RESUMEN
Block copolymer-mediated self-assembly of colloidal nanoparticles has attracted great attention for fabricating various nanoparticle arrays. We have previously shown that silica nanoparticles (SNPs) assemble into ring-like nanostructures in the presence of temperature-responsive block copolymers poly[(2-ethoxyethyl vinyl ether)-block-(2-methoxyethyl vinyl ether)] (PEOVE-PMOVE) in an aqueous phase. The ring-like nanostructures formed within an aggregate of PEOVE-PMOVE when the temperature was increased to 45 °C, at which the polymer is amphiphilic. Herein, we report that SNPs assemble into ring-like nanostructures even with a different temperature-responsive, amphiphilic block copolymer poly(propylene oxide)-block-poly(ethylene oxide) (PPO-PEO) at 45 °C. Field-emission scanning electron microscopy for SNP assemblies that were spin-coated on a substrate indicated that SNP first assembled into chain-like nanostructures and then bent into closed loops over several days. In contrast, in situ small-angle X-ray diffraction measurements revealed the formation of SNP nanorings within 75 s at 45 °C in the liquid phase. These results indicated that ring-like assembly of SNPs occurs quickly in the liquid phase, but the slow formation of Si-O-Si bonds between SNPs leads to their structure being destroyed by spin-coating. Intriguingly, SNPs with a diameter of 15 nm form a well-defined nanoring structure, with five SNPs located at the vertex points of a regular pentagon. Additionally, small-angle neutron scattering, where the contrast of the solvent (a mixture of H2O and D2O) matches that of SNPs, clarified that SNPs are contained within the spherical micelle formed from PPO-PEO. This work offers a facile and versatile approach to preparing ring-like arrays from inorganic colloidal nanoparticles, leading to applications including sensing, catalysis, and nanoelectronics.
RESUMEN
Ceramic biomaterials have been used for the treatment of bone defects and have stimulated intense research on such materials. We have previously reported that a salt composed of calcium ions and a phosphate ester (SCPE) transformed into hydroxyapatite (HAp) in a simulated body fluid (SBF) modified with alkaline phosphatase (ALP), and proposed SCPEs as a new category of ceramic biomaterials, namely bioresponsive ceramics. However, the factors that affect the transformation of SCPEs to HAp in the SBF remained unclear. Therefore, in this study, we investigated the behaviour of calcium salts of methyl phosphate (CaMeP), ethyl phosphate (CaEtP), butyl phosphate (CaBuP), and dodecyl phosphate (CaDoP) in SBF with and without ALP modification. For the standard SBF, an X-ray diffraction (XRD) analysis indicated that these SCPEs did not readily transform into calcium phosphate. However, CaMeP, CaEtP, and CaBuP were transformed into HAp and octacalcium phosphate in the SBF modified with ALP; therefore, these SCPEs can be categorised as bioresponsive ceramics. Although CaDoP did not exhibit a sufficient response to ALP to be detected by XRD, it is likely to be a bioresponsive ceramic based on the results of morphological observations. The transformation rate for the SCPEs decreased with increasing size of the linear alkyl group of the phosphate esters. The rate-determining steps for the transformation reaction of the SCPEs were changed from the dissolution of the SCPEs to the hydrolysis of the phosphate esters with increasing size of the phosphate ester alkyl groups. These findings contribute to designing novel bioresponsive ceramic biomaterials.
RESUMEN
The present study aims to develop a layered zirconium phosphate/phosphonate (LZP) powder to control the release of therapeutic inorganic ions. Organically modified LZPs were successfully prepared with various contents of phenyl groups via a reflux method in an aqueous solution containing phosphoric and phenylphosphonic acids. Powder X-ray diffraction analysis and Fourier transform infrared spectroscopy revealed that the crystal structure of the synthesized LZP samples was identical to that of α-zirconium phosphate, even after modification. The amount of incorporated organic molecules increased with increasing molar fractions of phenylphosphonic acid in the starting composition, as determined from the thermal analysis. Cobalt ion (Co2+), a type of therapeutic inorganic ion, was incorporated into the organically modified LZP through treatment with an acetonitrile solution containing tetrabutylammonium ions, followed by treatment with an acetonitrile solution containing CoCl2. The amount of incorporated Co2+ depended on the concentration of the phenyl groups. Furthermore, the highest amount of Co2+ was incorporated in the sample (ZP-Ph-0.5) prepared with equimolar phosphoric/phenylphosphonic acid. The ZP-Ph-0.5 sample additionally showed the ability to incorporate copper or iron ions (Cu2+ or Fe3+). The incorporated ion, either Co2+ or Cu2+, was continuously released from the ZP-Ph-0.5 sample in a saline solution over a period of three weeks, whereas the release of Fe3+ was negligible. The quantity of Co2+ released was higher than that of Cu2+. The controlled release of Co2+ from the ZP-Ph-0.5 sample was also observed in a simulated body fluid that mimicked the ionic concentration of human blood plasma. These results confirm that a specific degree of phenyl modification makes LZP a candidate host material for releasing therapeutic inorganic ions.
RESUMEN
Physically crosslinked hydrogels with thixotropic properties attract considerable attention in the biomedical research field because their self-healing nature is useful in cell encapsulation, as injectable gels, and as bioinks for three-dimensional (3D) bioprinting. Here, we report the formation of thixotropic hydrogels containing nanofibers of double-hydrophobic elastin-like polypeptides (ELPs). The hydrogels are obtained with the double-hydrophobic ELPs at 0.5 wt%, the concentration of which is an order of magnitude lower than those for previously reported ELP hydrogels. Although the kinetics of hydrogel formation is slower for the double-hydrophobic ELP with a cell-binding sequence, the storage moduli G' of mature hydrogels are similar regardless of the presence of a cell-binding sequence. Reversible gel-sol transitions are demonstrated in step-strain rheological measurements. The degree of recovery of the storage modulus G' after the removal of high shear stress is improved by chemical crosslinking of nanofibers when intermolecular crosslinking is successful. This work would provide deeper insight into the structure-property relationships of the self-assembling polypeptides and a better design strategy for hydrogels with desired viscoelastic properties.
Asunto(s)
Elastina/química , Hidrogeles/química , Interacciones Hidrofóbicas e Hidrofílicas , Nanofibras/química , Péptidos/química , Secuencia de Aminoácidos , Reactivos de Enlaces Cruzados/química , Módulo de Elasticidad , Iridoides/química , Nanofibras/ultraestructura , ReologíaRESUMEN
Elastin-like polypeptides (ELPs) are promising candidates for fabricating tissue-engineering scaffolds that mimic the extracellular environment of elastic tissues. We have developed a "double-hydrophobic" block ELP, GPG, inspired by non-uniform distribution of two different hydrophobic domains in natural elastin. GPG has a block sequence of (VGGVG)5-(VPGXG)25-(VGGVG)5 that self-assembles to form nanofibers in water. Functional derivatives of GPG with appended amino acid motifs can also form nanofibers, a display of the block sequence's robust self-assembling properties. However, how the block length affects fiber formation has never been clarified. This study focuses on the synthesis and characterization of a novel ELP, GPPG, in which the central sequence (VPGVG)25 is repeated twice by a short linker sequence. The self-assembly behavior and the resultant nanostructures of GPG and GPPG were when compared through circular dichroism spectroscopy, atomic force microscopy, and transmission electron microscopy. Dynamic rheology measurements revealed that the nanofiber dispersions of both GPG and GPPG at an extremely low concentration (0.034 wt%) exhibited solid-like behavior with storage modulus G' > loss modulus G" over wide range of angular frequencies, which was most probably due to the high aspect ratio of the nanofibers that leads to the flocculation of nanofibers in the dispersion.
Asunto(s)
Elastina/química , Nanofibras/química , Péptidos/química , Secuencia de Aminoácidos , Interacciones Hidrofóbicas e Hidrofílicas , Microscopía de Fuerza Atómica , Peso Molecular , Nanofibras/ultraestructura , Reología , Análisis EspectralRESUMEN
Block copolymer-mediated self-assembly of colloidal nanoparticles has attracted great attention for the fabrication of a wide variety of nanoparticle arrays. We have previously shown that silica nanospheres (SNSs) 15 nm in diameter assemble into ring-like nanostructures in the presence of amphiphilic block copolymers poly[(2-ethoxyethyl vinyl ether)- block-(2-methoxyethyl vinyl ether)] (EOVE-MOVE) in an aqueous phase. Here, the effects of particle size of SNSs on this polymer-mediated self-assembly are studied systematically using scanning electron microscopy to observe SNSs of seven different sizes between 13 to 42 nm. SNSs of 13, 16, 19, and 21 nm in diameter assemble into nanorings in the presence of EOVE-MOVE. In contrast, larger SNSs of 26, 34, and 42 nm aggregate heavily, form chain-like networks, and remain dispersed, respectively, instead of forming ring-like nanostructures. The assembly trend for 26-42 nm-SNSs agrees with that expected from the increased colloidal stability for larger particles. Time-course observation for the assembled morphology of 16 nm-SNSs reveals that the nanorings, once formed, assemble further into network-like structures, as if the nanorings behave as building units for higher-order assembly. This indicates that the ring-like assembly is a fast process that can proceed onto random colloidal aggregation. Detailed analysis of nanoring structures revealed that the average number of SNSs comprising one ring decreased from 5.0 to 3.1 with increasing the SNS size from 13 to 21 nm. A change in the number of ring members was also observed when the length of EOVE-MOVE varied while the size of SNSs was fixed. Dynamic light scattering measurements and atomic force microscopy confirmed the SNSs/polymer composite structures. We hypothesize that a stable composite morphology may exist that is influenced by both the size of SNSs and the polymer molecular structures.
RESUMEN
Surface morphology is a key factor that might significantly influence the properties of biomaterials. In this study, periodic surface-ring structures have been constructed for calcium phosphate thin films via biomineralization-inspired crystallization process. The patterned octacalcium phosphate crystals have been obtained on poly(2-hydroxyethyl methacrylate) (PHEMA) matrix in the presence of poly(acrylic acid) (PAA). The patterned surface morphologies of the crystal thin films could be tuned by the amount of PAA additives. In addition, the rapid and topotactic transformation to hydroxyapatite (HAP) thin films with surface-ring structures has also been achieved. This study may provide new strategy toward the design of functional calcium phosphate-based thin-film hybrids.
RESUMEN
α-tricalcium phosphate (α-TCP, α-Ca3(PO4)2) receives great attention for bone repairing due to its biodegradability and capability of transformation to human bone's main inorganic components, hydroxyapatite (HAp). α-TCP porous scaffold is easily procurable by sintering of the low-temperature polymorph of TCP, ß-TCR Still, porous body of α-TCP is too brittle to being handled and shaped, limiting its clinical application as implant materials. To improve mechanical properties of α-TCP porous scaffold, the present study focused on coating of a type of polysaccharides on α-TCP scaffolds. Gellan gum was chosen as the polysaccharide for coating because of its biodegradability as well as the potential acting as substrate for HAp deposition during hydration of α-TCP after exposure to body fluid. After coating of gellan gum on α-TCP scaffolds with porosity of 75 vol%, the compressive strength increased from 0.45 MPa to around 2.00 MPa. Among the coated scaffold, the maximum compressive strength, 3.97 MPa, was obtained on the scaffold with porosity of 63 vol%. Improvement of mechanical properties of α-TCP/gellan gum composites was achieved to show easy handling performance for a bone substitute for tissue repairing. The dissolving rate of the coated scaffolds was also controlled by adjusting the concentration of GG solutions.
Asunto(s)
Huesos , Fosfatos de Calcio/química , Polisacáridos Bacterianos/química , Ingeniería de Tejidos , Andamios del Tejido , Microscopía Electrónica de Rastreo , Porosidad , Difracción de Rayos XRESUMEN
The aim of this study was to propose and validate a new unified method for testing dissolution rates of bioactive glasses and their variants, and the formation of calcium phosphate layer formation on their surface, which is an indicator of bioactivity. At present, comparison in the literature is difficult as many groups use different testing protocols. An ISO standard covers the use of simulated body fluid on standard shape materials but it does not take into account that bioactive glasses can have very different specific surface areas, as for glass powders. Validation of the proposed modified test was through round robin testing and comparison to the ISO standard where appropriate. The proposed test uses fixed mass per solution volume ratio and agitated solution. The round robin study showed differences in hydroxyapatite nucleation on glasses of different composition and between glasses of the same composition but different particle size. The results were reproducible between research facilities. Researchers should use this method when testing new glasses, or their variants, to enable comparison between the literature in the future.
Asunto(s)
Apatitas/química , Materiales Biomiméticos/química , Materiales Biomiméticos/normas , Líquidos Corporales/química , Cerámica/química , Vidrio/química , Ensayo de Materiales/normas , Apatitas/normas , Cerámica/análisis , Cerámica/normas , Vidrio/análisis , Vidrio/normas , Internacionalidad , Ensayo de Materiales/métodos , Tamaño de la Partícula , Estándares de Referencia , Reproducibilidad de los Resultados , Sensibilidad y EspecificidadRESUMEN
Bioresponsive ceramics, a new concept in ceramic biomaterials, respond to biological molecules or environments, as exemplified by salts composed of calcium ions and phosphate esters (SCPEs). SCPEs have been shown to form apatite in simulated body fluid (SBF) containing alkaline phosphatase (ALP). Thus, surface modification with SCPEs is expected to improve the apatite-forming ability of a material. In this study, we modified the surface of α-tricalcium phosphate (α-TCP) using methyl, butyl, or dodecyl phosphate to form SCPEs and investigated their apatite formation in SBF and SBF containing ALP. Although apatite did not form on the surface of the unmodified α-TCP in SBF, apatite formation was observed following surface modification with methyl or butyl phosphate. When ALP was present in SBF, apatite formation was especially remarkable on α-TCP modified with butyl phosphate. These SCPEs accelerated apatite formation by releasing calcium ions through dissolution and supplying inorganic phosphate ions, with the latter process only occurring in SBF containing ALP. Notably, no apatite formation occurred on α-TCP modified with dodecyl phosphate, likely because of the low solubility of the resulting calcium dodecyl phosphate/calcium phosphate composites. This new method of using SCPEs is anticipated to contribute to the development of novel ceramic biomaterials.
RESUMEN
Several varieties of ceramics, such as Bioglass-type glasses, sintered hydroxyapatite and glass-ceramic A-W, exhibit specific biological affinity, i.e., direct bonding to surrounding bone, when implanted in bony defects. These bone-bonding ceramics are called bioactive ceramics and are utilized as important bone substitutes in the medical field. However, there is a limitation to their clinical applications because of their inappropriate mechanical properties. Natural bone takes a kind of organic-inorganic composite, where apatite nanocrystals are precipitated on collagen fibers. Therefore, problems with the bioactive ceramics can be solved by material design based on the composites. In this paper, current research topics on the development of bioactive organic-inorganic composites inspired by actual bone microstructure have been reviewed in correlation with preparation methods and various properties. Several kinds of inorganic components have been found to exhibit bioactivity in the body environment. Combination of the inorganic components with various organic polymers enables the development of bioactive organic-inorganic composites. In addition, novel biomedical applications of the composites to drug delivery systems, scaffolds for tissue regeneration and injectable biomaterials are available by combining drugs or biological molecules with appropriate control of its microstructure.
Asunto(s)
Sustitutos de Huesos/química , Cerámica/química , Nanocompuestos/química , Humanos , Polímeros/químicaRESUMEN
Glass ionomer cements (GICs) are composed of an acid degradable glass, polyacrylic acid and water. Sol-gel processing to prepare the glass phase has certain advantages, such as the ability to employ lower synthesis temperatures than melt quenching and glasses that are reported to have higher purity. A previous study reported the effects of glass synthesis route on GIC fabrication. However, in that study, the sol-gel derived glass exhibited a reduced concentration of cations. This study investigates increasing the cation content of a sol-gel derived glass, 12CaO.4SrO.36ZnO.48SiO2 (molar ratio) by heating before aging to reduce dissolution of cations. This glass was prepared by both sol-gel and melt-quenched routes. GICs were subsequently prepared using both glasses. The resultant cement based on the sol-gel derived glass had a shorter working time than the cement based on the melt-quenched one. Contrary to this, setting time was considerably longer for the cement based on the sol-gel derived glass than for the cement based on the melt-quenched one. The cements based on the sol-gel derived glass were stronger in both compression and biaxial flexure than the cements prepared from the melt-quenched glass. The differences in setting and mechanical properties were associated with both cation content in the glass phase and the different surface area of the resultant cements.
Asunto(s)
Compuestos de Calcio/química , Cementos de Ionómero Vítreo/química , Vidrio/química , Óxidos/química , Silicio/química , Estroncio/química , Óxido de Zinc/química , Cationes , Fuerza Compresiva , Cementos Dentales/química , Tamaño de la Partícula , Transición de Fase , Polvos , Presión , Estrés Mecánico , TemperaturaRESUMEN
Strategic materials design is essential for the development of small-diameter, tissue-engineered vascular grafts. Self-assembled nanofibers of elastin-like polypeptides represent promising vascular graft components as they replicate the organized elastin structure of native blood vessels. Further, the bioactivity of nanofibers can be modified by the addition of functional peptide motifs. In the present study, we describe the development of a novel nanofiber-forming elastin-like polypeptide (ELP) with an arginine-glutamic acid-aspartic acid-valine (REDV) sequence. The biological characteristics of the REDV-modified ELP nanofibers relevant to applications in vascular grafting were compared to ELP without ligands for integrin, ELP with arginine-glycine-aspartic acid (RGD) sequence, collagen and cell culture glass. Among them, REDV-modified ELP nanofibers met the preferred biological properties for vascular graft materials, i.e. (i) inhibition of platelet adhesion and activation, (ii) endothelial cell adhesion and proliferation and (iii) maintenance of smooth muscle cells in a contractile phenotype to prevent cell overgrowth. The results indicate that REDV-modified ELP nanofibers represent promising candidates for the further development of small-diameter vascular grafts.
RESUMEN
Double-step hydrothermal processing is a process where powder compacts of calcium phosphates are exposed to vapor of solvent solution, followed by being immersed in the solution. In the present study, we investigated the effects of ammonium carbonate on formation of calcium-deficient hydroxyapatite (CDHA) through double-step hydrothermal processing. The synthesized CDHA has high crystallinity when the solution has relatively low concentration of the ammonium carbonate ranging from 0.01 to 0.25 mol dm(-3). Carbonate content in the prepared samples were distinctly increased with increasing the concentration of ammonium carbonate to indicate formation of carbonate-containing calcium-deficient hydroxyapatite (CHAp) with low crystallinity. Morphology of the CHAp formed on the compacts varied progressively from rods and rosette-like shape to irregular shape with increase in the initial concentration of the ammonium carbonate in the solution. Application of ammonium carbonate in the double-step hydrothermal processing allows fabrication of irregular-shaped CDHA containing carbonate ions in both phosphate and hydroxide site, with low crystallinity, when the initial concentration of ammonium carbonate was 0.5 mol dm(-3) and more.
Asunto(s)
Calcio/química , Durapatita/química , Compuestos de Amonio Cuaternario/química , Carbonatos/química , Cristalización , Diseño de Equipo , Concentración de Iones de Hidrógeno , Hidróxidos/química , Iones , Ensayo de Materiales , Modelos Químicos , Fosfatos/química , Espectrofotometría Atómica/métodos , Temperatura , Difracción de Rayos XRESUMEN
Octacalcium phosphate (OCP; Ca8(HPO4)2(PO4)4 â 5H2O) is a precursor of hydroxyapatite found in human bones and teeth, and is among the inorganic substances critical for hard tissue formation and regeneration in the human body. OCP has a layered structure and can incorporate carboxylate ions into its interlayers. However, studies involving the incorporation of tetracarboxylic and multivalent (pentavalent and above) carboxylic acids into OCP have not yet been reported. In this study, we investigate the incorporation of pyromellitic acid (1,2,4,5-benzenetetracarboxylic acid), a type of tetracarboxylic acid, into OCP. We established that pyromellitate ions could be incorporated into OCP by a wet chemical method using an acetate buffer solution containing pyromellitic acid. The derived OCP showed a brilliant blue emission under UV light owing to the incorporated pyromellitate ions. Incorporation of a carboxylic acid into OCP imparted new functions, which could enable the development of novel functional materials for biomedical applications.
RESUMEN
Porous bulk composites were produced by depositing silver nanoparticles of diameter 11.0 +/- 3.2 nm on hydroxyapatite of micrometer sizes. Adsorption of bovine serum albumin (BSA) and lysozyme (LSZ) on the composite material was observed in 2 and 10 mol m(-3) phosphate buffer solutions. More BSA than LSZ was adsorbed in 2 mol m(-3) phosphate buffer and this was attributed to a larger a-face surface area present in the plate- and rod-shaped hydroxyapatite compared with the c-face surface area. Peak shifts in localized surface plasmon resonance (LSPR) spectra were clearly related to adsorbed amounts of BSA and LSZ after exposure of the porous bulk composites to protein solutions. The sensing capability of the porous bulk composite results from changes in the dielectric constant of the surface fluid surrounding the silver nanoparticles. Adsorption/desorption cycles of BSA were applied to the porous bulk composite, confirming the reversibility of the sensing capability.
Asunto(s)
Técnicas Biosensibles/instrumentación , Durapatita/química , Nanopartículas del Metal/química , Nanocompuestos/química , Proteínas/farmacocinética , Plata/química , Adsorción , Animales , Bovinos , Materiales Biocompatibles Revestidos/química , Modelos Biológicos , Muramidasa/metabolismo , Muramidasa/farmacocinética , Tamaño de la Partícula , Porosidad , Unión Proteica , Proteínas/metabolismo , Albúmina Sérica Bovina/metabolismo , Albúmina Sérica Bovina/farmacocinética , Resonancia por Plasmón de Superficie , Propiedades de SuperficieRESUMEN
The osteoconduction potential of artificial materials is usually evaluated in vitro by apatite formation in a simulated body fluid (SBF) proposed by Kokubo and his colleagues. This paper reports the compositional dependence of apatite formation on organic-inorganic hybrids in the CaO-SiO(2)-PO(5/2)-poly(tetramethylene oxide) system, initiated from tetraethoxysilane (TEOS), triethyl phosphate (OP(OEt)(3)), calcium chloride (CaCl(2)) and poly(tetramethylene oxide)(PTMO) modified with alkoxysilane. Formation of an apatite layer was observed on the surface of the organic-inorganic hybrids with molar ratios of TEOS/OP(OEt)(3) ranging from 100/0 to 20/80. The rate of apatite formation remarkably decreased when the hybrids were synthesized with TEOS/OP(OEt)(3) ratios of 40/60 or less. Hybrids without TEOS showed no apatite formation in SBF for up to 14 days. Addition of small amounts of OP(OEt)(3) to TEOS in the hybrids led to the high dissolution of calcium and silicate, while addition of large amounts of OP(OEt)(3) decreased the dissolution of calcium and silicate ions and resulted in reduced apatite formation regardless of the dissolution of phosphate ions from the hybrids.
Asunto(s)
Apatitas/síntesis química , Líquidos Corporales/química , Sustitutos de Huesos/química , Compuestos de Calcio/química , Glicoles/química , Óxidos/química , Dióxido de Silicio/química , Cristalización/métodos , Compuestos Inorgánicos/química , Ensayo de Materiales , Compuestos Orgánicos/químicaRESUMEN
Biomimetic mineralization of supramolecular scaffolds consisting of biomolecules or their analogues has received much attention recently from the viewpoint of creation of novel biomaterials. This study investigated biomimetic deposition of hydroxyapatite (HAp) on cerasomes, morphologically stable organic-inorganic hybrid vesicles. Scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction studies revealed that the pristine cerasomes induced heterogeneous nucleation of HAp when they were immersed in 1.5SBF, a solution having 1.5 times higher ion concentration than that of a simulated body fluid (SBF). The HAp deposition was further accelerated when dicarboxylic and monocarboxylic acid groups were displayed on cerasome surfaces. These carboxylic acid groups are expected to enhance calcium ion binding to the cerasome surface, causing an increase of HAp nucleation sites. At lower surface concentrations on the cerasome surface, the dicarboxylic acid group is apparently more effective for HAp deposition than the monocarboxylic acid group. The resultant HAp-cerasome hybrids are useful as biocompatible materials having unique properties deriving from the lipid bilayer structure of the cerasomes.
Asunto(s)
Materiales Biomiméticos/metabolismo , Líquidos Corporales/fisiología , Ácidos Carboxílicos/farmacología , Durapatita/farmacocinética , Liposomas/química , Dióxido de Silicio/química , Materiales Biomiméticos/química , Materiales Biomiméticos/farmacología , Líquidos Corporales/química , Líquidos Corporales/metabolismo , Ácidos Carboxílicos/química , Materiales Biocompatibles Revestidos/química , Materiales Biocompatibles Revestidos/metabolismo , Estabilidad de Medicamentos , Liposomas/metabolismo , Liposomas/farmacología , Ensayo de Materiales , Modelos Biológicos , Dióxido de Silicio/farmacología , Siloxanos/química , Siloxanos/farmacología , Propiedades de Superficie/efectos de los fármacos , Andamios del Tejido/químicaRESUMEN
Alpha-tricalcium phosphate (alpha-TCP) ceramic is a bioresorbable material that degrades in bone tissue after implantation, since it exhibits higher solubility than beta-tricalcium phosphate (beta-TCP) ceramics. The high solubility of alpha-TCP in an aqueous solution causes its transformation into hydroxyapatite (HAp) through hydrolysis. While one expects the formation of hydroxyapatite after exposure to an aqueous solution mimicking a body environment, we occasionally find variation in HAp formation in the simulated body fluid (SBF). In the present study, HAp formation resulting from exposure to SBF was investigated for some types of alpha-TCP ceramics with different porosities and specific surface area. Reduced porosity and large surface area of porous specimens may increase the local density of Ca2+ in the surrounding SBF to increase the degree of supersaturation with respect to HAp. Thus, the porosity and specific surface area are significant parameters for determining not only bioabsorbability but also the ability to form HAp.
Asunto(s)
Líquidos Corporales/química , Fosfatos de Calcio/química , Cerámica/química , Durapatita/síntesis química , Porosidad , SolubilidadRESUMEN
This study aims to evaluate the in vitro cytocompatibility of layered zirconium phosphate (ZP) and its derivative material that was organically modified using glycerophosphate (ZGP). The ZP and ZGP particles were prepared via a reflux method in an aqueous solution containing phosphoric acid. The field emission scanning electron microscopy showed the prepared samples were fine particles with 70-100 nm diameter. X-ray diffraction and Raman spectrometry indicated the presence of a layered crystal structure. The interlayer distance of ZP was estimated to be 0.76 nm from the 002 diffraction. Modification of ZP with ß-glycerophosphate, lead to expansion of the interlayer distance of 0.85 nm. Grazing incidence X-ray diffraction and Raman spectrometry showed that the crystal structures of ZP and ZGP were maintained even after the samples were coated onto polyethylene (PE) substrates via hot pressing. The water droplet contact angles on the PE substrates coated with the ZP and ZGP particles (ZP/PE and ZGP/PE) were 2 â¼ 6° lesser than that on the uncoated PE substrate. After human adipose-derived stem cells (hASCs) were cultured on the substrates, 2.5-3.5 times higher numbers of adhered cells were observed on the substrates coated with ZP and ZGP than on the uncoated PE substrates and 1.1-1.6 times higher than on the substrate coated with hydroxyapatite particles (HAp/PE). Increasing cell numbers were observed after culturing for 24 h, indicating that the ZP/PE and ZGP/PE showed low cytotoxicity to the hASCs. Furthermore, the ZP/PE showed the highest area of hASC adhesion among all the samples. These results highlight the possibility that layered zirconium phosphate and its organically modified substances can be applied to biomaterials for tissue repair.