RESUMEN
Photoelectrochemical (PEC) sensors show great potential for the detection of heavy metal ions because of their low background noise, high sensitivity, and ease of integration. However, the detection limit is relatively high for hexavalent chromium (Cr(VI)) monitoring in addition to the requirement of an external bias. Herein, a CuO film is readily synthesized as the photoactive material via reactive sputtering and thermal annealing in the construction of a PEC sensing photocathode for Cr(VI) monitoring. A different mechanism (i.e., Signal-Weakening PEC sensing) is confirmed by examining the electrochemical impedance and photocurrent response of different CuO film photoelectrodes prepared with the same conditions in contact with various solutions containing concentration-varying Cr(VI) for different durations. The detection of Cr(VI) is successfully achieved with the Signal-Weakening PEC response; a drop of photocathode signal with an increasing Cr(VI) concentration from the steric hindrance effect of the in situ formed Cr(OH)3 precipitates. The photocurrent of the optimized CuO film photocathode linearly declines as the concentration of Cr(VI) increases from 0.08 to 20 µM, with a detection limit down to 2.8 nM (Signal/Noise = 3) and a fitted sensitivity of 4.22 µA·µM-1. Moreover, this proposed sensing route shows operation simplicity, satisfactory selectivity, and reproducibility.
RESUMEN
For the first time, ordered mesoporous ZnO nanoparticles have been synthesized by a template method. The electroplating after chemical plating method was creatively used to form copper film on the surface of the prepared ZnO, and then a CuO film-decorated ordered porous ZnO composite (CuO/ZnO) was obtained by a high-temperature oxidation method. In2O3 was loaded into the prepared CuO film-ZnO by an ultrasonic-assisted method to sensitize the room temperature gas-sensing performance of the prepared CuO/ZnO materials. The doped In2O3 could effectively improve the gas-sensing properties of the prepared materials to nitrogen oxides (NO x ) at room temperature. The 1% In2O3 doped CuO/ZnO sample (1 wt% In2O3-CuO/ZnO) showed the best gas-sensing properties whose response to 100 ppm NO x reached 82%, and the detectable minimum concentration reached 1 ppm at room temperature. The prepared materials had a good selectivity, better response, very low detection limit, and high sensitivity to NO x gas at room temperature, which would have a great development space in the gas sensor field and a great research value.
RESUMEN
In this work we have demonstrated a facile formation of CuO nanostructures on copper substrates by the oxidation of copper foil in ethylene glycol (EG) at 80 °C. On immersing a prepared CuO film into a solution containing 0.1 g Zn(acac)2 in 20 mL EG for 8 h, ZnO flower-like microstructures composed of hierarchical three-dimensional (3D) aggregated nanoparticles and spherical architectures were spontaneously formed at 100 °C. The as-synthesized thin films and 3D microstructures were characterized using XRD, SEM, and EDS techniques. The effects of sodium dodecyl sulphate (SDS), cetyltrimethylammonium bromide (CTAB), and polyethylene glycol (PEG) 6000 as surfactants and stabilizers on the morphology of the CuO and ZnO structures were discussed. Possible growth mechanisms for the controlled organization of primary building units into CuO nanostructures and 3D flower-like ZnO architectures were proposed. The hydrophobic property of the products was characterized by means of water contact angle measurement. After simple surface modification with stearic acid and PDMS, the resulting films showed hydrophobic and even superhydrophobic characteristics due to their special surface energy and nano-microstructure morphology. Importantly, stable superhydrophobicity with a contact angle of 153.5° was successfully observed for CuO-ZnO microflowers after modification with PDMS. The electrochemical impedance measurements proved that the anticorrosion efficiency for the CuO/ZnO/PDMS sample was about 99%.