Effect of protective coating agents on microleakage and flexural strength of glass ionomer cement and zirconomer. an in vitro study.

ABSTRACT

PURPOSE: The objective of this study was to assess the microleakage and flexural strength of glass ionomer cement (GIC) and modified GIC (Zirconomer) when coated with protective coating agents such as COAT-IT and G-COAT plus. METHODS: Sixty tooth specimens were grouped into two groups based on the type of restorations (GIC (n = 30) and Zirconomer (n = 30)). The samples were further divided into three subgroups (n = 10) based on the protective coating agent (Petroleum jelly, G-COAT Plus, or COAT IT) applied. This study evaluated the microleakage at the occlusal and cervical margins of class V restoration after being subjected to dye penetration and sectioning. Each specimen was viewed under a 40 × microscope and was given scores based on the depth of dye penetration. They were statistically analyzed using the Kruskal-Wallis test and compared within the groups using the Mann- Whitney Test. In addition, flexural strength was assessed using standardized cuboid (25 × 2 × 2 mm) specimens of restorative materials with and without protective coating agents. The mean flexural strength data of all the subgroups were statistically evaluated using a one-way analysis of variance (ANOVA) and compared within the subgroups using the student t test. RESULTS: A statistically significant difference was found when occlusal margin microleakage scores were evaluated with G-COAT Plus demonstrating the lowest occlusal margin microleakage when applied over GIC restoration. The increasing order of occlusal margin microleakage scores is as follows GIC with G-COAT Plus, Zirconomer with COAT-IT, GIC with COAT-IT, GIC, Zirconomer with G-COAT Plus, and Zirconomer. However, the cervical margin microleakage scores revealed no significant difference. While flexural strength was found to be highest for the GIC group coated with G-COAT Plus, it was observed that there was a significant improvement in the flexural strength of both GIC and Zirconomer when coated with either of the protective coating agents. CONCLUSION: Within the limitations of this in vitro study, it was observed that the application of protective coating agents can significantly reduce the potential microleakage and improve the flexural strength of the restorative material especially when zirconia-reinforced GIC is the restorative material.