Effect of fence tray matching care on excess adhesive and bracket placement accuracy for orthodontic bonding: an in vitro study.

OBJECTIVE: This study aimed to evaluate the effect of fence tray matching care (FTMC) in bracket bonding by measuring excess adhesive, as well as linear and angular deviations, and by comparing it with the half-wrapped tray (HWT). MATERIALS AND METHODS: An intraoral scanner was used to acquire data on the maxillary dental arch of a patient with periodontitis.Furthermore, 20 maxillary dental arch models were 3D printed. Using 3Shape, PlastyCAD software, and 3D printing technology, 10 FTMC (method I) and HWT (method II) were obtained. By preoperative preparation, intraoperative coordination, and postoperative measurement, the brackets were transferred from the trays to the 3D-printed maxillary dental arch models. Additionally, the bracket's excess adhesive as well as linear and angular deviations were measured, and the differences between the two methods were analyzed. RESULTS: Excess adhesive was observed in both methods, with FTMC showing less adhesive (P< 0.001), with a statistical difference. Furthermore, HWT's vertical, tip and torque, which was significantly greater than FTMC (P< 0.05), with no statistical difference among other respects. The study data of incisors, canines, and premolars, showed that the premolars had more adhesive residue and were more likely to have linear and angular deviations. CONCLUSIONS: The FTMC had higher bracket bonding effect in comparison to HWT, and the adhesive residue, linear and angular deviations are smaller. The fence tray offers an intuitive view of the precise bonding of the bracket, and can remove excess adhesive to prevent white spot lesions via care, providing a different bonding method for clinical applications.

Does surface priming increase the bond strength of orthodontic brackets? An experimental study.

OBJECTIVE: To evaluate the effects of metal primer II (MP II) on the shear bond strength (SBS) of orthodontic brackets bonded to teeth and bis-acryl composite provisional material (Bis-Acryl). MATERIAL AND METHODS: Twenty extracted human premolars specimens and 20 premolar shaped Bis-Acryl specimens were obtained and randomly divided into two surface groups. The first group consisted of human premolars (T) bonded to brackets in the conventional way while in the second (T-MP) MP II was applied on the bracket base before bonding. Similarly, one group of provisional material (PM) was prepared according to conventional treatment and another with the application of MP-II metal bonder (PM-MP). In all cases Ortho-brackets (Victory Series, 3 M) were bonded employing Transbond XT resin cement. Then the brackets were debonded under shear and the results were statistically analyzed by two-way analysis of variance and Holm Sidak at α = .05. The debonded surfaces of all specimens were examined by light microscopy and the Adhesive Remnant Index (ARI) was recorded. RESULTS: The SBS results exhibited significant differences er (p < .001). For both the T and TM the application of MP-II increased the SBS compared to respective control groups (p < .001). The T-C group was found inferior compared to PM-C (p < .001) and the same is true for the comparison between T-MP and PM-MP (p < .001). ARI indexes demonstrated that the tooth groups were characterized by a predominantly adhesive failure at the resin-dentin interface. In contrast, the control group for provisional crowns (PM-C) showed a predominantly cohesive failure mode, which moved to predominantly adhesive after the application of MP II. CONCLUSION: The application of MP II enhances the SBS on both, human enamel and provisional crown materials.

Effect of water glass treatment for zirconia and silane coupling on bond strength of resin cement.

OBJECTIVE: To evaluate the ability of the water glass treatment to penetrate zirconia and improve the bond strength of resin cement. MATERIAL AND METHODS: Water glass was applied to zirconia specimens, which were then sintered. The specimens were divided into water-glass-treated and untreated zirconia (control) groups. The surface properties of the water-glass-treated specimens were evaluated using surface roughness and electron probe micro-analyser (EPMA) analysis. A resin cement was used to evaluate the tensile bond strength, with2 and without a silane-containing primer. After 24 h in water storage at 37 °C and thermal cycling, the bond strengths were statistically evaluated with t-test, and the fracture surfaces were observed using SEM. RESULTS: The water glass treatment slightly increased the surface roughness of the zirconia specimens, and the EPMA analysis detected the water glass penetration to be 50 µm below the zirconia surface. The application of primer improved the tensile bond strength in all groups. After 24 h, the water-glass-treated zirconia exhibited a tensile strength of 24.8 ± 5.5 MPa, which was significantly higher than that of the control zirconia (17.6 ± 3.5 MPa) (p < 0.05). After thermal cycling, the water-glass-treated zirconia showed significantly higher tensile strength than the control zirconia. The fracture surface morphology was mainly an adhesive pattern, whereas resin cement residue was occasionally detected on the water-glass-treated zirconia surfaces. CONCLUSION: The water glass treatment resulted in the formation of a stable silica phase on the zirconia surface. This process enabled silane coupling to the zirconia and improved the adhesion of the resin cement.

The multi-luting concept: a new approach to facilitate the adhesive luting of multiple indirect restorations.

Bonded indirect restorations can be difficult to lute in an accurate position due to the lack of preparation geometry. Furthermore, while the use of a rubberdam has been proven to be the best technique for providing the most efficient conditions for adhesive luting, its use often requires the use of secondary clamps, which do not allow the operator to lute more than two prosthetic pieces at the same time. The multi-luting concept is a pragmatic approach that of- fers the possibility to deliver several, if not all restorations, to be bonded at the same time, thus ensuring their correct positioning.

Effect of surface treatment and resin cement type on the bond strength of polyetheretherketone to lithium disilicate ceramic.

BACKGROUND: This study aims to evaluate the effect of surface treatment and resin cement on the shear bond strength (SBS) and mode of failure of polyetheretherketone (PEEK) to lithium disilicate ceramic (LDC). This is suggested to study alternative veneering of PEEK frameworks with a ceramic material. METHODS: eighty discs were prepared from PEEK blank and from lithium disilicate ceramic. Samples were divided into four groups according to surface treatment: Group (A) air abraded with 110 µm Al2O3, Group (AP) air abrasion and primer application, Group (S) 98% sulfuric acid etching for 60 s, Group (SP) Sulfuric acid and primer. Each group was subdivided into two subgroups based on resin cement type used for bonding LDC:1) subgroup (L) self- adhesive resin cement and 2) subgroup (B) conventional resin cement (n = 10). Thermocycling was done for all samples. The bond strength was assessed using the shear bond strength test (SBS). Failure mode analysis was done at 50X magnification with a stereomicroscope. Samples were chosen from each group for scanning electron microscope (SEM). The three-way nested ANOVA followed by Tukey's post hoc test were used for statistical analysis of results. Comparisons of effects were done utilizing one way ANOVA and (p < 0.05). RESULTS: The highest mean of shear bond strength values was demonstrated in Group of air abrasion with primer application using conventional resin cement (APB) (12.21 ± 2.14 MPa). Sulfuric acid groups showed lower shear bond strength values and the majority failed in thermocycling especially when no primer was applied. The failure mode analysis showed that the predominant failure type was adhesive failure between cement and PEEK, while the remaining was mixed failure between cement and PEEK. CONCLUSION: The air abrasion followed by primer application and conventional resin cement used for bonding Lithium Disilicate to PEEK achieved the best bond strength. Primer application did not have an effect when self-adhesive resin cement was used in air-abraded groups. Priming step is mandatory whenever sulfuric acid etching surface treatment is utilized for PEEK.

Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

Effect of Various Surface Treatments of Zirconia on its Adhesive Properties to Dentin: An In Vitro Study.

AIM: To assess the effectiveness of various surface treatments and adhesives on the bond strength of zirconia-based ceramic to dentin. MATERIALS AND METHODS: Eighty samples of zirconia were subjected to the four-surface treatment protocols (sandblasting, 48% hydrofluoric acid (HF), 48% hydrofluoric acid + 70% nitric acid (HNO3) and no treatment (control) following which the samples from each group were subdivided into two subgroups (n = 10) based on the resin cement employed for cementation (RelyX U200 and G-Cem Linkforce). The bonded specimens were subjected to shear stress to measure the bond strength using Universal testing machine. To test the difference in bond strength among the eight study groups, the Kruskal-Wallis ANOVA test was applied and for comparison between cements in each group, Mann-Whitney U test was applied. RESULTS: The highest bond strength values were observed for 48% HF group cemented with G-Cem Linkforce resin cement (16.220 ± 1.574) and lowest for control group-RelyX (4.954 ± 0.972). G-Cem cement showed higher bond strength than RelyX for all surface treatments except 48% HF + 70% nitric acid. CONCLUSION: It can be inferred that 48% HF can etch zirconia and generate a porous structure that proves to be beneficial for bonding. CLINICAL SIGNIFICANCE: The increasing demand for esthetics has led to the replacement of metal-ceramic materials with zirconia-based ceramics. However, the chemical inertness of zirconia to various conventional surface treating agents has continuously challenged researchers to discover a new surface treatment protocol that could enhance the bond strength of zirconia. How to cite this article: Yenamandra MS, Joseph A, Singh P, et al. Effect of Various Surface Treatments of Zirconia on its Adhesive Properties to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):226-230.

Restoration of Complicated Crown-Root Fracture in a Primary Incisor with Fragment Reattachment.

In traumatic dental injuries in children, due to a lack of maturity to cope with the situation, pain intolerance, amount of treatment procedure, and parental anxiety, simplified and non-invasive treatment procedures, such as biologic restorations, are useful. Using advanced adhesive material for fragment reattachment provides excellent esthetic results and a positive attitude from the patient and family. The purpose of this case report is to describe the biological restoration of a complicated crown-root fracture of a primary maxillary central incisor with the fragment reattachment technique.

Bleaching versus color change resistant adhesive in the discoloration of bracket-bonded tooth surfaces: an in vitro study.

OBJECTIVES: The aim of this study was to compare the effect of office bleaching of teeth bonded with Transbond XTTM (3M Unitek, Monrovia, CA, USA) (TRXT) and the use of color change resistant Orthocem (FGM, Joinville, Brazil) in bracket bonding on coffee-induced enamel discoloration. MATERIALS AND METHODS: Eighty premolars were distributed in equal numbers (n = 20) to group 1 (TRXT + distilled water), group 2 (TRXT + coffee solution), group 3 (TRXT + coffee solution + bleaching), and group 4 (Orthocem + coffee solution). Color was measured using a SpectroShade Micro (MHT, International, Verona, Italy) device at the beginning (T0), after coloring (T1), after bleaching (T1B), and after debonding (T2). ΔE color change values were calculated as T1-T0, T1B-T0 and T2-T0 differences. The conformity of the data to the normal distribution was examined with the Shapiro-Wilk test. Multiple comparisons were made with Tamhane's T2 test and Tukey's HSD test using one-way analysis of variance in the comparison of normally distributed data, and multiple comparisons were made with Dunn's test using the Kruskal-Wallis H test for comparison of non-normally distributed data. The significance level was set at p < 0.050. RESULTS: A statistically significant (p < 0.001) difference was found between the T1-T0 and T2-T0 stages for group 1-4 ΔE values. A statistically significant (p < 0.001) difference was also found when the T1B-T0 ΔE values of group 3 were compared with the T1-T0 ΔE values of groups 1, 2, and 4. CONCLUSIONS: After coffee-induced enamel discoloration, bleaching of teeth bonded with TRXT produced acceptable color difference of the incisal, middle, and gingival regions of the crown. In teeth bonded with Orthocem, acceptable color difference was seen only in the middle of the crown. CLINICAL RELEVANCE: The presented study will guide the clinician on how enamel discoloration side effect of fixed orthodontic appliance can reduce.

Effects of different primers and colouring solutions on orthodontic bonding: shear bond strength and colour change.

OBJECTIVES: This in vitro study evaluated the effect of different colouring solutions and primer systems used in the bonding of brackets on enamel colour change and bond strength. MATERIALS AND METHODS: 120 premolar teeth were divided into four main groups; brackets were bonded with 37% orthophosphoric acid + Transbond XT Primer in Group 1, 3 M Single Bond Universal in Group 2, Transbond Plus SEP in Group 3, and G-Premio Bond in Group 4. Each group was divided into three subgroups, and the teeth were placed in a cup containing coffee and tea mixture, in a cup containing cola and in distilled water. A bond strength test was applied to all teeth. Colour measurements of all teeth were performed at 2 different times: before bonding and after the bond strength test. RESULTS: The average bond strength of the 37% orthophosphoric acid group was higher than that of the other groups. The effect of primer and solution groups on colour change was statistically significant (p = 0.001 and p = 0.023, respectively). CONCLUSIONS: In this study, the bond strength was clinically sufficient in all primer groups. The highest colour change was observed when the tea-coffee solution and Transbond Plus SEP primer were used. CLINICAL RELEVANCE: This study has identified enamel discoloration and bond strength from different colouring solutions and primer systems used for bonding braces, which can be used to inform clinicians and patients to achieve better treatment results.

Effect of Salvadora persica on resin-dentin bond stability.

BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.

Shear bond strength of adhesive cement to zirconia: Effect of added proportion of yttria for stabilization.

STATEMENT OF PROBLEM: Zirconium dioxide (zirconia) cannot be etched in a clinical setting, but zirconia restorations with minimal to no micromechanical bonding are approved and widely used in contemporary dentistry. However, information on the shear bond strength of zirconia and adhesive cement, on the effect of an added proportion of yttria, and on the effect of aging is lacking. PURPOSE: The purpose of this in vitro study was to evaluate the shear bond strength of cement luted to zirconia and the effect of aging. MATERIAL AND METHODS: A total of 131 test specimens were made from 4 zirconia materials with different amounts of yttria added to formulate yttria-partially stabilized zirconia (Y-PSZ); 3Y-PSZ (n=32), 4Y-PSZ (n=34), and 2 5Y-PSZs (n=32 and n=33). A dual-polymerizing cement and 10-methacryloyloxydecyl dihydrogen phosphate-containing primer were used. All specimens were stored in water at 37 °C, half of them for 24 hours and the other half for 6 months. After aging, the specimens were subjected to a shear bond strength test with a notched crosshead according to the International Organization for Standardization (ISO) 29022:2013 standard. The data were analyzed using the independent 2-sample t test, ANOVA, and the Levene test (α=.05). RESULTS: The 3Y-PSZ material had higher mean ±standard deviation shear bond strength (31.83 ±12.80 MPa) compared with 4Y-PSZ (23.34 ±7.66 MPa) after 24 hours of aging in water and higher (28.98 ±14.03 MPa) than 4Y-PSZ (14.35 ±9.62 MPa) and one of the 5Y-PSZ (16.05 ±11.34 MPa) after 6 months. Debonding before loading occurred in all groups except for one of the 5Y-PSZ groups. CONCLUSIONS: Zirconia without macromechanical retention, regardless of an added proportion of yttria, showed high shear bond strength, but the tested materials also had a high coefficient of variance, which, in practice, leads to the risk of the occasional debonding of zirconia restorations.

Influence of different immediate dentin sealing strategies on bond strength of indirect resin nanoceramic restorations.

In this study, we evaluated the effect of four different strategies for bonding a CAD/CAM resin nanoceramic restoration (Lava Ultimate, 3M) to the dentin surface using a universal adhesive (Scotch Bond Universal, 3M) and adhesive resin cement (RelyX Ultimate, 3M) on the shear bond strength (SBS) and failure mode. The strategies comprised: (i) immediate sealing, immediate bonding; (ii) immediate sealing, bonding after 2 weeks with provisional restoration; (iii) immediate sealing with flowable resin composite reinforcement and bonding after 2 weeks with provisional restoration; and (iv) no immediate sealing, and bonding after 2 weeks with provisional restoration. After bonding, all the specimens were thermocycled, shear tests were performed using a universal testing machine, and failure modes were determined using stereomicroscope and scanning electron microscopy. The highest mean SBS was recorded with immediate sealing, immediate bonding strategy. Most adhesive failures with exposed dentinal tubules were noted in specimens exposed to bonding after 2 weeks with no immediate sealing, which was associated with the lowest SBS. Mixed failures predominated in all immediate dentin sealing groups. Immediate sealing with universal adhesives improves SBS, particularly in the single-visit approach, which has shown significantly better performance, whereas the provisional phase has a negative effect.

Adhesion of tooth fragment after trauma: effect of adhesion strategy and storage in the rescue box.

This study aims to investigate the impact of storage conditions for crown fragments (specifically, whether they were stored within a tooth rescue box or in tap water) on their adhesion to fractured teeth when subjected to two different adhesive systems (namely, total etch and self etch). Sixty maxillary premolars were sectioned to obtain tooth fragments. These fragments were stored briefly (2 hours) and reattached in the following groups: Group 1 (fragments stored in tooth rescue box and reattached with etch and rinse (E&R) technique), Group 2 (fragments stored in tap water and reattached with E&R technique), Group 3 (fragments stored in tooth rescue box and reattached with self-etch (SE) technique), and Group 4 (fragments stored in tap water and reattached SE technique). After reattachment, the bonded tooth fragments underwent thermal cycling (500 cycles, 5-55 °C) and bond strength testing using a universal testing machine. Two-way Analysis of Variance (ANOVA) and Tukey's tests were used for bond strength comparison (p ≤ 0.05). A two-parameter Weibull distribution was conducted to evaluate the reliability of the storage medium and adhesion modality on bond strength. The results showed that measured shear bond values (MPa ± Standard deviation (SD); arranged in descending order) for each group were: Group 2 (Tap water/E&R = 6.5 ± 2.1), Group 1 (Rescue box/E&R = 6.0 ± 2.5), Group 4 (Tap water/E&R = 5.1 ± 2.8), and Group 3 (Rescue box/SE = 3.6 ± 3.2). Significant differences were found only between Groups 2 and 3 (p = 0.002). In conclusion, storing crown fragments in a tooth rescue box did not significantly affect the shear bond strength of the restored tooth. However, fragments reattached using the self-etch technique showed comparable shear bond strength but a higher rate of adhesive failures compared to the E&R technique.

Influence of airborne particle abrasion on dentin bonding effectiveness of a 2-step universal adhesive.

OBJECTIVE: To determine the effect of airborne particle abrasion (APA) on micro-tensile bond strength (µTBS) to dentin using different air-abrasion/polishing powders. METHODS: The bonding effectiveness of G2 Bond Universal (G2B), used in etch-and-rinse (E&R) and self-etch mode (SE), was tested on bur-cut dentin and dentin air abraded/polished using six different powders (aluminum oxide 29 µm (AO29) and 53 µm (AO53), aluminum trihydroxide (AT), sodium bicarbonate (SB), sodium bicarbonate soft (SBsoft) and bioactive glass (BG); Velopex). Adhesive-composite resin specimens were immersed in distilled water at 37 °C for one week and cut into microspecimens. Half of the specimens were subjected to 50,000 thermocycles (aged). Immediate and aged µTBS to dentin were measured. Statistical analysis was performed using linear mixed-effects (LME) modeling (p < 0.05). RESULTS: Comparing the aged bond strengths to air-abraded/polished dentin with bur-cut dentin, pretreatment with SB and SBsoft in combination with G2B used in E&R mode, and BG air polishing in combination with both application modes (E&R, SE), resulted in a significantly higher bond strength. Dentin bond strength was only significantly lower when air abraded with AO29 and using G2B in SE mode. Aging did not significantly influence bond strength for both application modes (E&R, SE), except for AO29 and AT-treated dentin, where bond strengths decrea sed significantly using G2B in SE mode. In general, G2B reached significantly higher bond strengths on air-abraded/polished dentin in E&R mode than in SE mode. CONCLUSION: Air-abrasion/polishing did not impair dentin bond strength using G2B, except when dentin was air abraded with AO29 and using G2B in SE mode. Air polishing positively influenced the bond strength to dentin in specific groups. CLINICAL SIGNIFICANCE: APA is safe concerning bonding to dentin. The E&R application mode is preferred using G2B as adhesive on air-abraded/polished dentin. Air polishing with BG positively influenced dentin bond strength for both application methods.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Effect of ultrasonic and sonic instrumentation on shear bond strength of resin composite to enamel: An in vitro study.

PURPOSE: To assess and compare the effects of sonic and ultrasonic instrumentation on shear bond strength (SBS) and investigate the influence of adhesive system application modes (etch&rinse/self-etch) on SBS. METHODS: In this experimental study, 45 extracted sound human molars were selected. Mesial and distal surfaces of the teeth were abraded until 90 smooth enamel surfaces were obtained. Specimens were divided into two groups, with half (N= 45) conditioned in etch&rinse mode and the remaining (N= 45) in self-etch mode using Tetric N Bond Universal. Composite resin discs were produced on these surfaces by filling Teflon molds. All specimens were aged via thermocycling. Each group was further divided into three more groups (n= 15) according to the type of periodontal instrumentation (ultrasonic, sonic or none). SBS values were recorded and analyzed using two-way ANOVA. Fracture sites were examined under a stereomicroscope. RESULTS: The type of periodontal instrumentation had no significant effect on SBS values, whether sonic, ultrasonic or their absence (P= 0.945). The type of adhesive system mode had a significant influence on the shear bond strength values. Etch&rinse groups had significantly higher shear bond strength values than self-etch groups (P< 0.001). CLINICAL SIGNIFICANCE: This study reassures practitioners that sonic and ultrasonic instruments are safe for enamel bonding and highlights the importance of selecting adhesive techniques for optimal restorative outcomes.

Effects of different surface treatments on surface topography and bond strength in the repair of fiber-reinforced dentin composite.

OBJECTIVE: This study aimed to evaluate the effects of different surface treatments on the repair bond strength between a fiber-reinforced dentin composite and a posterior composite. METHODS: Forty fiber-reinforced dentin composite resin blocks (4 mm × 4 mm × 4 mm) were separated into eight groups (n = 5) according to the surface preparation methods: (G1) negative control group, (G2) adhesive application, (G3) 50% dimethylsulfoxide (DMSO) application, (G4) 50% DMSO + adhesive application, (G5) 37% phosphoric acid etch + adhesive application, (G6) air abrasion + adhesive application, (G7) 37% phosphoric acid etch + 50% DMSO application + adhesive application, and (G8) air abrasion +50% DMSO application + adhesive application group. The composite surfaces were repaired in two layers with a posterior composite. Composite sticks were subjected to a micro tensile bond strength (µTBS) test. Fractured surfaces were evaluated using a stereomicroscope (×25). Short fiber-reinforced composite samples' surfaces were investigated by scanning electron microscope (SEM). Shapiro Wilk, one-way ANOVA, and Tukey HSD tests were used for statistical evaluation. RESULTS: The highest average (µTBS) values were observed in G8, whereas the lowest mean µTBS values were evident in the G1 group. Statistically significant µTBS values were found in all adhesive-applied groups when compared with the negative control group. Notably, the application of 50% DMSO without adhesive did not lead to a statistically significant increase in µTBS values. SEM images demonstrated that acid etching partially eliminated residues on the composite surface, while air abrasion had a detrimental effect on the integrity of fiber structures. CONCLUSION: In the repair of fiber-reinforced dentin composite with a posterior composite, adhesive application is an effective approach. The treatment of 50% DMSO without adhesive did not confer a statistically significant advantage, and the supplemental use of acid etch or air abrasion did not show an additional benefit compared to adhesive-only repairs. CLINICAL SIGNIFICANCE: Adhesive application emerges as a potent and effective strategy for the repair of bur-roughened fiber-reinforced dentin composites. With its limitations, the study highlights the efficacy of adhesive-only repairs without the necessity for additional surface treatments.

Assessing push-out bond strength in re-irradiated teeth: Universal resin cement performance in self-etch and self-adhesive modes.

OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.