Chemical, morphological and microhardness analysis of coronary dentin submitted to internal bleaching with hydrogen peroxide and violet LED.

BACKGROUND: Violet LED has been used for internal bleaching, however its implications on coronary dentin composition are unclear. The present study aims to evaluate the effect of bleaching with violet LED, either associated with 35 % hydrogen peroxide or not, on microhardness, chemical composition, and morphological characteristics of coronal dentin. METHODS: Thirty maxillary canines were selected to obtain 30 blocks of coronal dentin, distributed in 3 groups (n = 10): 35 % hydrogen peroxide (HP); violet LED (LED); HP 35 % + LED, (HP+LED). The chemical analysis was performed by FTIR and the morphological evaluation of the dentin structure by confocal laser scanning microscopy before (T0) and after treatment (T1). The microhardness analysis was performed by microdurometer after bleaching. The data were submitted to repeated measures ANOVA test (P> 0.05). RESULTS: The intensity of the inorganic peaks decreased after bleaching for all groups (P = 0.003). There was an increase in the organic peak intensity after bleaching with HP, a decrease for LED, while HP+LED did not change the intensity (P = 0.044). Moreover, the inorganic/organic ratio decreased for HP (P = 0.022), while for LED and HP+LED there was no significant changes (P>0.05). HP and HP+LED showed lower microhardness values compared to LED (P< 0.05). Regarding morphological changes, an increase in the perimeter of the dentinal tubules was found for all groups, with the smallest increase being observed for LED. CONCLUSION: HP bleaching decreased the chemical stability and microhardness of the coronal dentin, while the violet LED treatments had no significant impact on dentin stability. In all groups, there was an increase in exposure of the dentinal tubules after bleaching, which was less pronounced with the violet LED bleaching.