Electro-Thermo-Magnetic Effect-Induced Large Thermoelectric Performance of Calcium Cobaltite Nanocomposites.

ABSTRACT

As attractive thermoelectric oxides, Ca3Co4O9-based materials have been intensively studied for their applications in recent years. However, their thermoelectric performance is enormously limited due to the contradiction of electrical resistivity and thermal conductivity. Herein, BaFe12O19 nanospheres were introduced into the Ca3Co4O9 matrix. The metallic Ag, ferrites, and matrix phase survived together, and a high density of nanoscale BaFe12O19 precipitation was observed. The reduction of work function could lead to band bending and form an interface potential due to the electro-thermo-magnetic effect contributing to the hole migration. As a result, a huge ZT value of 0.51 for the 8 wt % BaFe12O19/Ca3Co4O9 nanocomposites was obtained at 1073 K, accompanied by a low electrical resistivity of 6.7 mΩ·cm and a high Seebeck coefficient of 217.5 µV/K. In addition, a significant reduction of thermal conductivity (1.11 W/(m·K)) occurred, which was due to the nanoscale ferromagnetic phase effectively scattering the mid- and short-wavelength heat-carrying phonons. The synergistic enhancement of thermoelectric performance confirmed that the electro-thermo-magnetic effect is an effective way to solve the challenging problem of performance deterioration in oxide thermoelectric materials.