Purification of the leaching solution of recycling zinc from the hazardous electric arc furnace dust through an as-bearing jarosite.
Ecotoxicol Environ Saf
; 202: 110893, 2020 Oct 01.
Article
em En
| MEDLINE
| ID: mdl-32615495
ABSTRACT
Leaching of the hazardous electric arc furnace (EAF) dust containing mainly zinc ferrite and zinc oxide, accompanied by minor concentrations of arsenic compounds, was investigated using sulfuric acid. In order to reach the maximum recovery of zinc, the leaching solution was adjusted to recover both iron and zinc at their maximum possible values. To obtain a high recovery value of zinc and iron, analyzed by AAS, the optimum leaching condition was found to be the temperature of 90 °C, the sulfuric acid concentration of 3 M, the particle size of 75 µm, the S/L ratio of 110 g/mL and the leaching time of 2 h. The percentages of the zinc and iron recovery under the optimum condition were ca. 98.6% and 99.1% respectively, which were verified by a confirmation test and were very close to the predicted values of 100% based on the optimized model, obtained through the software. From the thermodynamics' point of view, it has been found that Zn2+ is the predominant species (90%) under the leaching condition applied. Moreover, the predominant species of iron are FeSO4+, FeHSO42+, Fe(SO4)2- and Fe3+ in the magnitudes of 65.8%, 25.6%, 4.4% and 4.0%, respectively. According to the kinetic results, the controlling step in the leaching was the chemical reaction at the most of the operating temperatures and times. In order to purify the zinc solution for electrowinning, iron and arsenic were removed through the jarosite formation process as confirmed by the XRD results. The speciation of arsenic in the precipitated jarosite was explored by XPS. Finally, the low concentrations of arsenic (less than 0.1 ppm) and iron (less than 50 ppm) were determined by the ICP analysis.
Palavras-chave
Texto completo:
1
Base de dados:
MEDLINE
Assunto principal:
Sulfatos
/
Zinco
/
Compostos Férricos
/
Reciclagem
/
Metalurgia
Idioma:
En
Ano de publicação:
2020
Tipo de documento:
Article