RESUMO
Perovskite oxides exhibiting mixed protonic and electronic conductivities have interesting applications in protonic ceramic fuel cells. In this work, we report on a hydrated phase of BaCoO1.80(OH)0.86 synthesized using nebulized spray pyrolysis. Structural analysis based on X-ray and neutron powder diffraction data showed that the compound is isotypic to BaFeO2.33(OH)0.33. The water loss behaviour was studied using simultaneous thermal analysis and high temperature X-ray diffraction, indicating that protons (respectively water) can be stabilized within the compound up to temperatures significantly above 673 K, confirmed by ex situ Fourier transform infrared spectroscopy studies. Impedance spectroscopy was used to determine the conductivity characteristics of BaCoO1.80(OH)0.86, finding and a total electrical conductivity in the order of 10-4 S cm-1 at ambient temperature with an activation energy of 0.28 eV.
RESUMO
Reduction of the operating temperature to an intermediate temperature range between 350 °C and 600 °C is a necessity for Solid Oxide Fuel/Electrolysis Cells (SOFC/SOECs). In this respect the application of proton-conducting oxides has become a broad area of research. Materials that can conduct protons and electrons at the same time, to be used as electrode catalysts on the air electrode, are especially rare. In this article we report on the proton conduction in expitaxially grown BaFeO2.5+δ (BFO) thin films deposited by pulsed laser deposition on Nb:SrTiO3 substrates. By using Electrochemical Impedance Spectroscopy (EIS) measurements under different wet and dry atmospheres, the bulk proton conductivity of BFO (between 200 °C and 300 °C) could be estimated for the first time (3.6 × 10-6 S cm-1 at 300 °C). The influence of oxidizing measurement atmosphere and hydration revealed a strong dependence of the conductivity, most notably at temperatures above 300 °C, which is in good agreement with the hydration behavior of BaFeO2.5 reported previously.