Improvement of the photoelectric dye sensitized solar cell performance using Fe/S-TiO2 nanoparticles as photoanode electrode.

A sulfur nanoparticles-incorporated iron-doped titanium oxide (Fe/TiO2) with different ratio was successfully synthesized by photolysis method and utilized as effective photoanode in dye sensitized solar cell (DSSC) application with N719 dye. The photolysis method was contained the irradiation of the Fe, S and Ti mixture solution with 15 W source irradiation, and then calcined the formed precipitate. The DSSCs fabricated with Fe/S-TiO2 photoanode appeared an improved solar-to-electrical energy conversion efficiency of 6.46, which more than pure TiO2 (3.43) below full sunlight illumination (1.5 G). The impact of Fe content on the total efficiency was also inspected and the Fe content with 6% S-TiO2 was found 5 wt%. Due to the improved the efficiency of solar cell conversion of Fe/S-TiO2 nanocomposite, it should be deemed as a potential photoanode for DSSCs with high performance.

Experimental and theoretical study of improved mesoporous titanium dioxide perovskite solar cell: The impact of modification with graphene oxide.

The present study serves experimental and theoretical analyses in developing a hybrid advanced structure as a photolysis, which is based on electrospun Graphene Oxide-titanium dioxide (GO-TiO2) nanofibers as an electron transfer material (ETMs) functionalized for perovskite solar cell (PVSCs) with GO. The prepared ETMs were utilized for the synthesis of mixed-cation (FAPbI3)0.8(MAPbBr3)0.2. The effect of GO on TiO2 and their chemical structure, electronic and morphological characteristic were investigated and discussed. The elaborated device, namely ITO/Bl-TiO2/3 wt% GO-TiO2/(FAPbI3)0.8(MAPbBr3)0.2/spiro-MeTAD/Pt, displayed 20.14% disposition and conversion solar energy with fill factor (FF) of 1.176%, short circuit current density (Jsc) of 20.56 mA/cm2 and open circuit voltage (VOC) 0.912 V. The obtained efficiency is higher than titanium oxide (18.42%) and other prepared GO-TiO2 composite nanofibers based ETMs. The developed materials and device would facilitate elaboration of advanced functional materials and devices for energy storage applications.

CdIn2Se4@chitosan heterojunction nanocomposite with ultrahigh photocatalytic activity under sunlight driven photodegradation of organic pollutants.

This research focused on synthesizing a CdIn2Se4@Ch nanocomposite by doping CdIn2Se4 into chitosan using a photolysis assisted ultrasonic process. The aim was to enhance the photodegradation efficiency of ofloxacin and 2,4-dichlorophenoxyacetic acid under sunlight. The synthesized CdIn2Se4@Ch nanocomposite was investigated via different techniques, including XRD, XPS, FTIR, TEM, DSC, TGA, UV-Vis and PL. The study also investigated the influence of various reaction parameters, including the effects of inorganic and organic ions. The synthesized nanocomposite demonstrated exceptional efficiency, achieving 86 % and 95 % removal rates, with corresponding rate constants of 0.025 and 0.047 min-1. This performance surpasses that of CdIn2Se4 by approximately 1.35 and 2.25 times, respectively. The values of COD were decreased to 78 and 86 % for ofloxacin and 2,4-dichlorophenoxyacetic, while the TOC values decreased to 71 and 84 %, respectively, from their premier values. The improvement in performance is associated with the introduction of CdIn2Se4 into chitosan, resulting in the self-integration of Cd into the catalyst. This creates a localized accumulation point for electrons, enhancing the efficiency of charge separation and further reducing the surface charge of chitosan. Experimental evidence suggests that superoxide and hydroxyl radicals play a significant role in the photodegradation of pollutants. Additionally, the nanocomposite exhibits excellent stability and can be reused up to five times, indicating remarkable stability and reusability of the developed photocatalyst.

2-(Benzhydryl sulfinyl)-N-sec-butylacetamide) isolated from fig augmented trastuzumab-triggered phagocytic killing of cancer cells through interface with Fcγ receptor.

The objective of the current study was to extract 2-(benzhydryl sulfinyl)-N-sec-butylacetamide), a novel compound from fig, and then determine its role in enhancing trastuzumab-triggered phagocytic killing of SKOV-3 cancer cells. In this study, Soxhlet was used to extract the compound from the mature and air-dried fig fruits. The production of the isolated extracts was enhanced by using polar and non-polar solvents. Several solvents, such as methanol, ethyl acetate, chloroform, and n-hexane, were used to isolate the effective compound 2-(benzhydryl sulfinyl)-N-sec-butylacetamide) from the organic layer. UV-spectroscopy, FT-IR, 1H-NMR, and 13C-NMR were applied to identify the purified compound. The in vitro and in vivo assays demonstrated that the 2-(benzhydryl sulfinyl)-N-sec-butylacetamide) can increase the activity of the phagocytic cells, via the interaction with FcY receptors, along with trastuzumab, and the pathway can use a model for the therapeutic strategy for effective treatment of ovarian cancer cells.