Colloidal Synthesis of Monodisperse High-Entropy Spinel Oxide Nanocrystals.

Synthesis of high-entropy oxide (HEO) nanocrystals has focused on increasing the temperature in the entropy term (T(ΔS)) to overcome the enthalpy term. However, these high temperatures lead to large, polydisperse nanocrystals. In this work, we leverage the low solubility product (Ksp) of metal oxides and optimize the Lewis-acid-catalyzed esterification reaction for equal rate production of the cation monomers to synthesize HEO nanocrystals at low temperatures, producing the smallest (<4 nm) and most monodisperse (<15% size dispersity) HEOs to date. We apply these HEO nanocrystals as electrocatalysts, exhibiting promising activity toward the oxygen evolution reaction in alkaline media, with an overpotential of 345 mV at 10 mA/cm2.

General Route to Colloidally Stable, Low-Dispersity Manganese-Based Ternary Spinel Oxide Nanocrystals.

While certain ternary spinel oxides have been well-explored with colloidal nanochemistry, notably the ferrite spinel family, ternary manganese (Mn)-based spinel oxides have not been tamed. A key composition is cobalt (Co)-Mn oxide (CMO) spinel, CoxMn3-xO4, that, despite exemplary performance in multiple electrochemical applications, has few reports in the colloidal literature. Of these reports, most show aggregated and polydisperse products. Here, we describe a synthetic method for small, colloidally stable CMO spinel nanocrystals with tunable composition and low dispersity. By reacting 2+ metal-acetylacetonate (M(acac)2) precursors in an amine solvent under an oxidizing environment, we developed a pathway that avoids the highly reducing conditions of typical colloidal synthesis reactions; these reducing conditions typically push the system toward a monoxide impurity phase. Through surface chemistry studies, we identify organic byproducts and their formation mechanism, enabling us to engineer the surface and obtain colloidally stable nanocrystals with low organic loading. We report a CMO/carbon composite with low organic contents that performs the oxygen reduction reaction (ORR) with a half-wave potential (E1/2) of 0.87 V vs RHE in 1.0 M potassium hydroxide at 1600 rpm, rivaling previous reports for the highest activity of this material in ORR electrocatalysis. We extend the general applicability of this procedure to other Mn-based spinel nanocrystals such as Zn-Mn-O, Fe-Mn-O, Ni-Mn-O, and Cu-Mn-O. Finally, we show the scalability of this method by producing inorganic nanocrystals at the gram scale.