Lithium dendrites belong to the key challenges of solid-state battery research. They are unavoidable due to the imperfect nature of surfaces containing defects of a critical size that can be filled by lithium until fracturing the solid electrolyte. The penetration of Li metal occurs along the propagating crack until a short circuit takes place. It is hypothesized that ion implantation can be used to introduce stress states into Li6.4La3Zr1.4Ta0.6O12 which enables an effective deflection and arrest of dendrites. The compositional and microstructural changes associated with the implantation of Ag-ions are studied via atom probe tomography, electron microscopy, and nano X-ray diffraction indicating that Ag-ions can be implanted up to 1 µm deep and amorphization takes place down to 650-700 nm, in good agreement with kinetic Monte Carlo simulations. Based on diffraction results pronounced stress states up to -700 MPa are generated in the near-surface region. Such a stress zone and the associated microstructural alterations exhibit the ability to not only deflect mechanically introduced cracks but also dendrites, as demonstrated by nano-indentation and galvanostatic cycling experiments with subsequent electron microscopy observations. These results demonstrate ion implantation as a viable technique to design "dendrite-free" solid-state electrolytes for high-power and energy-dense solid-state batteries.
RESUMEN
Lithium dendrite growth in inorganic solid-state electrolytes acts as a main stumbling block for the commercial development of all-solid-state lithium batteries. Indeed, Li dendrites often lead to solid-state electrolyte fractures, undermining device integrity and safety. Despite the significance of these issues, the mechanisms driving the solid-state electrolyte fracture process at the microscopic level remain poorly understood. Here, via operando optical and ex situ dark field X-ray microscopy measurements of LiSnâ£single-crystal Li6.5La3Zr1.5Ta0.5O12â£LiSn symmetric cells, we provide insights into solid-state electrolyte strain patterns and lattice orientation changes associated with dendrite growth. We report the observation of dislocations in the immediate vicinity of dendrite tips, including one instance where a dislocation is anchored directly to a tip. This latter occurrence in single-crystalline ceramics suggests an interplay between dendrite proliferation and dislocation formation. We speculate that the mechanical stress induced by dendrite expansion triggers dislocation generation. These dislocations seem to influence the fracture process, potentially affecting the directional growth and branching observed in lithium dendrites.