Surface modification of bulk titanium substrates for biomedical applications via low-temperature microwave hydrothermal oxidation.

Micro-to-nanoscale surface topographies of orthopaedic and dental implants can affect fluid wetting and biological response. Nanoscale features can be superimposed on microscale roughness of titanium (Ti) surfaces at high temperatures, resulting in increased osteoblast differentiation. However, high temperatures can compromise mechanical properties of the bulk material. Here, we have developed a novel low-temperature microwave hydrothermal (MWHT) oxidation process for nanomodification of microrough (SLA) Ti surfaces. Nanoscale protuberances (20 -100 nm average diameter) were generated on SLA surfaces via MWHT treatment at 200°C in H2 O, or in aqueous solutions of H2 O2 or NH4 OH, for times ranging from 1 to 40 h. The size, shape, and crystalline content of the nanoprotuberances varied with the solution used and treatment time. The hydrophilicity of all MWHT-modified surfaces was dramatically enhanced. MG63 and normal human osteoblasts (NHOsts) were cultured on MWHT-treated SLA surfaces. While most responses to MWHT-modified surfaces were comparable to those seen on SLA controls, the MWHT-generated nanotopography reduced osteocalcin production by NHOst cells, suggesting that specific nanotopographic characteristics differentially mediate osteoblast phenotypic expression. MWHT processing provides a scalable, low-temperature route for tailoring nanoscale topographies on microroughened titanium implant surfaces with significantly enhanced wetting by water, without degrading the microscale surface structure of such implants. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 782-796, 2018.

Tunable multimodal adhesion of 3D, nanocrystalline CoFe2O4 pollen replicas.

3D replicas of sunflower pollen microparticles, comprised of a multicomponent magnetic spinel ferrite (CoFe2O4) with tailorable adhesive properties, have been synthesized for the first time via a conformal layer-by-layer (LbL) surface sol-gel (SSG) deposition process followed by organic pyrolysis and oxide compound formation at a peak temperature of 600 °C-900 °C. These high-fidelity ferrite pollen replicas exhibited multimodal (van der Waals, vdW, and magnetic) adhesion that could be tuned via control of the CoFe2O4 nanoparticle and crystal sizes. The CoFe2O4 pollen replicas exhibited a non-monotonic change in short-range (~10 nm) vdW adhesion with an increase in the peak firing temperature, which was consistent with the counteracting effects of particle coarsening on the size and number of nanoparticles present on the sharp tips of the echini (spines) on the pollen replica surfaces. The longer-range (up to ~1 mm) magnetic force of adhesion increased monotonically with an increase in firing temperature, which was consistent with the observed increases in the values of the saturation and remanent magnetization of CoFe2O4 with an increase in average nanocrystal size. By adjusting the nanocrystal/nanoparticle sizes of the CoFe2O4 pollen replicas, the total force of adhesion (vdW + magnetic) to a magnetic substrate could be increased by a factor of ~3 relative to native pollen grains.

Compartmentalisation of enzymes for cascade reactions through biomimetic layer-by-layer mineralization.

Cellular metabolic pathways are paradigms for the rapid and waste-free conversion of molecules into useful products through multiple enzyme-catalyzed steps (cascade reactions). Attempts to establish efficient cascade reactions for technological applications have focused on mimicking nature's high degree of organization by controlling the positioning of enzymes through immobilization in tailor-made compartments. The present work utilized peptide-mediated layer-by-layer mineralization as a facile and generic method for the compartmentalisation of multi-enzyme systems in nanoscale silica layers. It is demonstrated that, in a multilayer system, the overall rate of the reaction cascade was primarily affected by the placement of the enzyme catalyzing the first step, with the placement of the enzyme possessing the lowest catalytic efficiency also being an important factor. As the rate-limiting enzymes were positioned closer to the external silica surface, the overall rate of cascade reactions increased. Furthermore, distributing the enzymes into different adjacent silica compartments yielded higher overall cascade reaction rates compared to placement of the enzymes into the same silica layer. The synthetic methods and kinetic analyses presented here provide guidance for improving the performance of immobilized multi-enzyme systems for a wide range of technological applications.