RESUMEN
In-based halide perovskites have attracted a lot of attention because of their unique broadband emission properties. Herein, a series of In-based hybrid perovskites of (H2MP)2InCl7·H2O (1), (H2EP)2InCl7·H2O (2), (H2MP)2InBr7·H2O (3), and (H2EP)2InBr7·H2O (4) were synthesized under the control of halogen ions and organic cations. 1, 2, and 4 exhibit obvious photoluminescence properties with peaks at 392, 442, and 652 nm, respectively. The effects of the different components on the crystal structure and photoluminescence properties are discussed by calculating the structural distortion of the [InX6]3- octahedron. The photoluminescence properties of 1 and 4 were significantly improved after Sb3+ doping with PLQY values of 57.12 and 41.53%. Finally, a white LED was successfully fabricated with the two doped compounds coated onto the 365 nm blue LED chip.
RESUMEN
Halide perovskites have high photoelectric conversion efficiency, making them promising candidates for photocatalysis. However, their toxic and unstable nature limits their applications. Here, we successfully synthesised three hybrid Bi-based halide perovskites: (HTMG)3Bi2Br9 (1), (HEI)2BiBr5 (2) and (HTMA)3Bi2Br9 (3). X-ray single-crystal diffraction analysis shows that they all contained 0D structures composed of isolated Bi-Br clusters. The three compounds showed excellent degradability and cycling stability for Sudan III dissolved in ethanol under simulated sunlight. In addition, the photocatalytic degradation performance of four Bi-based halide perovskites previously reported by our group is also characterised and summarised in this work.