Magnesium hydrides (MgH2) have drawn a lot of interest as a promising hydrogen storage material option due to their good reversibility and high hydrogen storage capacity (7.60 wt.%). However, the high hydrogen desorption temperature (more than 400 °C) and slow sorption kinetics of MgH2 are the main obstacles to its practical use. In this research, nickel zinc oxide (Ni0.6Zn0.4O) was synthesized via the solid-state method and doped into MgH2 to overcome the drawbacks of MgH2. The onset desorption temperature of the MgH2-10 wt.% Ni0.6Zn0.4O sample was reduced to 285 °C, 133 °C, and 56 °C lower than that of pure MgH2 and milled MgH2, respectively. Furthermore, at 250 °C, the MgH2-10 wt.% Ni0.6Zn0.4O sample could absorb 6.50 wt.% of H2 and desorbed 2.20 wt.% of H2 at 300 °C within 1 h. With the addition of 10 wt.% of Ni0.6Zn0.4O, the activation energy of MgH2 dropped from 133 kJ/mol to 97 kJ/mol. The morphology of the samples also demonstrated that the particle size is smaller compared with undoped samples. It is believed that in situ forms of NiO, ZnO, and MgO had good catalytic effects on MgH2, significantly reducing the activation energy and onset desorption temperature while improving the sorption kinetics of MgH2.
RESUMEN
Given its significant gravimetric hydrogen capacity advantage, lithium alanate (LiAlH4) is regarded as a suitable material for solid-state hydrogen storage. Nevertheless, its outrageous decomposition temperature and slow sorption kinetics hinder its application as a solid-state hydrogen storage material. This research's objective is to investigate how the addition of titanium silicate (TiSiO4) altered the dehydrogenation behavior of LiAlH4. The LiAlH4-10 wt% TiSiO4 composite dehydrogenation temperatures were lowered to 92 °C (first-step reaction) and 128 °C (second-step reaction). According to dehydrogenation kinetic analysis, the TiSiO4-added LiAlH4 composite was able to liberate more hydrogen (about 6.0 wt%) than the undoped LiAlH4 composite (less than 1.0 wt%) at 90 °C for 2 h. After the addition of TiSiO4, the activation energies for hydrogen to liberate from LiAlH4 were lowered. Based on the Kissinger equation, the activation energies for hydrogen liberation for the two-step dehydrogenation of post-milled LiAlH4 were 103 and 115 kJ/mol, respectively. After milling LiAlH4 with 10 wt% TiSiO4, the activation energies were reduced to 68 and 77 kJ/mol, respectively. Additionally, the scanning electron microscopy images demonstrated that the LiAlH4 particles shrank and barely aggregated when 10 wt% of TiSiO4 was added. According to the X-ray diffraction results, TiSiO4 had a significant effect by lowering the decomposition temperature and increasing the rate of dehydrogenation of LiAlH4 via the new active species of AlTi and Si-containing that formed during the heating process.
RESUMEN
The high hydrogen storage capacity (10.5 wt.%) and release of hydrogen at a moderate temperature make LiAlH4 an appealing material for hydrogen storage. However, LiAlH4 suffers from slow kinetics and irreversibility. Hence, LaCoO3 was selected as an additive to defeat the slow kinetics problems of LiAlH4. For the irreversibility part, it still required high pressure to absorb hydrogen. Thus, this study focused on the reduction of the onset desorption temperature and the quickening of the desorption kinetics of LiAlH4. Here, we report the different weight percentages of LaCoO3 mixed with LiAlH4 using the ball-milling method. Interestingly, the addition of 10 wt.% of LaCoO3 resulted in a decrease in the desorption temperature to 70 °C for the first stage and 156 °C for the second stage. In addition, at 90 °C, LiAlH4 + 10 wt.% LaCoO3 can desorb 3.37 wt.% of H2 in 80 min, which is 10 times faster than the unsubstituted samples. The activation energies values for this composite are greatly reduced to 71 kJ/mol for the first stages and 95 kJ/mol for the second stages compared to milled LiAlH4 (107 kJ/mol and 120 kJ/mol for the first two stages, respectively). The enhancement of hydrogen desorption kinetics of LiAlH4 is attributed to the in situ formation of AlCo and La or La-containing species in the presence of LaCoO3, which resulted in a reduction of the onset desorption temperature and activation energies of LiAlH4.
RESUMEN
One of the ideal energy carriers for the future is hydrogen. It has a high energy density and is a source of clean energy. A crucial step in the development of the hydrogen economy is the safety and affordable storage of a large amount of hydrogen. Thus, owing to its large storage capacity, good reversibility, and low cost, Magnesium hydride (MgH2) was taken into consideration. Unfortunately, MgH2 has a high desorption temperature and slow ab/desorption kinetics. Using the ball milling technique, adding cobalt lanthanum oxide (LaCoO3) to MgH2 improves its hydrogen storage performance. The results show that adding 10 wt.% LaCoO3 relatively lowers the starting hydrogen release, compared with pure MgH2 and milled MgH2. On the other hand, faster ab/desorption after the introduction of 10 wt.% LaCoO3 could be observed when compared with milled MgH2 under the same circumstances. Besides this, the apparent activation energy for MgH2-10 wt.% LaCoO3 was greatly reduced when compared with that of milled MgH2. From the X-ray diffraction analysis, it could be shown that in-situ forms of MgO, CoO, and La2O3, produced from the reactions between MgH2 and LaCoO3, play a vital role in enhancing the properties of hydrogen storage of MgH2.
RESUMEN
Despite the application of lithium aluminium hydride (LiAlH4) being hindered by its sluggish desorption kinetics and unfavourable reversibility, LiAlH4 has received special attention as a promising solid-state hydrogen storage material due to its hydrogen storage capacity (10.5 wt.%). In this work, investigated for the first time was the effect of the nanosized cobalt titanate (CoTiO3) which was synthesised via a solid-state method on the desorption behaviour of LiAlH4. Superior desorption behaviour of LiAlH4 was attained with the presence of a CoTiO3 additive. By means of the addition of 5, 10, 15 and 20 wt.% of CoTiO3, the initial desorption temperature of LiAlH4 for the first stage was reduced to around 115−120 °C and the second desorption stage was reduced to around 144−150 °C, much lower than for undoped LiAlH4. The LiAlH4-CoTiO3 sample also presents outstanding desorption kinetics behaviour, desorbing hydrogen 30−35 times faster than undoped LiAlH4. The LiAlH4-CoTiO3 sample could desorb 3.0−3.5 wt.% H2 in 30 min, while the commercial and milled LiAlH4 desorbs <0.1 wt.% H2. The apparent activation energy of the LiAlH4-CoTiO3 sample based on the Kissinger analysis was decreased to 75.2 and 91.8 kJ/mol for the first and second desorption stage, respectively, lower by 28.0 and 24.9 kJ/mol than undoped LiAlH4. The LiAlH4-CoTiO3 sample presents uniform and smaller particle size distribution compared to undoped LiAlH4, which is irregular in shape with some agglomerations. The experimental results suggest that the CoTiO3 additive promoted notable advancements in the desorption performance of LiAlH4 through the in situ-formed AlTi and amorphous Co or Co-containing active species that were generated during the desorption process.
RESUMEN
Magnesium hydride (MgH2) has received outstanding attention as a safe and efficient material to store hydrogen because of its 7.6 wt.% hydrogen content and excellent reversibility. Nevertheless, the application of MgH2 is obstructed by its unfavorable thermodynamic stability and sluggish sorption kinetic. To overcome these drawbacks, ball milling MgH2 is vital in reducing the particle size that contribute to the reduction of the decomposition temperature. However, the milling process would become inefficient in reducing particle sizes when equilibrium between cold-welding and fracturing is achieved. Therefore, to further ameliorate the performance of MgH2, nanosized cobalt titanate (CoTiO3) has been synthesized using a solid-state method and was introduced to the MgH2 system. The different weight percentages of CoTiO3 were doped to the MgH2 system, and their catalytic function on the performance of MgH2 was scrutinized in this study. The MgH2 + 10 wt.% CoTiO3 composite presents the most outstanding performance, where the initial decomposition temperature of MgH2 can be downshifted to 275 °C. Moreover, the MgH2 + 10 wt.% CoTiO3 absorbed 6.4 wt.% H2 at low temperature (200 °C) in only 10 min and rapidly releases 2.3 wt.% H2 in the first 10 min, demonstrating a 23-times-faster desorption rate than as-milled MgH2 at 300 °C. The desorption activation energy of the 10 wt.% CoTiO3-doped MgH2 sample was dramatically lowered by 30.4 kJ/mol compared to undoped MgH2. The enhanced performance of the MgH2-CoTiO3 system is believed to be due to the in situ formation of MgTiO3, CoMg2, CoTi2, and MgO during the heating process, which offer a notable impact on the behavior of MgH2.
RESUMEN
In this work, the catalytic effects of FeCl3 toward the hydrogen storage properties of the MgH2-Na3AlH6 composite were investigated for the first time. The temperature-programed desorption results indicated that the onset temperature of the hydrogen release of a 10 wt % FeCl3-doped MgH2-Na3AlH6 composite was â¼30 °C lower than that of the undoped MgH2-Na3AlH6 composite. The addition of FeCl3 into the MgH2-Na3AlH6 composite resulted in improved absorption and desorption kinetics performance. The absorption/desorption kinetics measurements at 320 °C (under 33 and 1 atm hydrogen pressure, respectively) indicated that within 10 min, the doped sample absorbed â¼4.0 wt % and desorbed â¼1.5 wt % hydrogen. By comparison, the undoped sample absorbed only â¼2.1 wt % and desorbed only â¼0.6 wt % hydrogen under the same conditions and time. Comparably, the apparent activation energy value of the doped composite is 128 kJ/mol, which is 12 kJ/mol lower than that of the undoped composite (140 kJ/mol). The formation of the new species of MgCl2 and Fe in the doped composite was detected from X-ray diffraction analysis after heating and absorption processes. These two components were believed to play a vital role in reducing the decomposition temperature and kinetics enhancement of the MgH2-Na3AlH6 composite.
RESUMEN
In this study, the modification of the desorption behavior of LiAlH4 by the addition of K2NbF7 was explored for the first time. The addition of K2NbF7 causes a notable improvement in the desorption behavior of LiAlH4. Upon the addition of 10 wt.% of K2NbF7, the desorption temperature of LiAlH4 was significantly lowered. The desorption temperature of the LiAlH4 + 10 wt.% K2NbF7 sample was lowered to 90°C (first-stage reaction) and 149°C (second-stage reaction). Enhancement of the desorption kinetics performance with the LiAlH4 + 10 wt.% K2NbF7 sample was substantiated, with the composite sample being able to desorb hydrogen 30 times faster than did pure LiAlH4. Furthermore, with the presence of 10 wt.% K2NbF7, the calculated activation energy values for the first two desorption stages were significantly reduced to 80 and 86 kJ/mol; 24 and 26 kJ/mol lower than the as-milled LiAlH4. After analysis of the X-ray diffraction result, it is believed that the in situ formation of NbF4, LiF, and K or K-containing phases that appeared during the heating process promoted the amelioration of the desorption behavior of LiAlH4 with the addition of K2NbF7.
RESUMEN
The K2NiF6 catalytic effect on the NaAlH4 dehydrogenation properties was studied in this work. The desorption temperature was studied using temperature-programmed desorption and exhibited a lower onset hydrogen release after doped with different wt % of K2NiF6 (5, 10, 15 and 20 wt %). It was found that the NaAlH4 doped with 5 wt % K2NiF6 showed the optimal value that can reduce the onset desorption temperature of about 160 °C compared to 190 °C for the milled NaAlH4. The NaAlH4 + 5 wt % K2NiF6 sample showed faster desorption kinetics where 1.5 wt % of hydrogen was released in 30 min at 150 °C. In contrast, the milled NaAlH4 only released about 0.2 wt % within the same time and temperature. From the Kissinger analysis, the apparent activation energy was 114.7 kJ/mol for the milled NaAlH4 and 89.9 kJ/mol for the NaAlH4-doped 5 wt % K2NiF6, indicating that the addition of K2NiF6 reduced the activation energy for hydrogen desorption of NaAlH4. It is deduced that the new phases of AlNi, NaF, and KH that were formed in situ during the dehydrogenation process are the key factors for the improvement of dehydrogenation properties of NaAlH4.