The disintegration of superEBA cement in solutions with adjusted pH and osmolarity.
J Endod
; 23(11): 663-8, 1997 Nov.
Article
em En
| MEDLINE
| ID: mdl-9587304
ABSTRACT
This study determined the disintegration of fast-set SuperEBA cement using ANSI/ADA Specification No. 30 (Spec #30) as well as modifications in pH, osmolarity, time before immersion, and duration of immersion that mimic the clinical, endodontic application of this material. After immersion intervals of 24 h, 1 wk, 1 m, 3 m, or 6 m, specimens were desiccated and weighed. The preimmersion and postdehydration weights were obtained to the nearest 1.0 mg and the percent weight loss from preimmersion levels was calculated. Adjusting the osmolarity to the physiologic level of 300 mOsm/kg resulted in significantly less weight loss (p < 0.05) than the control group in distilled water (no modification of Spec #30). The pH of the storage solution was found to be a significant factor in weight loss. As the acidity and the time of immersion increased, the weight loss also significantly increased with the greatest weight loss of 19.81% at pH 5.5 after 6 m storage. Immersion within 10 min of mixing was not significantly different (p > 0.05) in weight from the control of 1 h set-time. The 24 h weight loss measurements for the pHs of 5.5 and 6.4 were greater than the 1.5% allowed by Spec #30. All other 24 h measurements were less than the 1.5%.
Buscar no Google
Base de dados:
MEDLINE
Assunto principal:
Materiais Restauradores do Canal Radicular
/
Adesivos Dentinários
/
Cimentos Dentários
Idioma:
En
Ano de publicação:
1997
Tipo de documento:
Article