Atomically thin-layered WS2based resistive sensors for detection of CO and NO2at room temperature.
Nanotechnology
; 35(40)2024 Jul 17.
Article
em En
| MEDLINE
| ID: mdl-38959867
ABSTRACT
The number of layers present in a two-dimensional (2D) nanomaterial plays a critical role in applications that involve surface interaction, for example, gas sensing. This paper reports the synthesis of 2D WS2nanoflakes using the facile liquid exfoliation technique. The nanoflakes were exfoliated using bath sonication (BS-WS2) and probe sonication (PS-WS2). The thickness of the BS-WS2was found to range between 70 and 200 nm, and that of PS-WS2varied from 0.6 to 80 nm, indicating the presence of single to few layers of WS2when characterized using atomic force microscope. All the WS2samples were thoroughly characterized using electron microscopes, x-ray diffractometer, Raman spectroscopy, UV-Visible spectroscopy, Fourier transform infrared spectroscope, and thermogravimetric analyser. Both the nanostructured samples were exposed to 2 ppm of NO2at room temperature. Interestingly, BS-WS2which comprises of a greater number of WS2layers exhibited -14.2% response as against -3.4% response of PS-WS2, the atomically thin sample. The BS-WS2sample was found to be highly selective towards NO2but was slower (with incomplete recovery) as compared to PS-WS2. The PS-WS2sample was observed to exhibit -11.9% to -27.4% response to 2-10 ppm of CO and -3.4%-35.2% response to 2-10 ppm of NO2at room temperature, thereby exhibiting the potential to detect two gases simultaneously. These gases could be accurately predicted and quantified if the response times of the PS-WS2sample were considered. The atomically thin WS2-based sensor exhibited a limit of detection of 131 and 81 ppb for CO and NO2, respectively.
Texto completo:
1
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2024
Tipo de documento:
Article