Contribution of boundary non-stoichiometry to the lower-temperature plasticity in high-pressure sintered boron carbide.
Xu, Haiyue; Ji, Wei; Jiang, Jiawei; Liu, Junliang; Wang, Hao; Zhang, Fan; Yu, Ruohan; Tu, Bingtian; Zhang, Jinyong; Zou, Ji; Wang, Weimin; Wu, Jinsong; Fu, Zhengyi.
Afiliação
  • Xu H; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Ji W; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China. jiwei@whut.edu.cn.
  • Jiang J; Department of Materials, University of Oxford, Oxford, OX1 3PH, UK. jiwei@whut.edu.cn.
  • Liu J; Department of Materials, University of Oxford, Oxford, OX1 3PH, UK.
  • Wang H; Department of Materials, University of Oxford, Oxford, OX1 3PH, UK.
  • Zhang F; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Yu R; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Tu B; Hubei Longzhong Laboratory, Wuhan University of Technology Xiangyang Demonstration Zone, Xiangyang, 441000, China.
  • Zhang J; Nanostructure Research Centre, Wuhan University of Technology, Wuhan, 430070, China.
  • Zou J; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Wang W; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Wu J; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
  • Fu Z; State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan, 430070, China.
Nat Commun ; 14(1): 4889, 2023 Aug 21.
Article em En | MEDLINE | ID: mdl-37604800
Texto completo
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Base de dados: MEDLINE Idioma: En Ano de publicação: 2023 Tipo de documento: Article
Texto completo
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Base de dados: MEDLINE Idioma: En Ano de publicação: 2023 Tipo de documento: Article