Poly (Vinyl Alcohol) Hydrogels Boosted with Cross-Linked Chitosan and Silver Nanoparticles for Efficient Adsorption of Congo Red and Crystal Violet Dyes.

In our previous work, three different weight ratios of chitosan/PVA (1:3, 1:1, and 3:1) were blended and then cross-linked with trimellitic anhydride isothiocyanate (TAI) at a concentration depending on their chitosan content, obtaining three hydrogels symbolized by H13, H11, and H31. Pure chitosan was cross-linked with TAI, producing a hydrogel symbolized by H10. Further, three H31-based silver nanoparticles composites (H31/AgNPs1%, H31/AgNPs3%, and H31/AgNPs5%) were also synthesized. They were investigated, for the first time in this study, as adsorbents for Congo Red (CR) and Crystal Violet (CV) dyes. The removal efficiency of CR dye increased with increasing H10 content in the hydrogels, and with increasing AgNP content in the composites, reaching 99.91% for H31/AgNPs5%. For CV dye, the removal efficiency increased with the increase in the PVA content. Furthermore, the removal efficiency of CV dye increased with an increasing AgNP content, reaching 94.7% for H31/AgNPs5%. The adsorption capacity increased with the increase in both the initial dye concentration and temperature, while with an increasing pH it increased in the case of CV dye and decreased in the case of CR dye. The adsorption of CV dye demonstrated that the Freundlich isotherm model is better suited for the experimental results. Moreover, the results were best fitted with pseudo-second-order kinetic model.

Evaluation of Antimicrobial and Anti-Biofilm Formation Activities of Novel Poly(vinyl alcohol) Hydrogels Reinforced with Crosslinked Chitosan and Silver Nano-Particles.

Novel hydrogels were prepared by blending chitosan and poly(vinyl alcohol), PVA, then crosslinking the resulting blends using trimellitic anhydride isothiocyanate at a concentration based on chitosan content in the blends. The weight ratios of chitosan: PVA in the blends were 1:3, 1:1, and 3:1 to produce three hydrogels symbolized as H13, H11, and H31, respectively. For a comparison, H10 was also prepared by crosslinking pure chitosan with trimellitic anhydride isothiocyanate. For further modification, three H31/silver nanocomposites (AgNPs) were synthesized using three different concentrations of silver nitrate to obtain H31/AgNPs1%, H31/AgNPs3% and H31/AgNPs5%. The structures of the prepared samples were emphasized using various analytical techniques. PVA has no inhibition activity against the tested microbes and biofilms. The antimicrobial and anti-biofilm formation activities of the investigated samples was arranged as: H31/AgNPs5% ≥ H31/AgNPs3% > H31/AgNPs1% > H10 > H31 > H11 > H13 > chitosan. H31/AgNPs5% and H31/AgNPs3% were more potent than Vancomycin and Amphotericin B against most of the tested microbes. Interestingly, H31 and H31/AgNPs3% were safe on the normal human cells. Consequently, hydrogels resulting from crosslinked blends of chitosan and PVA loaded with AgNPs in the same structure have significantly reinforced the antimicrobial and inhibition activity against the biofilms of PVA.