The mechanical stability of barium titanate (ceramic) implants in vitro.
Biomater Med Devices Artif Organs
; 8(3): 265-72, 1980.
Article
em En
| MEDLINE
| ID: mdl-7407288
ABSTRACT
Dense, polycrystalline barium titanate (BaTiO3) specimens showed a modulus of rupture of 85.5 +/- 9.0 MPa and a compressive strength of 486 +/- 75 MPa. These values are considerable higher than those which had been previously reported. In addition, there was no significant drop in compressive strength after in vitro aging for 4 weeks in saline solution.