Preparation and Anti-Mold Properties of Nano-ZnO/Poly(N-isopropylacrylamide) Composite Hydrogels.

The aim of this study was to overcome drawbacks of the inhomogeneous dispersion and facile agglomeration of nano-ZnO/poly(N-isopropylacrylamide) composite hydrogels (nano-ZnO/PNIPAm composite hydrogels) during synthesis and improve the anti-mold property of the nano-ZnO/PNIPAm composite hydrogels. Here, nano-ZnO/PNIPAm composite hydrogels were prepared by the radical polymerization method. Fourier transform infrared (FTIR) spectroscopy, transmission electron microscopy (TEM), differential scanning calorimeter (DSC), and dynamic light scattering (DLS) were used to characterize the effects of different dispersants on the particle sizes, dispersions, and phase transition characteristics of the nano-ZnO/PNIPAm composite hydrogels. The anti-mold properties of nano-ZnO/PNIPAm composite hydrogels were studied. Results revealed that the nano-ZnO/PNIPAm composite hydrogel prepared by the addition of nano-ZnO dispersion liquid exhibited the smallest particle size, the most homogeneous dispersion, and the highest stability. The addition of the dispersant did not change the phase transition characteristics of nano-ZnO/PNIPAm, and the nano-ZnO/PNIPAm composite hydrogels (Pf) exhibited good anti-mold properties to the bamboo mold.

Preparation and Flame Retardant Properties of Calcium-Aluminium Hydrotalcite with Root Cutting Silicate Layers as Bamboo Flame Retardants.

Bamboo has been widely used in architecture, decoration and other fields because of its advantages of short growth period, high strength and degradability. However, bamboo, as a combustible material like wood, are easy to burn and cause building fires. However, the existing bamboo water-based flame retardants have some shortcomings, such as strong hygroscopicity and easy loss, which limits the application of bamboo products. In order to improve the flame retardant performance of bamboo, CaAl-SiO2 layered double hydroxide (LDH) as bamboo flame retardant was synthesised by coprecipitation method. The influence of preparation technology on CaAl-SiO3-LDH structures and properties as well as the flame retardant and smoke suppression characteristics of flame retardant-treated bamboo was discussed. The results revealed that the crystallisation temperature, crystallisation time and crystallisation concentration of CaAl-SiO3-LDHs considerably affected its structure and properties. The optimum technological parameters for preparing CaAl-SiO3-LDHs by using the coprecipitation method are as follows: crystallisation temperature of 100 °C, crystallisation time of 9 h and Ca2+ solution molar concentration of 0.33 mol/L. Compared with nonflame-retardant wood, CaAl-SiO3-LDH flame retardant treatment delayed the peak time of the heat release rate by 20 s and the ignition time by 77.78% and increased the carbon residue rate by 9.54%. This study can provide reference for the research of new flame retardant for bamboo products.