Local Structure in Crystalline, Glass and Melt States of a Hybrid Metal Halide Perovskite.

The pursuit of structure-property relationships in crystalline metal halide perovskites (MHPs) has yielded an unprecedented combination of advantageous characteristics for wide-ranging optoelectronic applications. While crystalline MHP structures are readily accessible through diffraction-based structure refinements, providing a clear view of associated long-range ordering, the local structures in more recently discovered glassy MHP states remain unexplored. Herein, we utilize a combination of Raman spectroscopy, solid-state nuclear magnetic resonance (NMR), Fourier transform infrared spectroscopy, in situ X-ray diffraction (XRD) and pair distribution function (PDF) analysis to investigate the coordination environment in crystalline, glass and melt states of the 2D MHP [(S)-(-)-1-(1-naphthyl)ethylammonium]2PbBr4. While crystalline SNPB shows polarization-dependent Raman spectra, the glassy and melt states exhibit broad features and lack polarization dependence. Solid-state NMR reveals disordering at the organic-inorganic interface of the glass due to significant spatial disruption in the tethering ammonium groups and the corresponding dihedral bond angles connecting the naphthyl and ammonium groups, while still preserving substantial naphthyl group registry and remnants of the layering from the crystalline state (deduced from XRD analysis). Moreover, PDF analysis demonstrates the persistence of corner-sharing PbBr6 octahedra in the inorganic framework of the melt/glass phases, but with a loss of structural coherence over length scales exceeding approximately one octahedron due to disorder in the inter- and intraoctahedra bond angles/lengths. These findings deepen our understanding of diverse MHP structural motifs and how structural alterations within the MHP glass affect properties, offering potential for advancing next-generation phase change materials and devices.

Quantitative determination of the phosphorus environment in lithium aluminosilicate glasses using solid-state NMR techniques.

We investigated using solid-state NMR spectroscopy the short-range structural features in lithium aluminosilicate glasses with the addition of P2O5 and considering various Al2O3/Li2O ratios. The phosphorus environment is determined quantitatively using 31P Magic Angle Spinning NMR constrained by results obtained from 31P-27Al Multiple-Quantum Coherence-based NMR techniques. Phosphorus is mainly located as orthophosphate and pyrophosphate species in glasses with a low amount of Al2O3. These depolymerized units disappear with increasing Al2O3 content and a strong affinity of PO4 tetrahedra for aluminum is revealed, which reduces phase separation. The local environments of framework (Si and Al) and charge-balancing (Li) cations are also studied through NMR experiments to assess the influence of P2O5 addition. The Si environment is mostly modified by the presence of P2O5 in glasses containing a low amount of Al2O3, with an increase of Q4Si species in relation to phase separation phenomena observed in these compositions. Conversely, P2O5 addition does not have a significant influence on the 27Al NMR response. 7Li NMR spectra reflect a change in the structural role of Li when P2O5 or Al2O3 is added. The observed structural changes can be rationalized to improve our knowledge of the structure-property relationships, focusing, in particular, on phase separation and nucleation/crystallization processes that are strongly affected by the presence of P and the evolution of its local environment with composition.

Observation of proximities between spin-1/2 and quadrupolar nuclei in solids: Improved robustness to chemical shielding using adiabatic symmetry-based recoupling.

We introduce a novel heteronuclear dipolar recoupling based on the R21-1 symmetry, which uses the tanh/tan (tt) shaped pulse as a basic inversion element and is denoted R21-1(tt). Using first-order average Hamiltonian theory, we show that this sequence is non-γ-encoded and that it reintroduces the |m| = 1 spatial component of the Chemical Shift Anisotropy (CSA) of the irradiated isotope and its heteronuclear dipolar interactions. Using numerical simulations and one-dimensional (1D) 27Al-{31P} through-space D-HMQC (Dipolar Heteronuclear Multiple-Quantum Correlation) experiments on VPI-5, we compare the performances of this recoupling to those of other non-γ-encoded |m| = 1 heteronuclear recoupling schemes: REDOR (Rotational-Echo DOuble Resonance), SFAM (Simultaneous Frequency and Amplitude Modulation) and R42-1(tt). Such comparison indicates that the R21-1(tt) scheme is more robust to CSA, offset and radiofrequency field inhomogeneities than the other schemes. We take advantage of the high robustness of R21-1(tt) to CSA and offset to demonstrate the possibility to correlate the signals of 207Pb isotope with those of neighboring half-integer spin quadrupolar nuclei. Such approach is demonstrated experimentally by acquiring 11B-{207Pb} D-HMQC 2D spectra of Pb4O(BO3)2 crystalline powder.

Structure and thermal relaxation of network units and crystallization of lithium silicate based glasses doped with oxides of Al and B.

The current study reports on the relaxation behaviour of lithium silicate based glasses as probed by NMR spectroscopy. A total of four glass compositions were studied with the parent composition being 28Li2O-72SiO2, and added dopants of Al and B. All the compositions showed significant differences in the NMR spectra of both annealed and non-annealed glasses demonstrating the structural relaxation behaviour. We extended our binary statistical mechanical model to these complex compositions to study the relaxation behaviour. By the combined use of the extended statistical mechanical model and broken ergodicity, we shed light on the mechanism of structural relaxation as understood by NMR spectroscopy. We studied the crystallization behaviour of the glasses and reported on the variations of the residual glass composition changes in the crystallization fraction.

31P MAS NMR spectroscopy with 93Nb decoupling and DFT calculations: A structural characterization of defects in a niobium-phosphate phase.

The present study has investigated the structure of four niobium phosphates compounds using 31P MAS NMR spectroscopy. Niobium 93Nb decoupling, applied during 31P NMR acquisition led to a resolution enhancement by a factor of 2-3, which allowed distinguish phosphorous sites separated by 1 ppm or less. The assignment of 31P spectra has been completed by use of first-principles calculations derived from the original XRD structures. One of the compounds, Na3.04Nb7P4O29, contains a sodium vacancy, clearly revealed in the 31P MAS spectrum obtained with 93Nb decoupling. A series of structural models were proposed to account for the sodium distribution in the structure of Na3.04Nb7P4O29 and the assignment was possible using DFT calculation and a statistical analysis of the NMR parameters.

Statistics of silicate units in binary glasses.

In this paper, we derive a new model to determine the distribution of silicate units in binary glasses (or liquids). The model is based on statistical mechanics and assumes grand canonical ensemble of silicate units which exchange energy and network modifiers from the reservoir. This model complements experimental techniques, which measure short range order in glasses such as nuclear magnetic resonance (NMR) spectroscopy. The model has potential in calculating the amounts of liquid-liquid phase segregation and crystal nucleation, and it can be easily extended to more complicated compositions. The structural relaxation of the glass as probed by NMR spectroscopy is also reported, where the model could find its usefulness.

B2O3-Doped LATP Glass-Ceramics Studied by X-ray Diffractometry and MAS NMR Spectroscopy Methods.

Two families of glasses in the Li2O-Al2O3-B2O3-TiO2-P2O5 system were prepared via two different synthesis routes: melt-quenching and ball-milling. Subsequently, they were submitted to crystallization and yielded the Li1.3Al0.3Ti1.7(PO4)3 (LATP)-based glass-ceramics. Glasses and corresponding glass-ceramics were studied by complementary X-ray diffraction (XRD) and 27Al, 31P, 7Li, 11B magic-angle spinning nuclear magnetic resonance (MAS NMR) methods in order to compare their structure and phase composition and elucidate the impact of boron additive on their glass-forming properties and crystallization process. XRD studies show that the addition of B2O3 improves the glass-forming properties of glasses prepared by either method and inhibits the precipitation of unwanted phases during heat treatment. MAS NMR studies allowed us to distinguish two LATP phases of slightly different chemical composition suggesting that LATP grains might not be homogeneous. In conclusion, the crystallization of boron-incorporated LATP glasses can is an effective way of obtaining LATP-based solid state electrolytes for the next generation of lithium-ion batteries provided the proper heat-treatment conditions are chosen.

New insights into oxygen environments generated during phosphate glass alteration: a combined 17O MAS and MQMAS NMR and first principles calculations study.

In the present study, we used a combination of (17)O NMR methods at a high magnetic field with first-principles calculations in order to characterize the oxygen sites in a series of hydroxylated sodium phosphate compounds, namely the hydrogen pyrophosphate Na(2)H(2)P(2)O(7) and the hydrogen orthophosphates NaH(2)PO(4), NaH(2)PO(4) x H(2)O and NaH(2)PO(4) x 2 H(2)O. The chemical shifts and quadrupolar parameters of these compounds were interpreted in terms of local and semi-local environment, i.e., the chemical composition of the immediate surroundings and the nature of the bonds, e.g. hydrogen bonding. The magnitude of the quadrupolar interaction and its asymmetry were revealed to be a precise indicator of the local structure in sodium hydrogen phosphates. Our (17)O NMR experimental and computing approach allowed for identification and quantification of the different crystalline phases involved in the weathering mechanism of a sodium phosphate glass, even in small amount.

Characterization of self-healing glassy composites by high-temperature environmental scanning electron microscopy (HT-ESEM).

In situ high-temperature healing of cracks in composites made of glass and vanadium boride (VB) particles was observed using an environmental scanning electron microscope equipped with a high-temperature chamber (HT-ESEM). HT-ESEM is an adequate tool for studying the self-healing property of these materials. The change in crack length as a function of redox atmospheric conditions is reported. No self-healing behaviour was observed under reducing conditions, while a complete and rapid healing of the cracks was measured under oxidizing conditions. HT-ESEM image analyses enabled the monitoring of the healing effect. The self-healing mechanism was identified as a consequence of the VB active particles oxidation and subsequent pouring of fluid oxides into the cracks. These innovative composites offer an interesting potential in the domain of solid oxide fuel cell sealants.

First-principles calculations of NMR parameters for phosphate materials.

In this short review, we discuss the ability to reproduce NMR parameters in the case of phosphates materials through electronic structure calculation within density functional theory linear response. Indeed, the gauge-including projector-augmented wave is today largely used by the solid-state NMR community as a tool for structural determination and it has been applied to a large variety of materials. We emphasise on the crucial points that should be taken into account to perform such calculations. In particular, we discuss the influence of the electronic structure and of the geometry on the calculation of NMR parameters. To illustrate the review, we present experimental and theoretical comparison of (31)P, (1)H and (23)Na NMR data on a series of sodium phosphate systems.

17O solid-state NMR and first-principles calculations of sodium trimetaphosphate (Na3P3O9), tripolyphosphate (Na5P3O10), and pyrophosphate (Na4P2O7).

The assignment of high-field (18.8 T) (17)O MAS and 3QMAS spectra has been completed by use of first-principles calculations for three crystalline sodium phosphates, Na 3P 3O 9, Na 5P 3O 10, and Na 4P 2O 7. In Na 3P 3O 9, the calculated parameters, quadrupolar constant ( C Q), quadrupolar asymmetry (eta Q), and the isotropic chemical shift (delta cs) correspond to those deduced experimentally, and the calculation is mandatory to achieve a complete assignment. For the sodium tripolyphosphate Na 5P 3O 10, the situation is more complex because of the free rotation of the end-chain phosphate groups. The assignment obtained with ab initio calculations can however be confirmed by the (17)O{ (31)P} MAS-J-HMQC spectrum. Na 4P 2O 7 (17)O MAS and 3QMAS spectra show a complex pattern in agreement with the computed NMR parameters, which indicate that all of the oxygens exhibit very similar values. These results are related to structural data to better understand the influence of the oxygen environment on the NMR parameters. The findings are used to interpret those results observed on a binary sodium phosphate glass.

A new 17O-isotopic enrichment method for the NMR characterisation of phosphate compounds.

Heating phosphate compounds under (17)O-enriched water vapour is an easy and rapid method to prepare homogeneously enriched and pure samples for the acquisition of (17)O NMR spectra with a good sensitivity.

Self-Healing Glassy Thin Coating for High-Temperature Applications.

Glass thin films (with nanometer to micrometer thicknesses) are promising in numerous applications, both as passive coatings and as active components. Self-healing is a feature of many current technological developments as a means of increasing the lifetime of materials. In the context of these developments, we report on the elaboration of the first self-healing glassy thin-film coating developed specifically for high-temperature applications. This coating is obtained by pulsed laser deposition of alternating layers of vanadium boride (VB) and a multicomponent oxide glass. Self-healing is obtained through the oxidation of VB at the operating temperature. The investigation of the effect of elaboration parameters on the coating composition and morphology made it possible to obtain up to seven-layer coatings, with good homogeneity and perfect interfaces, and with a total thickness of less than 1 µm. The autonomic self-healing capacity of the coating has been demonstrated by an in situ experiment, which shows that a crack of nanometric dimension can be healed within a few minutes at 700 °C.

Phase identification and quantification in a devitrified glass using homo- and heteronuclear solid-state NMR.

A complex mixture resulting from the devitrification of an aluminophosphate glass has been studied for the first time using a combination of homo- and heteronuclear solid-state NMR sequences that offers the advantage of subsequent quantification.

A very sensitive high-resolution NMR method for quadrupolar nuclei: SPAM-DQF-STMAS.

We show that by combining the intrinsically larger (with respect to MQMAS) efficiency of Double-Quantum Filtered Satellite-Transition MAS (DQF-STMAS), with the large S/N gain of the Soft-Pulse Added Mixing (SPAM) concept, a new very sensitive high-resolution solid-state NMR method can be obtained for semi-integer quadrupolar nuclei.

Immobilization of radioactive iodine in silver aluminophosphate glasses.

Silver aluminophosphate glasses have been investigated as matrices for the immobilization of radioactive iodine. In this study, up to 28mol% AgI have been incorporated without volatilization thanks to a low temperature synthesis protocol. Alumina was added in the composition in order to increase the glass transition temperature for a better thermal stability in a repository conditions. Two series of glasses have been investigated, based on AgPO3 and Ag5P3O10 compositions, and with 0-5mol% Al2O3. We report (31)P, (27)Al and (109)Ag NMR study of these glasses, including advanced measurement of the connectivities through {(27)Al}-(31)P cross-polarization and (31)P-(31)P double-quantum correlation. We confirm that AgI is inserted in the aluminophosphate glasses and does not form clusters. AgI does not induce any modification of the glass polymerization but only an expansion of the network. Despite no evidence for crystallization could be obtained from XRD, NMR revealed that the introduction of AgI induces an exclusion of alumina from the network, leading to the crystallization of aluminophosphate phases such as Al(PO3)3 or AlPO4. As a consequence, despite NMR gives evidence for the presence of aluminophosphate bonds, only a limited effect of alumina addition on thermal properties is observed.

SPAM-MQ-HETCOR: an improved method for heteronuclear correlation spectroscopy between quadrupolar and spin-1/2 nuclei in solid-state NMR.

The recently introduced concept of soft pulse added mixing (SPAM) is used in two-dimensional heteronuclear correlation (HETCOR) NMR experiments between half-integer quadrupolar and spin-1/2 nuclei. The experiments employ multiple quantum magic angle spinning (MQMAS) to remove the second order quadrupolar broadening and cross polarization (CP) or refocused INEPT for magnetization transfer. By using previously unexploited coherence pathways, the efficiency of SPAM-MQ-HETCOR NMR is increased by a factor of almost two without additional optimization. The sensitivity gain is demonstrated on a test sample, AlPO(4)-14, using CP and INEPT to correlate (27)Al and (31)P nuclei. SPAM-3Q-HETCOR is then applied to generate (27)Al-(31)P spectra of the devitrified 41Na(2)O-20.5Al(2)O(3)-38.5P(2)O(5) glass and the silicoaluminophosphate ECR-40. Finally, the method allowed the acquisition of the first high resolution solid-state correlation spectra between (27)Al and (29)Si.

Combined 17O NMR and 11B-31P double resonance NMR studies of sodium borophosphate glasses.

17O enriched sodium borophosphate glasses were prepared from isotopically enriched NaPO3 and H3BO3. These glasses have been studied by 17O, 11B and 31P NMR including 17O and 11B multiple quantum magic angle sample spinning (MQMAS), 11B-31P heteronuclear correlation (HETCOR) NMR and 11B{31P} rotational echo double resonance (REDOR). For comparison, the crystalline borophosphates BPO4 and Na5B2P3O13 were included in the investigations. The latter compound shows three sharp 31P resonances at -0.2, -2 and -8 ppm and two BO4 sites that can only be resolved by MQMAS. The 17O NMR spectra were recorded using both the static echo method at medium magnetic field (9.4 T) as well as MAS and MQMAS methods at high field (17.6 T). In total, five oxygen sites were identified in these borophosphate glasses: P-O-P, Na...O-P, P-O-B, B-O-B, Na...O-B. However, these five sites are not present simultaneously in any of the glasses. The 17O MQMAS spectra prove that P-O-B links play a major role in borophosphate glasses. These results are confirmed by the complementary 11B MAS spectra that show the presence of asymmetric and symmetric trigonal groups BO3a and BO3s and two tetrahedral BO4 units. 11B{31P} REDOR NMR is used to give independent information to assign the 11B lines to structural units present in the glasses. These REDOR measurements reveal that B-O-P bonds are present for each borate unit, including the BO3 groups. Particularly, a structural proposal for the two different BO4 resonances is given in terms of a different number of bonded phosphate tetrahedra. The 31P MAS spectra are usually broad and not well resolved. It is shown by 11B-31P HETCOR NMR that a possible structural assignment of a 31P signal at about -20 ppm to Q2 units as in binary sodium phosphate glasses is wrong and that the phosphate tetrahedron belonging to this resonance must be connected to borate groups.