Effect of Recycled Fine Aggregates on the Mechanical and Drying Shrinkage Properties of Alkali-Activated Recycled Concrete.

ABSTRACT

In this paper, the workability, mechanical, ion leaching, and drying shrinkage properties of alkali-activated concrete with recycled coarse and fine aggregates were studied, and the pore structure and micro-morphology of different alkali-activated recycled aggregate concretes (AARACs) were characterized by using the mercury intrusion method and scanning electron microscopy, respectively. The experimental results showed that with the increase in the replacement rate of the recycled fine aggregate (RFA), the flowability showed a decreasing trend. Adding a certain amount of RFA improves the mechanical properties of the AARAC. The compressive strength at a curing age of 28 days was 65.3 MPa with 70 wt% RFA replacement. When the replacement rate of the RFA was 100 wt%, the maximum splitting tensile strength (4.5 MPa) was obtained at a curing age of 7 days. However, the addition of the RFA had little effect on the flexural strength of the AARAC. As an extension of the curing age, the splitting tensile strength, flexural strength, tension-to-compression ratio, and flexure-to-compression ratio all showed an increasing trend at first and then a decreasing trend. At a curing age of 7 days, the tension-to-compression ratio and flexure-to-compression ratio were both high (except for those of R100), indicating that the ductility and toughness of the specimen were improved. The addition of the RFA increased the drying shrinkage of the AARAC. At a curing age of 120 days, compared to the specimen without the RFA, the drying shrinkage rate of the specimen with the addition of 70 wt% RFA increased by 34.15%. As the curing age increased, the microstructure of the reaction products became denser, but the proportion of large-diameter pores increased. This study evaluated the application of RFA in AARAC. The experimental results showed that the RFA-based AARAC had acceptable mechanical and durability properties.