Bioinspired Photoelectronic Synergy Coating with Antifogging and Antibacterial Properties.

Optically transparent glass with antifogging and antibacterial properties is in high demand for endoscopes, goggles, and medical display equipment. However, many of the previously reported coatings have limitations in terms of long-term antifogging and efficient antibacterial properties, environmental friendliness, and versatility. In this study, inspired by catfish and sphagnum moss, a novel photoelectronic synergy antifogging and antibacterial coating was prepared by cross-linking polyethylenimine-modified titanium dioxide (PEI-TiO2), polyvinylpyrrolidone (PVP), and poly(acrylic acid) (PAA). The as-prepared coating could remain fog-free under hot steam for more than 40 min. The experimental results indicate that the long-term antifogging properties are due to the water absorption and spreading characteristics. Moreover, the organic-inorganic hybrid of PEI and TiO2 was first applied to enhance the antibacterial performance. The Staphylococcus aureus and the Escherichia coli growth inhibition rates of the as-prepared coating reached 97 and 96% respectively. A photoelectronic synergy antifogging and antibacterial mechanism based on the positive electrical and photocatalytic properties of PEI-TiO2 was proposed. This investigation provides insight into designing multifunctional bioinspired surface materials to realize antifogging and antibacterial that can be applied to medicine and daily lives.

Does surface priming increase the bond strength of orthodontic brackets? An experimental study.

OBJECTIVE: To evaluate the effects of metal primer II (MP II) on the shear bond strength (SBS) of orthodontic brackets bonded to teeth and bis-acryl composite provisional material (Bis-Acryl). MATERIAL AND METHODS: Twenty extracted human premolars specimens and 20 premolar shaped Bis-Acryl specimens were obtained and randomly divided into two surface groups. The first group consisted of human premolars (T) bonded to brackets in the conventional way while in the second (T-MP) MP II was applied on the bracket base before bonding. Similarly, one group of provisional material (PM) was prepared according to conventional treatment and another with the application of MP-II metal bonder (PM-MP). In all cases Ortho-brackets (Victory Series, 3 M) were bonded employing Transbond XT resin cement. Then the brackets were debonded under shear and the results were statistically analyzed by two-way analysis of variance and Holm Sidak at α = .05. The debonded surfaces of all specimens were examined by light microscopy and the Adhesive Remnant Index (ARI) was recorded. RESULTS: The SBS results exhibited significant differences er (p < .001). For both the T and TM the application of MP-II increased the SBS compared to respective control groups (p < .001). The T-C group was found inferior compared to PM-C (p < .001) and the same is true for the comparison between T-MP and PM-MP (p < .001). ARI indexes demonstrated that the tooth groups were characterized by a predominantly adhesive failure at the resin-dentin interface. In contrast, the control group for provisional crowns (PM-C) showed a predominantly cohesive failure mode, which moved to predominantly adhesive after the application of MP II. CONCLUSION: The application of MP II enhances the SBS on both, human enamel and provisional crown materials.

Moldable Tissue-Sealant Hydrogels Composed of In Situ Cross-Linkable Polyethylene Glycol via Thiol-Michael Addition and Carbomers.

Moldable tissue-sealant hydrogels were developed herein by combining the yield stress fluidity of a Carbomer and in situ cross-linking of 3-arm PEG-thiol (PEG-SH) and 4-arm PEG-acrylate (PEG-AC). The Carbomer was mixed with each PEG oligomer to form two aqueous precursors: Carbomer/PEG-SH and Carbomer/PEG-AC. The two hydrogel precursors exhibited sufficient yield stress (>100 Pa) to prevent dripping from their placement on the tissue surface. Moreover, these hydrogel precursors exhibited rapid restructuring when the shear strain was repeatedly changed. These rheological properties contribute to the moldability of these hydrogel precursors. After mixing these two precursors, they were converted from yield-stress fluids to chemically cross-linked hydrogels, Carbomer/PEG hydrogel, via thiol-Michael addition. The gelation time was 5.0 and 11.2 min at 37 and 25 °C, respectively. In addition, the Carbomer/PEG hydrogels exhibited higher cellular viability than the pure Carbomer. They also showed stable adhesiveness and burst pressure resistance to various tissues, such as the skin, stomach, colon, and cecum of pigs. The hydrogels showed excellent tissue sealing in a cecum ligation and puncture model in mice and improved the survival rate due to their tissue adhesiveness and biocompatibility. The Carbomer/PEG hydrogel is a potential biocompatible tissue sealant that surgeons can mold. It was revealed that the combination of in situ cross-linkable PEG oligomers and yield stress fluid such as Carbomer is effective for developing the moldable tissue sealant without dripping of its hydrogel precursors.

Effectiveness of experimental dentifrices based on essential oils on biofilm on complete dentures: an in vitro study.

Specific products containing natural resources can contribute to the innovation of complete denture hygiene. OBJECTIVE: To conduct an in vitro evaluation of experimental dentifrices containing essential oils of Bowdichia virgilioides Kunth (BvK), Copaifera officinalis (Co), Eucalyptus citriodora (Ec), Melaleuca alternifolia (Ma) and Pinus strobus (Ps) at 1%. METHODOLOGY: The variables evaluated were organoleptic and physicochemical characteristics, abrasiveness (mechanical brushing machine) simulating 2.5 years, and microbial load (Colony Forming Units - CFU/mL), metabolic activity (XTT assay) and cell viability (Live/Dead® BacLight™ kit) of the multispecies biofilm (Streptococcus mutans: Sm, Staphylococcus aureus: Sa, Candida albicans: Ca and Candida glabrata: Cg). Specimens of heat-polymerized acrylic resins (n=256) (n=96 specimens for abrasiveness, n=72 for microbial load count, n=72 for biofilm metabolic activity, n=16 for cell viability and total biofilm quantification) with formed biofilm were divided into eight groups for manual brushing (20 seconds) with a dental brush and distilled water (NC: negative control), Trihydral (PC: positive control), placebo (Pl), BvK, Co, Ec, Ma or Ps. After brushing, the specimens were washed with PBS and immersed in Letheen Broth medium, and the suspension was sown in solid specific medium. The organoleptic characteristics were presented by descriptive analysis. The values of density, pH, consistency and viscosity were presented in a table. The data were analyzed with the Wald test in a generalized linear model, followed by the Kruskal-Wallis test, Dunn's test (mass change) and the Bonferroni test (UFC and XTT). The Wald test in Generalized Estimating Equations and the Bonferroni test were used to analyze cell viability. RESULTS: All dentifrices showed stable organoleptic characteristics and adequate physicochemical properties. CN, Ec, Ps, Pl and PC showed low abrasiveness. There was a significant difference between the groups (p<0.001) for microbial load, metabolic activity and biofilm viability. CONCLUSIONS: It was concluded that the BvK, Ec and Ps dentifrices are useful for cleaning complete dentures, as they have antimicrobial activity against biofilm. The dentifrices containing Bowdichia virgilioides Kunth showed medium abrasiveness and should be used with caution.

Targeted photodynamic therapy technique of Janus nanoparticles on breast cancer.

Spherical gold/polyacrylic acid (Au/PAA) polymer-inorganic Janus nanoparticles (JNPs) with simultaneous therapeutic and targeting functions were fabricated. The obtained Au/PAA JNPs were further selectively functionalized with folic acid (FA) and thiol PEG amine (SH-PEG-NH2) on Au sides to provide superior biocompatibility and active targeting, while the other PAA sides were loaded with 5-aminolevulinic acid (5-ALA) to serve as a photosensitizer (PS) for photodynamic therapeutic (PDT) effects on MCF-7 cancer cells. The PS loading of 5-ALA was found to be 83% with an average hydrodynamic size and z-potential of 146 ± 0.8 nm and -6.40 mV respectively for FA-Au/PAA-ALA JNPs. The in vitro PDT study of the JNPs on MCF-7 breast cancer cells under 636 nm laser irradiation indicated the cell viability of 24.7% ± 0.5 for FA-Au/PAA-ALA JNPs at the IC50 value of 0.125 mM. In this regard, the actively targeted FA-Au/PAA-ALA JNPs treatment holds great potential for tumour therapy with high cancer cell-killing efficacy.

Vantris vs. deflux for treatment of paediatric vesicoureteral reflux: Efficacy and obstruction risk.

INTRODUCTION: The aim was to compare the efficacy of polyacrylate polyalcohol copolymer (PPC) injections and dextranomer/hyaluronic acid (Dx/Ha) injections for the endoscopic treatment of vesicoureteral reflux in children. MATERIAL: This retrospective cohort study included 189 young patients who had endoscopic treatment for vesicoureteral reflux from January 2012 to December 2019 in our center. Among them, 101 had PCC injections and 88 had Dx/Ha injections. Indications for treatment were vesicoureteral reflux with breakthrough urinary tract infection or vesicoureteral reflux with renal scarring on dimercaptosuccinic acid (DMSA) renal scan. Endoscopic injection was performed under the ureteral meatus. Early complications, recurrence of febrile urinary tract infection and vesicoureteral reflux after endoscopic injection, ureteral obstruction and reintervention were evaluated and compared between groups. RESULTS: Endoscopic treatment was successful in 90.1% of patients who had PPC injection and in 82% of patients who had Dx/Ha injection. Four patients presented a chronic ureteral obstruction after PPC injection, one with a complete loss of function of the dilated kidney. One patient in the Dx/Ha group presented a postoperative ureteral dilatation after 2 injections. CONCLUSION: Despite a similar success rate after PPC and Dx/Ha injections for endoscopic treatment of VUR, there may be a greater risk of postoperative ureteral obstruction after PPC injections. The benefit of using PPC to prevent febrile UTI and renal scarring in children with low-grade VUR does not seem to outweigh the risk of chronic ureteral obstruction.

A novel acrylic orthodontic device for treatment of linguoverted mandibular canine teeth in small dogs.

Linguoverted mandibular canine teeth (LMC) is a common malocclusion in dogs. Several inclined bite-plane techniques using acrylic resin have been introduced to correct LMC in dogs. Although these techniques have suggested modifications to overcome shortcomings, there are still limitations; e.g., high technical sensitivity, as the viscous acrylic resin must still be fabricated in the oral cavity. The authors developed a novel method for small-breed dogs that uses a doughy acrylic resin form to achieve an easy intraoral design and extraoral fabrication. Eight small-breed dogs were presented to evaluate and treat malocclusion causing palatal trauma. First, a Class-1 malocclusion with linguoversion of the mandibular canine teeth (6 dogs with unilateral LMC and 2 dogs with bilateral) was diagnosed based on oral examination. Dogs were treated with the new method using a doughy acrylic resin form for 6 to 7 wk and had posttreatment follow-up 1 y after the procedure. All treated canine teeth were in correct positions 1 y after the appliances were removed. Key clinical message: The authors believe that the new method using a doughy acrylic resin form could be a good alternative for veterinarians to use when treating LMC.

Un nouveau dispositif orthodontique en acrylique pour le traitement des canines mandibulaires linguoverties chez les petits chiens. Les canines mandibulaires linguoverties (LMC) sont une malocclusion courante chez le chien. Plusieurs techniques de plan de morsure incliné utilisant de la résine acrylique ont été introduites pour corriger la LMC chez le chien. Bien que ces techniques aient suggéré des modifications pour surmonter les lacunes, elles présentent encore des limites; par exemple, une sensibilité technique élevée, car la résine acrylique visqueuse doit encore être fabriquée dans la cavité buccale. Les auteurs ont développé une nouvelle méthode pour les chiens de petite race qui utilise une forme pâteuse de résine acrylique pour obtenir une conception intra-orale et une fabrication extra-orale faciles. Huit chiens de petite race ont été présentés pour évaluer et traiter une malocclusion provoquant un traumatisme palatin. Tout d'abord, une malocclusion de classe 1 avec linguoversion des canines mandibulaires (6 chiens avec LMC unilatérale et 2 chiens avec bilatérale) a été diagnostiquée sur la base d'un examen oral. Les chiens ont été traités avec la nouvelle méthode en utilisant une forme pâteuse de résine acrylique pendant 6 à 7 semaines et ont fait l'objet d'un suivi post-traitement 1 an après la procédure. Toutes les canines traitées étaient dans la bonne position un an après le retrait des appareils.Message clinique clé:Les auteurs estiment que la nouvelle méthode utilisant une forme pâteuse de résine acrylique pourrait être une bonne alternative que les vétérinaires pourraient utiliser lors du traitement du LMC.(Traduit par Dr Serge Messier).

Dental biomaterials redefined: molecular docking and dynamics-driven dental resin composite optimization.

BACKGROUND: Dental resin-based composites are widely recognized for their aesthetic appeal and adhesive properties, which make them integral to modern restorative dentistry. Despite their advantages, adhesion and biomechanical performance challenges persist, necessitating innovative strategies for improvement. This study addressed the challenges associated with adhesion and biomechanical properties in dental resin-based composites by employing molecular docking and dynamics simulation. METHODS: Molecular docking assesses the binding energies and provides valuable insights into the interactions between monomers, fillers, and coupling agents. This investigation prioritizes SiO2 and TRIS, considering their consistent influence. Molecular dynamics simulations, executed with the Forcite module and COMPASS II force field, extend the analysis to the mechanical properties of dental composite complexes. The simulations encompassed energy minimization, controlled NVT and NPT ensemble simulations, and equilibration stages. Notably, the molecular dynamics simulations spanned a duration of 50 ns. RESULTS: SiO2 and TRIS consistently emerged as influential components, showcasing their versatility in promoting solid interactions. A correlation matrix underscores the significant roles of van der Waals and desolvation energies in determining the overall binding energy. Molecular dynamics simulations provide in-depth insights into the mechanical properties of dental composite complexes. HEMA-SiO2-TRIS excelled in stiffness, BisGMA-SiO2-TRIS prevailed in terms of flexural strength, and EBPADMA-SiO2-TRIS offered a balanced combination of mechanical properties. CONCLUSION: These findings provide valuable insights into optimizing dental composites tailored to diverse clinical requirements. While EBPADMA-SiO2-TRIS demonstrates distinct strengths, this study emphasizes the need for further research. Future investigations should validate the computational findings experimentally and assess the material's response to dynamic environmental factors.

Trypsin Encapsulation in the Zeolitic Imidazolate Framework for Low-Molecular Weight Protein Analysis with High Selectivity and Efficiency.

Low-molecular weight proteins (LWPs) are important sources of biological information in biomarkers, signaling molecules, and pathology. However, the separation and analysis of LWPs in complex biological samples are challenging, mainly due to their low abundance and the complex sample pretreatment procedure. Herein, trypsin modified by poly(acrylic acid) (PAA) was encapsulated by a zeolitic imidazolate framework (ZIF-L). Mesopores were formed on the ZIF-L with the introduction of PAA. An alternative strategy for separation and pretreatment of LWPs was developed based on the prepared ZIF-L-encapsulated trypsin with adjustable pore size. The mesoporous structure of the prepared materials selectively excluded high-molecular weight proteins from the reaction system, allowing LWPs to enter the pores and react with the internal trypsin, resulting in an improved separation efficiency. The hydrophobicity of the ZIF-L simplified the digestion process by inducing significant structural changes in substrate proteins. In addition, the enzymatic activity was significantly enhanced by the developed encapsulation method that maintained the enzyme conformation, allowed low mass transfer resistance, and possessed a high enzyme-to-substrate ratio. As a result, the ZIF-L-encapsulated trypsin can achieve highly selective separation, valid denaturation, and efficient digestion of LWPs in a short time by simply mixing with substrate proteins, greatly simplifying the separation and pretreatment process of the traditional hydrolysis method. The prepared materials and the developed strategy demonstrated an excellent size-selective assay performance in model protein mixtures, showing great potential in the application of proteomics analysis.

Development and in vitro/in vivo evaluation of famotidine hydrochloride bioadhesive sustained release suspension.

To develop a new kind of famotidine-resin microcapsule for gastric adhesion sustained release by screening out suitable excipients and designing reasonable prescriptions to improve patient drug activities to achieve the expected therapeutic effect. The famotidine drug resin was prepared using the water bath method with carbomer 934 used as coating material. Microcapsules were prepared using the emulsified solvent coating method and appropriate excipients were used to prepare famotidine sustained release suspension. Pharmacokinetics of the developed microcapsules were studied in the gastrointestinal tract of rats. The self-made sustained-release suspension of famotidine hydrochloride effectively reduced the blood concentration and prolonged the action time. The relative bioavailability of the self-made suspension of the famotidine hydrochloride to the commercially available famotidine hydrochloride was 146.44%, with an average retention time of about 5h longer, which indicated that the new suspension had acceptable adhesion properties. The findings showed that the newly developed famotidine-resin microcapsule increased the bioavailability of the drug with a significant sustained-release property.

Enhancing the coagulation process for the removal of microplastics from water by anionic polyacrylamide and natural-based Moringaoleifera.

The existence of microplastics (MPs) in water is a significant global concern since they have the potential to pose a threat to human health. Therefore, there is a need to develop a sustainable treatment technology for MPs removal, as the conventional methods are inadequate to address this problem. Coagulation is a typical process in treatment plants that can capture MPs before releasing them into the environment. In this work, the removal behaviors of polyamide (PA), polystyrene (PS), and polyethylene (PE) MPs were systematically investigated through coagulation processes using aluminum sulfate (Al2(SO4)3) and Moringa oleifera (MO) seeds extract. Subsequently, the coagulation performance of Al2(SO4)3 was improved by the separate addition of anionic polyacrylamide (APAM) and naturally derived MO. Results showed that Al2(SO4)3 in combination with APAM had better performance than Al2(SO4)3 or MO alone. In the Al2(SO4)3+APAM system, the removal efficiencies were 93.47%, 81.25%, and 29.48% for PA, PS, and PE MPs, respectively. Furthermore, the effectiveness of the Al2(SO4)3 and MO blended system was approximately similar to the Al2(SO4)3+APAM system. However, the required amount of Al2(SO4)3 was decreased to 50% in the Al2(SO4)3+MO system compared to the optimal dosage in the Al2(SO4)3 system alone. The combination of 40 mg/L of Al2(SO4)3 and 60 mg/L of MO resulted in removal efficiencies of 92.99%, 80.48%, and 28.94% for PA, PS, and PE MPs, respectively. The high efficacy of these enhanced methods was due to the synergic effects of charge neutralization and agglomeration adsorption, which were validated through zeta potential assessments and visual analysis using scanning electron microscopy (SEM) images. In the case of experimental conditions, initial pH had little impact on removal efficiency, while NaCl salinity and stirring speed directly affected MPs removal. Consequently, this research took a step toward finding a green strategy to remove MPs from water systems.

In vitro effects of wound-dressings on key wound healing properties of dermal fibroblasts.

Healing of complex wounds requires dressings that must, at least, not hinder and should ideally promote the activity of key healing cells, in particular fibroblasts. This in vitro study assessed the effects of three wound-dressings (a pure Ca2+ alginate: Algostéril®, a Ca2+ alginate + carboxymethylcellulose: Biatain alginate® and a polyacrylate impregnated with lipido-colloid matrix: UrgoClean®) on dermal fibroblast activity. The results showed the pure calcium alginate to be non-cytotoxic, whereas the other wound-dressings showed moderate to strong cytotoxicity. The two alginates stimulated fibroblast migration and proliferation, whereas the polyacrylate altered migration and had no effect on proliferation. The pure Ca2+ alginate significantly increased the TGF-ß-induced fibroblast activation, which is essential to healing. This activation was confirmed by a significant increase in Vascular endothelial growth factor (VEGF) secretion and a higher collagen production. The other dressings reduced these fibroblast activities. The pure Ca2+ alginate was also able to counteract the inhibitory effect of NK cell supernatants on fibroblast migration. These in vitro results demonstrate that tested wound-dressings are not equivalent for fibroblast activation. Only Algostéril was found to promote all the fibroblast activities tested, which could contribute to its healing efficacy demonstrated in the clinic.

Digital manufacturing techniques and the in vitro biocompatibility of acrylic-based occlusal device materials.

OBJECTIVES: Material chemistry and workflow variables associated with the fabrication of dental devices may affect the biocompatibility of the dental devices. The purpose of this study was to compare digital and conventional workflow procedures in the manufacturing of acrylic-based occlusal devices by assessing the cytotoxic potential of leakage products. METHODS: Specimens were manufactured by 3D printing (stereolithography and digital light processing), milling, and autopolymerization. Print specimens were also subjected to different post-curing methods. To assess biocompatibility, a human tongue epithelial cell line was exposed to material-based extracts. Cell viability was measured by MTT assay while Western blot assessed the expression level of selected cytoprotective proteins. RESULTS: Extracts from the Splint 2.0 material printed with DLP technology and post-cured with the Asiga Flash showed the clearest loss of cell viability. The milled and autopolymerized materials also showed a significant reduction in cell viability. However, by storing the autopolymerized material in dH2O for 12 h, no significant viability loss was observed. Increased levels of cytoprotective proteins were seen in cells exposed to extracts from the print materials and the autopolymerized material. Similarly to the effect on viability loss, storing the autopolymerized material in dH2O for 12 h reduced this effect. CONCLUSIONS/CLINICAL RELEVANCE: Based on the biocompatibility assessments, clinical outcomes of acrylic-based occlusal device materials may be affected by the choice of manufacturing technique and workflow procedures.

Nitrocellulose/acrylic resin coated screen-printed carbon electrode to construct a capacitive immunosensor for anti-BSA.

The capacitive immunosensor, known for its label-free simplicity, has great potential for point-of-care diagnostics. However, the interaction between insulation and recognition layers on the sensing electrode greatly affects its performance. This study introduces a pioneering dual-layer strategy, implementing a novel combination of acrylic resin (AR) and nitrocellulose (NC) coatings on screen-printed carbon electrodes (SPCEs). This innovative approach not only enhances the dielectric properties of the capacitive sensor but also streamlines the immobilization of recognizing elements. Particularly noteworthy is the superior reliability and insulation offered by the AR coating, surpassing the limitations of traditional self-assembled monolayer (SAM) modifications. This dual-layer methodology establishes a robust foundation for constructing capacitive sensors optimized specifically for liquid medium-based biosensing applications. The NC coating in this study represents a breakthrough in effectively immobilizing BSA, unraveling the capacitive response intricately linked to the quantity of adsorbed recognizing elements. The results underscore the prowess of the proposed immunosensor, showcasing a meticulously defined linear calibration curve for anti-BSA (ranging from 0 to 25 µg/ml). Additionally, specific interactions with anti-HAS and anti-TNF-α further validate the versatility and efficacy of the developed immunosensor. This work presents a streamlined and highly efficient protocol for developing label-free immunosensors for antibody determination and introduces a paradigm shift by utilizing readily available electrodes and sensing systems. The findings are poised to catalyze a significant acceleration in the advancement of biosensor technology, opening new avenues for innovative applications in point-of-care diagnostics.

Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study.

AIM: The aim of the study is to determine the difference in the shear bond strengths to dentin among dental composite (Filtek Z350®, 3M), compomer (Dyract Flow®, Dentsply) and Giomer (Beautifil®, Shofu) with 3MTM Single BondTM Universal Adhesive (SBU) (7th generation, self-etch, single solution adhesive) and AdperTM Single Bond 2 Adhesive (ASB) (5th generation, total-etch, two solution adhesive). MATERIALS AND METHODS: Sixty extracted human permanent teeth were collected, cleansed of debris, and placed in distilled water. The samples were segregated into two groups depicting the two bonding agents-AdperTM (ASB) and 3MTM Single Bond Universal (SBU) and sub-grouped into three groups depicting the three restorative materials (Composite, Giomer, and Compomer) used. Groups were respresented as follows: Group I-ASB + Composite; Group II-ASB + Giomer; Group III-ASB + Compomer; Group IV-SBU + Giomer; Group V-SBU + Compomer; Group VI-SBU + Composite. After applying the bonding agent as per the manufacturer's instructions, following which the restorative material was placed. A Universal Testing Machine (Instron 3366, UK) was employed to estimate the shear bond strength of the individual restorative material and shear bond strengths were calculated. RESULTS: Composite bonded with SBU (group VI) displayed the greatest shear strength (11.16 ± 4.22 MPa). Moreover, Giomers and flowable compomers displayed better bond strengths with ASB compared with their SBU-bonded counterparts. CONCLUSION: These results mark the importance of careful material selection in clinical practice and the bonding agent used to achieve optimal bond strength and enhance the clinical longevity and durability of dental restorations. CLINICAL SIGNIFICANCE: From a clinical perspective, to avoid a compressive or a shear failure, it would be preferrable to use a direct composite restorative material with SBU (Single bond universal adhesive, 7th generation) to achieve maximum bond strength. How to cite this article: Kuchibhotla N, Sathyamoorthy H, Balakrishnan S, et al. Effect of Bonding Agents on the Shear Bond Strength of Tooth-colored Restorative Materials to Dentin: An In Vitro Study. J Contemp Dent Pract 2024;25(3):245-249.

Assessment of Adaptability and Linear Dimensional Changes of Two Heat Cure Denture Base Resin with Different Cooling Techniques: An In Vitro Study.

AIM: The current study was designed to assess the linear dimensional changes and adaptability of two heat-cured denture base resins using various cooling methods. MATERIALS AND METHODS: To prepare a total of 90 acrylic resin samples (45 acrylic resin samples for each material), four rectangular stainless-steel plates measuring 25 × 25 × 10 mm were fabricated. For both groups, the material was put into the mold at the dough stage. Group I - SR Triplex Hot Heat Cure acrylic; group II - DPI Heat Cure acrylic. Both groups used the same curing procedure. One of the following three techniques was used to cool the material (15 samples from each material) once the curing cycle was finished: (A) water bath, (b) quenching, and (C) air. A traveling microscope was used to measure the distance between the markings on the acrylic samples. The data was recorded and statistically analyzed. RESULTS: In SR Triplex Hot heat cure acrylic material, the maximum linear dimensional changes were found in the quenching technique (0.242 ± 0.05), followed by the air technique (0.168 ± 0.11) and the least was found in the water bath technique (0.146 ± 0.01). In DPI Heat Cure acrylic material, the maximum linear dimensional changes were found in the quenching technique (0.284 ± 0.09), followed by the air technique (0.172 ± 0.18) and the least was found in the water bath technique (0.158 ± 0.10). There was a statistically significant difference found between these three cooling techniques. On comparison of adaptability, the water bath technique, the marginal gap SR Triplex Hot was 0.012 ± 0.02 and DPI Heat Cure was 0.013 ± 0.02. In the quenching technique, the marginal gap SR Triplex Hot was 0.019 ± 0.04 and DPI Heat Cure was 0.016 ± 0.04. In the air technique, the marginal gap SR Triplex Hot was 0.017 ± 0.01 and DPI Heat Cure was 0.019 ± 0.01. CONCLUSION: The present study concluded that among the different cooling methods, the water bath technique had the least linear dimensional change, followed by the air and quenching techniques. When comparing the materials, DPI Heat Cure acrylic resin showed a greater linear dimensional change than SR Triplex Hot heat cure acrylic resin. CLINICAL SIGNIFICANCE: During polymerization, heat-cured acrylic resins experience dimensional changes. Shrinkage and expansion are dimensional changes that occur in heat-cured acrylic resins and have an impact on the occlusal relationship and denture fit. However, the denture base's material qualities and the different temperature variations it experiences during production may have an impact on this. How to cite this article: Kannaiyan K, Rathod A, Bhushan P, et al. Assessment of Adaptability and Linear Dimensional Changes of Two Heat Cure Denture Base Resin with Different Cooling Techniques: An In Vitro Study. J Contemp Dent Pract 2024;25(3):241-244.

Effectiveness and safety of polyacrylamide hydrogel injection for knee osteoarthritis: results from a 12-month follow up of an open-label study.

OBJECTIVE: There are few effective osteoarthritis (OA) therapies. A novel injectable polyacrylamide hydrogel (iPAAG) previously demonstrated efficacy and safety up to week 26 in an open-label study of knee OA. Here we report longer-term effectiveness and safety data. METHODS: This multi-centre, open-label study included patients with symptomatic and radiographic knee OA. Primary outcome was WOMAC pain (0-100 scale) at 13 weeks, and patients continued to 26 weeks before entering a further 26-week extension phase. Secondary efficacy outcomes included WOMAC stiffness and function subscales, Patient Global Assessment (PGA) and proportion of OMERACT-OARSI responders. Safety outcomes were adverse events (AEs). RESULTS: 49 participants (31 women, mean age 70) received an ultrasound-guided, intra-articular injection of 6 ml iPAAG; 46 completed the extension phase to 52 weeks. There was a significant reduction in the WOMAC pain score from baseline to 52 weeks (- 17.7 points (95% CI - 23.1; - 12.4); p < 0.0001). Similar sustained improvements were observed for WOMAC stiffness (11.0 points; 95% CI - 17.0; - 4.9), physical function (18.0 points; 95% CI - 19.1; - 10.6), and PGA (16.3 points; 95% CI - 23.1; - 9.4). At 52 weeks 62.2% of patients were OMERACT-OARSI responders. From 26 to 52 weeks, 8 adverse effects (AE), including 1 serious AE (cerebrovascular accident) were reported in 5 subjects. None of the new adverse events were thought to be device related. CONCLUSION: This open-label study suggests persistent benefits and safety of iPAAG through 52 weeks after a single injection. TRIAL REGISTRATION: Clinicaltrials.gov NCT04179552.

Nano-scaled polyacrylonitrile for industrialization of nanofibers with photoluminescence and microbicide performance.

Nanofibers are investigated to be superiorly applicable in different purposes such as drug delivery systems, air filters, wound dressing, water filters, and tissue engineering. Herein, polyacrylonitrile (PAN) is thermally treated for autocatalytic cyclization, to give optically active PAN-nanopolymer, which is subsequently applicable for preparation of nanofibers through solution blow spinning. Whereas, solution blow spinning is identified as a process for production of nanofibers characterized with high porosity and large surface area from a minimum amounts of polymer solution. The as-prepared nanofibers were shown with excellent photoluminescence and microbicide performance. According to rheological properties, to obtain spinnable PAN-nanopolymer, PAN (12.5-15% wt/vol, honey like solution, 678-834 mPa s), thermal treatment for 2-4 h must be performed, whereas, time prolongation resulted in PAN-nanopolymer gelling or rubbering. Size distribution of PAN-nanopolymer (12.5% wt/vol) is estimated (68.8 ± 22.2 nm), to reflect its compatibility for the production of carbon nanofibers with size distribution of 300-400 nm. Spectral mapping data for the photoluminescent emission showed that, PAN-nanopolymer were exhibited with two intense peaks at 498 nm and 545 nm, to affirm their superiority for production of fluorescent nanofibers. The microbial reduction % was estimated for carbon nanofibers prepared from PAN-nanopolymer (12.5% wt/vol) to be 61.5%, 71.4% and 81.9%, against S. aureus, E. coli and C. albicans, respectively. So, the prepared florescent carbon nanofibers can be potentially applicable in anti-infective therapy.

Synthesis, characterization and column adsorption properties of gum ghatti and water hyacianth derived cellulose grafted poly(vinyl sulfonic acid-co-acrylamide) composites.

Vinylsulfonic acid (VSA), acrylamide (AM) and N, N methylene bis acrylamide(MBA) were copolymerized by radical polymerization in the presence of gum ghatti (GG) and treated water hyacianth (WH) in water. Several composite copolymers were prepared by varying the i) AM: VSA molar ratios ii) wt% of GG and iii) wt% of treated WH based on a Box-Behnken Design(BBD) of a response surface methodology (RSM) model with three input variables and the batch adsorption capacity (mg/g) of 100 mg/L Cd (II) from water as response. The composite polymer was characterized by Fourier transform Infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis(TGA), X- ray photo electron spectroscopy (XPS), compressive strength, pH reversibility, pH at point zero charge (pHPZC), Brunauer-Emmett-Teller (BET) surface area and scanning electron microscopy (SEM). The network parameters of the composites were determined. The copolymer composite prepared with AM: VSA of 5:1 containing 10 wt% GG and 4 wt% treated WH showed an optimum batch adsorption capacity of 399.15 mg/g Cd (II) from water containing 100 mg/L Cd (II). The same composite showed an adsorption capacity of 170.1 mg/g and a removal% of 31.5 at a feed concentration/feed flow rate/bed height of 150 mgL-1/30mLmin-1/30 mm in a fixed bed column.

The impact of recycling polyaluminium chloride and anionic polyacrylamide water treatment residuals on heavy metal adsorption in soils: implications for stormwater bioretention systems.

Despite the high adsorption capacity of polyaluminum chloride and anionic polyacrylamide water treatment residuals (PAC-APAM WTRs) for Pb2+, Cd2+, Cu2+, and Zn2+, their influence on the adsorption behavior of heavy metals in traditional bioretention soil media remains unclear. This study investigated the impact of PAC-APAM WTRs at a 20% weight ratio on the adsorption removal of Pb2+, Cd2+, Cu2+, and Zn2+ in three types of soils. The results demonstrated improved heavy metal adsorption in the presence of PAC-APAM WTRs, with enhanced removal observed at higher pH levels and temperatures. The addition of PAC-APAM WTRs augmented the maximum adsorption capacity for Pb2+ (from 0.98 to 3.98%), Cd2+ (from 0.52 to 10.99%), Cu2+ (from 3.69 to 36.79%), and Zn2+ (from 2.63 to 13.46%). The Langmuir model better described the data in soils with and without PAC-APAM WTRs. The pseudo-second-order model more accurately described the adsorption process, revealing an irreversible chemical process, although qe demonstrated improvement with the addition of PAC-APAM WTRs. This study affirms the potential of PAC-APAM WTRs as an amendment for mitigating heavy metal pollution in stormwater bioretention systems. Further exploration of the engineering application of PAC-APAM WTRs, particularly in field conditions for the removal of dissolved heavy metals, is recommended.