The determination of phosphorus containing compounds in dental casting investment products by 31P solid-state MAS-NMR spectroscopy.
Dent Mater
; 23(4): 415-24, 2007 Apr.
Article
em En
| MEDLINE
| ID: mdl-16563493
ABSTRACT
OBJECTIVES:
To use (31)P solid-state MAS-NMR to determine the phosphorus compounds that occur in dental casting investmentmaterial:
(a) as-received, (b) after setting and (c) after burn-out and discover whether such compounds are the same in each material across a product range.METHODS:
[(1)H] High powered decoupling (HPDC) and [(1)H] cross-polarization (CP) (31)P solid-state MAS-NMR spectroscopy at a resonance frequency of 121.4 MHz were used. Six commercial products were examined. Manufacturer's instructions were followed and a special liquid was used without dilution.RESULTS:
All products contain ammonium dihydrogen phosphate as the acid phosphate required for the setting reaction. All set by the formation of struvite and significant amounts of amorphous magnesium orthophosphate. In three products, lesser amounts of newberyite were present and in another the equivalent amorphous compound was formed. When burnt-out, magnesium metaphosphate or pyrophosphate was the dominant matrix compound. A higher burn-out temperature favoured pyrophosphate formation. Farringtonite was present to a lesser extent with the metaphosphate.SIGNIFICANCE:
Compounds that were not detected in earlier X-ray powder diffraction spectroscopy studies were detected by NMR, notably amorphous and glassy compounds (magnesium orthophosphate in set investment and magnesium metaphosphate in burnt-out material). The variation between products was significant and far greater than expected from the published scientific literature. Since the formation of compounds is affected by technical procedure and ambient conditions, these findings could offer some insight into the cause of the unpredictability of expansion measurements between laboratories. Further research is being undertaken.
Buscar no Google
Base de dados:
MEDLINE
Assunto principal:
Compostos de Fósforo
/
Revestimento para Fundição Odontológica
Idioma:
En
Ano de publicação:
2007
Tipo de documento:
Article