Studying the Degradation of Three Polymers under Different Chlorine Concentrations and Exposure Times.

Due to chlorine's ability to kill bacteria and fungi through a chemical reaction, chlorine solutions are commonly used to clean and disinfect numerous public facilities, although these actions are also dependent to the equipment present in those facilities. Accordingly, the interest in studying its effect when in contact with different materials is obvious. This study was carried out through accelerated degradation tests and various analysis methods (optical microscope, scanning electron microscope, and tensile tests). The objective was to observe the wear presented by three polymeric materials, polyvinyl chloride (PVC), high-density polyethylene (HDPE), and polypropylene (PP), when exposed to chlorine's action in swimming pools and drinking water treatment plants. The resulting effect depends on the chlorine content and the type of contact between the chemical agent and the material. The aim was to select the material less likely to be affected by chlorine through tests and analyses, allowing a longer component life. The use of certain more resistant polymeric materials can drastically reduce maintenance, reducing fundamental factors such as costs, the downtime of municipal facilities, and also the risk to public health. It was concluded that PVC has the most stable behaviour overall when in contact with chlorine solutions.

The Impact of the Deterioration on Wood by Chlorine: An Experimental Study.

The use of disinfection and cleaning chemicals in several municipal facilities, such as swimming pools and drinking water treatment plants, causes the degradation of various types of wood, which leads to failures in equipment and the corresponding need for maintenance. This degradation creates added costs for municipalities, as well as the closure of certain facilities due to curative or preventive maintenance and, in many cases, public health issues, due to the water being contaminated with deteriorating products. Through a thorough study of the degradation effect on the products, more resistant materials can be found which are able to withstand these adversities and increase the lifespan of wood in regular contact with chemical agents. This is achievable by the determination of the cost-effectiveness of the substitute material to replace these components with alternative ones, with properties that better resist the deterioration effects promoted by aggressive environments. No studies have been found so far strictly focused on this matter. The objective of this study is to evaluate the degradation presented by two types of wood, beech and oak, which are exposed to the action of chlorine in municipal facilities. This degradation varies according to the chlorine content and the materials' time of contact with the chemical agent, allowing the selection of new materials which will provide an extended lifetime of the components, reducing maintenance drastically, as well as costs for the facilities and the risk to public health. The performed experimental tests have shown that the oak wood has the best results regarding chlorine degradation resistance.