RESUMEN
The optical properties of organic semiconductor thin films deposited on nanostructured surfaces are investigated using time-resolved two-photon photoluminescence (PL) microscopy. The surfaces consist of parallel aligned metallic or dielectric nanowires forming well-defined arrays on glass substrates. Keeping the nanowire dimensions constant and varying only their spacing from 40 to 400 nm, we study the range of different types of nanowire-semiconductor interactions. For silver nanowires and spacings below 100 nm, the PL intensity and lifetime of P3HT and MDMO-PPV decrease rapidly due to the short-ranged metal-induced quenching that dominates the PL response with respect to a possible plasmonic enhancement of optical transition rates. In the case of P3HT however, we observe an additional longer-ranged reduction of non-radiative losses for both metallic and dielectric nanowires that is not observed for MDMO-PPV. Excitation polarization dependent measurements indicate that this reduction is due to self-assembly of the P3HT polymer chains along the nanowires. In conclusion, nanostructured surfaces, when fabricated across large areas, could be used to control film morphologies and to improve energy transport and collection efficiencies in P3HT-based solar cells.
RESUMEN
Patterning of organic compounds on a nanometer length scale is of great interest for solar applications: defined control over the donor-acceptor interface will allow design of an optimized nano-morphology promoting exciton separation and reducing charge recombination. Herein we present an imprinting technique using anodized alumina oxide (AAO) hard templates as stamps. We show an exact pattern transfer of the AAO structures into a solution processable hexa-peri-hexabenzocoronene (HBC), a discotic small molecule with acrylate moieties which is polymerized in situ. Film fabrication is realized for a variety of nanowire dimensions on square centimeter areas. The fabrication directly on conductive glass support and control over the formation of a dense barrier layer render this approach appealing for the fabrication of fully organic nanostructured photovoltaic devices.
RESUMEN
The length of titania nanotubes formed by anodization of 0.1 mm thick titanium foil was found to be a strong function of the pH of the electrolyte. The longest nanotubes were formed by using an electrolyte consisting of 1 M Na(2)SO(4) plus 5 wt% NH(4)F with pH 7. At this pH, after 30 min of anodization, 3 microm length nanotubular titania arrays with top diameters of approximately 50 nm and bottom diameters of 100 nm were produced. No acid was added to this electrolyte. The formation of titania nanotubes in neutral pH systems was therefore successful due to the excess NH(4)F in the electrolyte which increases the chemical dissolution process at the metal/oxide interface. Since the pH of the electrolyte at the top part of the nanotubes is kept very high, the dissolution of the nanotubes at the surface is minimal. However, the amount is adequate to remove the initial barrier layer, forming a rather well-defined nanoporous structure. All anodized foils were weakly crystalline and the transformation to anatase phase was achieved by heat treatment at temperatures from 200 to 500 degrees C for 1 h in air. Annealing at temperatures above 500 degrees C induce rutile phase formation and annealing at higher temperatures accelerates the diffusion of Ti(4+) leading to excessive growth and the nanotubular structure diminishes.
RESUMEN
Self-organization of liquid crystalline and crystalline-conjugated materials has been used to create, directly from solution, thin films with structures optimized for use in photodiodes. The discotic liquid crystal hexa-peri-hexabenzocoronene was used in combination with a perylene dye to produce thin films with vertically segregated perylene and hexabenzocoronene, with large interfacial surface area. When incorporated into diode structures, these films show photovoltaic response with external quantum efficiencies of more than 34 percent near 490 nanometers. These efficiencies result from efficient photoinduced charge transfer between the hexabenzocoronene and perylene, as well as from effective transport of charges through vertically segregated perylene and hexabenzocoronene pi systems. This development demonstrates that complex structures can be engineered from novel materials by means of simple solution-processing steps and may enable inexpensive, high-performance, thin-film photovoltaic technology.
RESUMEN
We report a hydrothermal synthesis method for MgO shell coatings directly onto the surface of ZnO nanowire arrays. The entire process can be carried out below 100 °C. The MgO shells are produced by the addition of 10 mM magnesium nitrate with 0.2 M sodium hydroxide in water, resulting in a shell thickness of up to 8 nm, verified by high resolution transmission electron microscopy. The viability of the MgO layer as a functional element of optoelectronic devices was tested on solid-state organic hole-transporter based dye-sensitized solar cells. Incorporation of the MgO shell into the solar cell resulted in substantive efficiency improvements of over 400% in comparison to the pristine ZnO nanowire based photovoltaics, indicating that electrons can efficiently tunnel through the 'insulating' MgO shell.