (p <0.01). The Bland Altman plot, however, showed poor agreement between the two test parameters. Conclusion: Further work is needed to validate the use of this methodology in the quantitative assessment of tooth surface loss due to abrasion (AU)

Objetivo: O objetivo deste estudo foi determinar se o MEV usado com software de imagem poderia ser usado para determinar quantitativamente a extensão da rugosidade da dentina devido à escovação dentária. Material e Métodos: Superfícies dentinárias planas e polidas foram submetidas a 25.000 ciclos de escovação dentária simulada a 2 movimentos por segundo com uma carga de 200g. No final do ciclo de escovação, as superfícies dentinárias foram primeiro avaliadas por perfilometria e depois submetidas à análise MEV. Leituras de Ra (rugosidade média) foram obtidas para avaliação perfilométrica. Utilizando um software de imagem, foi medida a distância horizontal entre sulcos característicos adjacentes observados nas micrografias, garantindo que o meio de cada crista do sulco associado fosse usado como ponto de referência, a distância crista a crista (distância CC). Esses dois parâmetros foram examinados estatisticamente para correlação. Resultados: Quando foram utilizados os testes de Spearman Rank, a correlação entre a média de Ra e as medidas de crista a crista foi de 0,709 (p<0,01). O gráfico de Bland Altman, no entanto, mostrou fraca concordância entre os dois parâmetros de teste. Conclusão: Mais trabalhos são necessários para validar o uso desta metodologia na avaliação quantitativa da perda da superfície dentária devido à abrasão(AU)

The effect of location/site on polished human enamel after mechanical and chemical wear.

OBJECTIVE: To compare profilometry and microhardness of polished occlusal and buccal human enamel following a mechanical and chemical wear regime. METHODS: Enamel from polished human molars were sectioned into buccal and occlusal surfaces and randomly allocated into two groups (n = 10) and then exposed to 0.3 % citric acid at pH 2.7 for 10, 20, 40 and 60 mins each followed by abrasion with non-fluoridated toothpaste for 240 strokes in a reciprocating brushing machine. A white light profilometer with a spot size of 12 um measured mean step-height following each cycle. Microhardness indentations were conducted following the final cycled 60 mins erosion/abrasion using 0.01, 0.02, 0.1, 0.5 and 2.5 kgf indentation load. Statistical disparity were evaluated using a two-way ANOVA and post-hoc Sidak's multiple comparisons tests at α = 0.05. RESULTS: After erosion/abrasion, the mean (SD) step-heights on occlusal and buccal surfaces were not significantly different until 60 mins, when occlusal surfaces exhibited greater step-heights, 32.9 µm (2.8) and 31.1 µm (1.8) and p = 0.02, respectively. Buccal and occlusal microhardness was statistically lower following erosion/abrasion at loads of 0.01 kgf (p = 0.0005) and 0.02 kgf (p = 0.0006) but no significant differences were observed in the microhardness between the surfaces at any loads. CONCLUSION: The occlusal and buccal surfaces were not statistically different for microhardness or step height suggesting the susceptibility to wear is not related to the anatomy and structure of the tooth and is more likely related to other factors such as the environment. CLINICAL SIGNIFICANCE: The study emphasizes that a notable difference in wear between occlusal and buccal enamel surfaces emerges only after prolonged exposure to simultaneous chemical and mechanical stress. This finding necessitates a preventive dental approach that accounts for both the duration of exposure and environmental factors.

Longterm abrasive and erosive effect of whitening toothpaste on dentin surface.

PURPOSE: To evaluate the amount of dentin loss following immersion in or toothbrushing with whitening toothpaste (WT) containing hydrogen peroxide (HP) and citric acid (CA). Additionally, the amount of dentin loss after brushing with a WT alone or in combination with a conventional toothpaste was assessed, and the effects of HP and CA solutions on the dentin surface were investigated. METHODS: Bovine dentin specimens (n= 350) were randomly assigned to seven solutions of various compositions as toothpaste: The specimens assigned to each solution were then further divided into five treatment groups (n=10 each) : Group A = 1-hour immersion in each solution (ES); Group B = 10,000 brushing in ES; Group C = 1-hour immersion in ES + 10,000 brushing in ES; Group D = 1-hour immersion in ES + 10,000 brushing in reference slurry (RS); Group E = 10,000 brushing in ES + 10,000 brushing in RS. The amount and pattern of dentin loss were determined, and the surfaces were observed using noncontact profilometry. RESULTS: The WT (pH 5.0) caused lower dentin loss than RS after a single brushing cycle; however, the extent of dentin loss after 1 hour of immersion in the WT was significantly greater than that in the RS. Among the specimens treated with WT, a significant difference in dentin loss was observed between Group C and Groups D and E (P< 0.05) but not between Groups D and E. The surfaces exposed to CAS1, CAPB, and WT exhibited U-shaped patterns of dentin loss after brushing or immersion, whereas a wedge-shaped pattern was observed in those that underwent brushing with the RS. CLINICAL SIGNIFICANCE: The effects (dentin abrasion) of a whitening toothpaste containing hydrogen peroxide and citric acid when used in combination with a conventional toothpaste were similar to those seen with the continuous use of a conventional toothpaste alone.

Envejecimiento dental prematuro en deportistas / Premature dental aging in athletes

El desgaste natural de los dientes ocurre dependiendo de factores como: calidad de la estructura dental, calidad de la saliva, biotipo facial que determina la fuerza de mordida; de acuerdo a estos factores locales bucales se va envejeciendo la dentadura. Pero los deportistas presentan un patrón de desgaste mayor y continuo debido al tipo de deporte que practican, las horas de entrenamiento, el consumo de bebidas con pH ácido, el cepillado dental vigoroso; todos estos factores pueden conducirlos a que desarrollen lesiones no cariosas (AU)

The natural wear of the teeth occurs depending on factors such as: quality of the dental structure, quality of the saliva, facial biotype that determines the bite force, according to these local oral factors, the teeth age. But in athletes they present a pattern of greater and continuous wear due to the type of sport they practice, the hours of training, the consumption of drinks with an acidic pH, vigorous tooth brushing; all these factors can lead them to develop non-carious lesions (AU)

In Vitro Assessment of Different Toothbrush Designs on Enamel Surface Abrasion: A Profilometric Study.

AIM: The purpose of this study was to evaluate the impact of three different toothbrush designs on enamel surface abrasion. MATERIALS AND METHODS: Sixty intact freshly extracted maxillary central incisors were considered for the study. All of the extracted teeth's surfaces were severely trimmed, leaving only the labial surface intact. In the trial, a conventional teeth-whitening dentifrice slurry was utilized. A brushing model was created to deliver uniform force in unidirectional motion. Dontrix Gauge was used to control the tension of the spring. The force was kept constant at 180 ± 20 g. The mounted enamel samples were separated into three groups (20 samples each) at random: group A: toothbrushes have a flat trim bristle design, group B: toothbrushes have a zigzag pattern, and group C: toothbrushes have a bi-level bristle design. For 2 weeks, each sample was brushed twice daily for 2 minutes. A profilometer was used to measure the average surface roughness. RESULTS: After toothbrushing, the maximum mean surface roughness score was found in zigzag pattern group (2.10 ± 0.23), followed by bi-level bristle design group (2.06 ± 0.12) and the least was in the flat trim bristle design group (1.96 ± 0.09). There was a significant difference between the different toothbrush bristle pattern groups (p < 0.001). CONCLUSION: On conclusion, the results of this study showed that, in comparison to toothbrushes with zigzag patterns and bi-level bristle designs, flat trim toothbrush bristle designs cause the least amount of surface abrasion and are relatively safe to use. CLINICAL SIGNIFICANCE: Toothbrushing with toothpaste contributes significantly to dental abrasion. A variety of parameters, including toothpaste abrasivity and concentration, brushing frequency, brushing length, brushing force, and toothbrush bristle stiffness, have the potential to influence the abrasion process of dental hard tissue.

Supplementation of Energy Drinks with Green Tea Extract: Effect on In Vitro Abrasive/Erosive Dentin Wear.

PURPOSE: To investigate the effect of the supplementation of energy drinks with green tea extract on abrasive and erosive dentin wear. MATERIALS AND METHODS: Six groups, each comprising 15 bovine dentin samples, were prepared, yielding a total of 90 samples. Erosion was performed by immersing the samples in Red Bull and Red Bull light with and without green tea extract. Tap water with and without green tea extract was used as the control groups. The samples were subjected to abrasive/erosive cycling for five days. The following cycling was performed daily: toothbrush abrasion (20 brushstrokes; 2.5 N); eight erosive cycles (2 min storage in the respective solutions); in between the erosive cycles, storage in artificial saliva (60 min) and again toothbrush abrasion (20 brushstrokes; 2.5 N). During the night, samples were again stored in artificial saliva. Abrasive/erosive dentin wear was measured using a stylus profilometer (µm, accuracy = 40 nm). The measured dentin loss results from the vertical position shift on the y-axis from base to final profile after the wear process in 2D. Pairwise comparisons between the groups were carried out using Wilcoxon signed-rank test. RESULTS: The following dentin wear (median [IQR]) was measured: Red Bull: 1.9 µm (0.5); Red Bull Light: 1.3 µm (0.3); Red Bull with green tea extract: 0.8 µm (0.3); Red Bull Light with green tea extract: 0.3 µm (0.5); Tap water with green tea extract: -0.2 µm (0.7); Tap water: -1.0 µm (1.2). The comparison of all tested groups to each other proved to be statistically significant (p < 0.05). CONCLUSION: The supplementation of energy drinks with green tea extract provide a protective effect against erosive/abrasive wear in vitro.

[Aesthetic management of erosive tooth wear using injection molding technique]. / Esteticheskoe lechenie vertikal'noi stiraemosti zubov s ispol'zovaniem in"ektsionnoi tekhniki.

In this article, on the example of a clinical case, the technique of restoring two central teeth in a patient with increased enamel erasability with highly filled fluid composite materials using injection techniques is described. The application of this technique has become possible because the new fluid composites have similar mechanical, physical and aesthetic properties to universal composite materials.

Interaction between Hexametaphosphate, Other Active Ingredients of Toothpastes, and Erosion-Abrasion in Enamel in vitro.

Sodium hexametaphosphate (HMP) as toothpaste additive is claimed to reduce erosive tooth wear and to stabilize stannous ions. However, little is known about the impact of concentration and its interactions with fluoride (F) or stannous+fluoride ions (F/Sn) on enamel erosion and erosion-abrasion. In a 10 day cyclic in vitro erosion-abrasion model, 320 flat human enamel specimens were divided into ten groups (n = 32 each) and daily subjected to six erosive challenges (0.5% citric acid, 2 min) and two toothpaste suspension applications (2 min, 1:3 F-free toothpaste:mineral-salt solution, 0.23% sodium gluconate). Half of specimens per group were additionally brushed twice/day (200 g, 15 s) during suspension immersion. Nine suspensions contained HMP (0.25%, 1.75%, 3.25%), either on its own or combined with F (373 ppm F-) or F/Sn (800 ppm Sn2+, 373 ppm F-). One suspension contained sodium gluconate only (NegContr). After 10 days, specimens' surfaces were analysed with profilometry, energy dispersive X-ray spectroscopy, and scanning electron microscopy. Tissue loss (µm, mean ± standard deviation) in NegContr was 10.9 ± 2.0 (erosion), 22.2 ± 1.6 (erosion-abrasion). Under erosive conditions, only 0.25% HMP in any combination and 1.75% HMP with F/Sn reduced loss significantly (-28% to -54%); 3.25% HMP without F and F/Sn increased loss significantly (+35%). With additional abrasion, no suspension reduced loss significantly compared to NegContr, instead, in groups without F and F/Sn or with 3.25% HMP loss was increased (+15% to +30%). Conclusively, at higher concentrations, HMP increased erosive tooth wear and seemed to reduce anti-erosive effects of fluoride and stannous ions.