Scalable Glass-Fiber-Polymer Composite Solid Electrolytes for Solid-State Sodium-Metal Batteries.
ACS Appl Mater Interfaces
; 15(17): 20946-20957, 2023 May 03.
Article
em En
| MEDLINE
| ID: mdl-37078742
ABSTRACT
In this work, we report a method for producing a thin (<50 µm), mechanically robust, sodium-ion conducting composite solid electrolyte (CSE) by infiltrating the monomers of polyethylene glycol diacrylate (PEGDA) and polyethylene glycol (PEG) and either NaClO4 or NaFSI salt into a silica-based glass-fiber matrix, followed by an UV-initiated in situ polymerization. The glass fiber matrix provided mechanical strength to the CSE and enabled a robust, self-supporting separator. This strategy enabled the development of CSEs with high loadings of PEG as a plasticizer to enhance the ionic conductivity. The fabrication of these CSEs was done under ambient conditions, which was highly scalable and can be easily implemented in roll-to-roll processing. While NaClO4 was found to be unstable with the sodium-metal anode, the use of a NaFSI salt was found to promote stable stripping and plating in a symmetric cell, reaching current densities of as high as 0.67 mA cm-2 at 60 °C. The PEGDA + PEG + NaFSI separators were then used to form solid-state full cells with a cobalt-free, low-nickel layered Na2/3Ni1/3Mn2/3O2 cathode and a sodium-metal anode, achieving a full capacity utilization exhibiting 70% capacity retention after 50 cycles at a cycling rate of C/5 at 60 °C.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2023
Tipo de documento:
Article