The effect of Er, Cr:YSGG laser debonding on the bond strength of two ceramic materials to dentin.
BMC Oral Health
; 23(1): 17, 2023 01 12.
Article
em En
| MEDLINE
| ID: mdl-36635647
OBJECTIVES: Evaluating the bond strength of two ceramic materials to dentin after Er,Cr:YSGG laser debonding. Would laser debonding affect the bond strength of ceramic to dentin? MATERIALS AND METHODS: Recently extracted human molars were ground to expose dentin. Forty square shaped samples were prepared from CAD/CAM ceramic blocks. Samples were divided into two groups according to the type of ceramic material; group E: Lithium disilicate and group T: Ultra-translucent Zirconia (n = 20) Each group was divided into two subgroups (n = 10) according to the laser debonding effect (subgroup B: bonded samples, subgroup R: re-bonded samples after laser debonding). Ceramic samples were bonded to dentin using dual cure self-adhesive resin cement. Laser debonding of ceramic samples of subgroups R using Er, Cr:YSGG laser, were then re-bonded again to dentin surface with same resin cement. The Shear bond strength test using Universal testing machine was done. The failure mode was analyzed. Two-way analysis of variance was used to compare the mean bond strength and re-bond strength of two materials. The significance level was set at P ≤ 0.05. RESULTS: Two-Way ANOVA showed that ceramic type had a significant effect on the re-bond strength to dentin. The predominant failure mode was adhesive. CONCLUSIONS: Laser debonding of Lithium disilicate and Ultra translucent Zirconia decreased the re-bond strength to dentin. Deterioration in re-bond strength for Lithium disilicate ceramics was more pronounced than for Ultra translucent Zirconia. Clinical Relevance Deterioration in the bond strength between ceramics & dentin after laser debonding still needs improvement to allow its clinical use.
Palavras-chave
Texto completo:
1
Base de dados:
MEDLINE
Assunto principal:
Colagem Dentária
/
Lasers de Estado Sólido
Idioma:
En
Ano de publicação:
2023
Tipo de documento:
Article