Cooperative Catalysis of Vibrationally Excited CO2 and Alloy Catalyst Breaks the Thermodynamic Equilibrium Limitation.

Using nonthermal plasma (NTP) to promote CO2 hydrogenation is one of the most promising approaches that overcome the limitations of conventional thermal catalysis. However, the catalytic surface reaction dynamics of NTP-activated species are still under debate. The NTP-activated CO2 hydrogenation was investigated in Pd2Ga/SiO2 alloy catalysts and compared to thermal conditions. Although both thermal and NTP conditions showed close to 100% CO selectivity, it is worth emphasizing that when activated by NTP, CO2 conversion not only improves more than 2-fold under thermal conditions but also breaks the thermodynamic equilibrium limitation. Mechanistic insights into NTP-activated species and alloy catalyst surface were investigated by using in situ transmission infrared spectroscopy, where catalyst surface species were identified during NTP irradiation. Moreover, in in situ X-ray absorption fine-structure analysis under reaction conditions, the catalyst under NTP conditions not only did not undergo restructuring affecting CO2 hydrogenation but also could clearly rule out catalyst activation by heating. In situ characterizations of the catalysts during CO2 hydrogenation depict that vibrationally excited CO2 significantly enhances the catalytic reaction. The agreement of approaches combining experimental studies and density functional theory (DFT) calculations substantiates that vibrationally excited CO2 reacts directly with hydrogen adsorbed on Pd sites while accelerating formate formation due to neighboring Ga sites. Moreover, DFT analysis deduces the key reaction pathway that the decomposition of monodentate formate is promoted by plasma-activated hydrogen species. This work enables the high designability of CO2 hydrogenation catalysts toward value-added chemicals based on the electrification of chemical processes via NTP.

Doubly Decorated Platinum-Gallium Intermetallics as Stable Catalysts for Propane Dehydrogenation.

Propane dehydrogenation (PDH) is a promising chemical process that can satisfy the increasing global demand for propylene. However, the Pt-based catalysts that have been reported thus far are typically deactivated at ≥600 °C by side reactions and coke formation. Thus, such catalysts possess an insufficient life. Herein, we report a novel catalyst design concept, namely, the double decoration of PtGa intermetallics by Pb and Ca, which synergize the geometric and electronic promotion effects on the catalyst stability, respectively. Pb is deposited on the three-fold Pt3 sites of the PtGa nanoparticles to block them, whereas Ca, which affords an electron-enriched single-atom-like Pt1 site, is placed around the nanoparticles. Thus, PtGa-Ca-Pb/SiO2 exhibits an outstandingly high catalytic stability, even at 600 °C (kd =0.00033 h-1 , τ=3067 h), and almost no deactivation of the catalyst was observed for up to 1 month for the first time.

Synthesis of Co2FeGe Heusler alloy nanoparticles and catalysis for selective hydrogenation of propyne.

Although intermetallic compounds are attracting attention of catalysis researchers, ternary intermetallic catalysts have scarcely been investigated due the difficulty of synthesizing supported nanoparticles. In this study, we successfully synthesized SiO2 supported Co2FeGe Heuslar alloy nanoparticles. This catalyst exhibited high catalytic performance for selective hydrogenation of propyne by nano-sizing.

Electroassisted Propane Dehydrogenation at Low Temperatures: Far beyond the Equilibrium Limitation.

Propylene production by propane dehydrogenation (PDH) generally requires high temperatures due to thermodynamic equilibrium limitations. This study developed a novel type of catalytic system for low-temperature PDH by combining a surface protonics methodology with intermetallic active sites. By application of an electric current, the intermetallic Pt-In/TiO2 catalyst gave a propylene yield of 10.2% with high selectivity, even at 250 °C, where the thermodynamic equilibrium yield was only 0.15%. Electroassisted proton collisions with propane allowed an unusual reaction pathway for low-temperature PDH. Alloying of Pt with In drastically enhanced the activity and selectivity due to the increased electron density of Pt.