RESUMEN
The Hall-Petch relationship, according to which the strength of a metal increases as the grain size decreases, has been reported to break down at a critical grain size of around 10 to 15 nanometres1,2. As the grain size decreases beyond this point, the dominant mechanism of deformation switches from a dislocation-mediated process to grain boundary sliding, leading to material softening. In one previous approach, stabilization of grain boundaries through relaxation and molybdenum segregation was used to prevent this softening effect in nickel-molybdenum alloys with grain sizes below 10 nanometres3. Here we track in situ the yield stress and deformation texturing of pure nickel samples of various average grain sizes using a diamond anvil cell coupled with radial X-ray diffraction. Our high-pressure experiments reveal continuous strengthening in samples with grain sizes from 200 nanometres down to 3 nanometres, with the strengthening enhanced (rather than reduced) at grain sizes smaller than 20 nanometres. We achieve a yield strength of approximately 4.2 gigapascals in our 3-nanometre-grain-size samples, ten times stronger than that of a commercial nickel material. A maximum flow stress of 10.2 gigapascals is obtained in nickel of grain size 3 nanometres for the pressure range studied here. We see similar patterns of compression strengthening in gold and palladium samples down to the smallest grain sizes. Simulations and transmission electron microscopy reveal that the high strength observed in nickel of grain size 3 nanometres is caused by the superposition of strengthening mechanisms: both partial and full dislocation hardening plus suppression of grain boundary plasticity. These insights contribute to the ongoing search for ultrastrong metals via materials engineering.
RESUMEN
In polycrystalline metals, plastic deformation is accompanied by lattice rotations resulting from dislocation glide. Following these rotations in three dimensions requires nondestructive methods that so far have been limited to grain sizes at the micrometer scale. We tracked the rotations of individual grains in nanograined nickel by using three-dimensional orientation mapping in a transmission electron microscope before and after in situ nanomechanical testing. Many of the larger-size grains underwent unexpected lattice rotations, which we attributed to a reversal of rotation during unloading. This inherent reversible rotation originated from a back stress-driven dislocation slip process that was more active for larger grains. These results provide insights into the fundamental deformation mechanisms of nanograined metals and will help to guide strategies for material design and engineering applications.