Effects of the combination of low-level laser therapy and anionic polymer membranes on bone repair.

In view of the limitations of bone reconstruction surgeries using autologous grafts as a gold standard, tissue engineering is emerging as an alternative, which permits the fabrication and improvement of scaffolds to stimulate osteogenesis and angiogenesis, processes that are essential for bone repair. Polymers are used to mimic the extracellular bone matrix and support cell growth. In addition, bone neoformation can be induced by external factors such as laser irradiation, which stimulates bone metabolism. The objective of this study was to evaluate the regeneration of bone defects using collagen and elastin membranes derived from intestinal serosa and bovine auricular cartilage combined with low-level laser application. Thirty-six Wistar rats were operated to create a 3-mm defect in the distal metaphysis of the left femur and divided into six groups: G1 (control, no treatment); G2 (laser); G3 (elastin graft), G4 (elastin+laser); G5 (collagen graft); G6 (collagen+laser). The animals were sacrificed 6 weeks after surgery and the femurs were removed for analysis of bone repair. Macroscopic and radiological results showed the absence of an infectious process in the surgical area. This was confirmed by histological analysis, which revealed no inflammatory infiltrate. Histomorphometry showed that the formation of new bone started from the margins of the bone defect and its volume was greater in elastin+laser and collagen+laser. We conclude that newly formed bone in the graft area was higher in the groups that received the biomaterials and laser. The collagen and elastin matrices showed biocompatibility.

Suitability of the use of an elastin matrix combined with bone morphogenetic protein for the repair of cranial defects.

The use of biomaterials in medical and dental areas has become increasingly important due to the need to restore areas with bone loss or defects. This study analyzed the use of a new elastin polymer matrix combined with Bone Morphogenetic Protein for the repair of cranial defects in rats. Thirty rats were divided into five groups: control (C) defect without graft, E24 (defect filled with elastin matrix submitted to alkaline hydrolysis at 50°C for 24 h), E24/BMP (defect filled with elastin matrix treated at 50°C for 24 h plus BMP), E96 (defect filled with elastin matrix treated at 37°C for 96 h) and E96/BMP (defect filled with elastin matrix treated at 37°C for 96 h plus BMP). The animals were killed after 6 weeks. In the histological and microtomographic analysis, all groups showed bone growth from the defect margins remaining in this region without a marked inflammatory process, but in the E96/BMP group the lamellae were thicker and the collagen fibers more organized. Histometrically, the same group presented higher percentage of new formation (43.25 ± 3.72) in relation to the other groups. It was concluded that the support and delivery system formed by the elastin matrix associated with BMPs had a positive effect on the bone repair process.

Use of an anionic collagen matrix made from bovine intestinal serosa for in vivo repair of cranial defects.

Polymeric biomaterials composed of extracellular matrix components possess osteoconductive capacity that is essential for bone healing. The presence of collagen and the ability to undergo physicochemical modifications render these materials a suitable alternative in bone regenerative therapies. The objective of this study was to evaluate the osteogenic capacity of collagen-based matrices (native and anionic after alkaline hydrolysis) made from bovine intestinal serosa (MBIS). Twenty-five animals underwent surgery to create a cranial defect to be filled with native and anionic collagen matrixes, mmineralized and non mineralized. The animals were killed painlessly 6 weeks after surgery and samples of the wound area were submitted to routine histology and morphometric analysis. In the surgical area there was new bone formation projecting from the margins to the center of the defect. More marked bone neoformation occurred in the anionic matrices groups in such a way that permitted union of the opposite margins of the bone defect. The newly formed bone matrix exhibited good optical density of type I collagen fibers. Immunoexpression of osteocalcin by osteocytes was observed in the newly formed bone. Morphometric analysis showed a greater bone volume in the groups receiving the anionic matrices compared to the native membranes. Mineralization of the biomaterial did not increase its osteoregenerative capacity. In conclusion, the anionic matrix exhibits osteoregenerative capacity and is suitable for bone reconstruction therapies.