Mn4+-doped fluoride phosphors are efficient narrowband red-emitting phosphors for white light-emitting diodes (WLEDs) and backlight displays. However, erosion by moisture is the main obstacle that limits their application. In this work, LNSF:Mn4+ (Li0.06Na1.94Si0.94Mn0.06F6) with high quantum yield (QY), luminescent thermal stability, and waterproofness was synthesized using the H2O2-free reaction method at room temperature. Compared to NSF:Mn4+(Na2Mn0.06Si0.94F6), the QY value, luminescence thermal stability, and water resistance of LNSF:Mn4+ are obviously improved by codoping of Li+ because of the formation of charge-carrier transfer (CT) and rare-Mn4+ layer induced by codoping of Li+. The former produces the negative thermal quenching (NTQ) effect, which results in the improvement of the luminescent thermal stability. The latter can inhibit the hydrolysis of Mn4+ on the surface of the sample, which leads to the enhancement of waterproofness. The formation mechanism of the rare-Mn4+ layer is discussed. A prototype WLED emitting the ideal warm white light (CCT = 3173 K, Ra = 90.4) was assembled by coating a mixture of LNSF:Mn4+, yellow emitting phosphor (YAG:Ce3+), and epoxy resin on the blue light InGaN chip, indicating that the performance of the WLED can be improved by using LNSF:Mn4+.
RESUMEN
Herein, a series of NSF:0.05Mn4+,0.04K+@GQD (NSF: Na2SiF6, GQDs: Cl-containing graphene quantum dot) phosphors was prepared. Double enhancement effects on the luminescent intensity and thermal stability triggered by the GQD coating were observed for the optimal sample as follows: (a) its PL intensity was 1.72 times that of the uncoated control sample and (b) its luminescent thermal stability was greatly enhanced, with integrated PL intensities of 120, 150 and 180 °C to 179.7%, 175.8%, and 119.3% of the initial value at 25 °C, respectively. It is proposed that the above-mentioned behaviors involve a change in some of the thermal energy into light energy via a phonon-induced mechanism. The thermal stability analysis results showed that the optimal sample is suitable for application in high-power WLEDs. Specifically, warm white light with a low correlated color temperature, high luminescent efficiency and high color rendering index was obtained from the prototype WLEDs using the optimal sample as a red-emitting component.