Super-tough poly(lactic acid)/silicone rubber thermoplastic vulcanizates: The organic and inorganic synergistic interfacial compatibilization.

ABSTRACT

Polymer modification using silicone rubber represents a promising avenue for enhancing physico-mechanical properties. However, achieving optimal performance through direct blending is hindered by the poor interface compatibility between silicone rubber and the matrix. In this study, we prepared super-tough thermoplastic vulcanizates (TPVs) of polylactic acid/silicone rubber through dynamic vulcanization with PLA, methyl vinyl silicone rubber (MVQ), glycidyl methacrylate grafted MVQ (MVQ-g-GMA), and fumed silica nanoparticles (SiO2). The impact of the SiO2 addition in MVQ on the morphology, mechanical properties, crystallization, and thermal properties of the TPVs was investigated. The results showed that MVQ-g-GMA and SiO2 exhibited a synergistic compatibilization effect significantly improving the interfacial adhesion between PLA and MVQ. Therefore, the impact and tensile strength of the TPVs increased from 8.0 kJ/m2 and 22.2 MPa to 62.6 kJ/m2 and 36.7 MPa, respectively. Moreover, the TPVs also presented good low-temperature toughness with a maximum impact strength of 40.4 kJ/m2 at -20 °C. Additionally, improvements in thermal stability and crystallization rate were also observed. Overall, combining organic and inorganic synergistic compatibilization is a feasible and effective method to fabricate outstanding low-temperature toughness to PLA.