RESUMO
Flexible and soft bioelectronics display conflicting demands on miniaturization, compliance, and reliability. Here, the authors investigate the design and performance of thin encapsulation multilayers against hermeticity and mechanical integrity. Partially cracked organic/inorganic multilayer coatings are demonstrated to display surprisingly year-long hermetic lifetime under demanding mechanical and environmental loading. The thin hermetic encapsulation is grown in a single process chamber as a continuous multilayer with dyads of atomic layer deposited (ALD) Al2 O3 -TiO2 and chemical vapor deposited Parylene C films with strong interlayer adhesion. Upon tensile loading, tortuous diffusion pathways defined along channel cracks in the ALD oxide films and through tough Parylene films efficiently postpone the hermeticity failure of the partially cracked coating. The authors assessed the coating performance against prolonged exposure to biomimetic physiological conditions using coated magnesium films, platinum interdigitated electrodes, and optoelectronic devices prepared on stretchable substrates. Designed extension of the lifetime preventing direct failures reduces from over 5 years yet tolerates the lifetime of 3 years even with the presence of critical damage, while others will directly fail less than two months at 37 °C. This strategy should accelerate progress on thin hermetic packaging for miniaturized and compliant implantable electronics.
Assuntos
Óxido de Alumínio , Próteses e Implantes , Eletrodos , Eletrônica , Reprodutibilidade dos TestesRESUMO
While water vapor transmission rate (WVTR) measurement is standardly used to assess material permeability, a system able to quantify liquid water transmission rate (WTR) measurement is highly desirable for implantable thin film barrier coatings. Indeed, since implantable devices are in contact or immersed in body fluids, liquid WTR was carried out to obtain a more realistic measurement of the barrier performance. Parylene is a well-established polymer which is often the material of choice for biomedical encapsulation applications due to its flexibility, biocompatibility, and attractive barrier properties. Four grades of parylene coatings were tested with a newly developed permeation measurement system based on a quadrupole mass spectrometer (QMS) detection method. Successful measurements of gas and water vapor and the water transmission rates of thin parylene films were performed and validated, comparing the results with a standardized method. In addition, the WTR results allowed for the extraction of an acceleration transmission rate factor from the vapor-to-liquid water measurement mode, which varies from 4 to 4.8 between WVTR and WTR. With a WTR of 72.5 µm g m-2 day-1, parylene C displayed the most effective barrier performance.
RESUMO
Biocompatible polymer films demonstrating excellent thermal stability are highly desirable for high-temperature (>250 °C) applications, especially in the bioelectronic encapsulation domain. Parylene, as an organic thin film, is a well-established polymer material exhibiting excellent barrier properties and is often the material of choice for biomedical applications. This work investigated the thermal impact on the bulk properties of four types of parylene films: parylene N, C, VT4, and AF4. The films, deposited using the standard Gorham process, were analyzed at varying annealing temperatures from room temperature up to 450 °C. Thermal properties were identified by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) methods, while X-ray diffraction (XRD) analysis showed the effect of high-temperature exposure on the structural properties. In addition to thermal and structural analysis, the barrier properties were measured through the helium transmission rate (HTR) and the water vapor transmission rate (WVTR). Fluorinated parylene films were confirmed to be exceptional materials for high-temperature applications. Parylene AF4 film, 25um thick, demonstrated excellent barrier performance after 300 °C exposure, with an HTR and a WVTR of 12.18 × 103 cm3 (STP) m−2 day−1 atm−1 and 6.6 g m−2 day−1, respectively.
RESUMO
Platinum is widely used as the electrode material for implantable devices. Owing to its high biostability and corrosion resistivity, platinum could also be used as the main metallization for tracks in active implants. Towards this goal, in this work we investigate the stability of parylene-coated Pt tracks using passive and active tests. The test samples in this study are Pt-on-SiO2 interdigitated comb structures. During testing all samples were immersed in saline for 150 days; for passive testing, the samples were left unbiased, whilst for active testing, samples were exposed to two different stress signals: a 5 V DC and a 5 Vp 500 pulses per second biphasic signal. All samples were monitored over time using impedance spectroscopy combined with optical inspection. After the first two weeks of immersion, delamination spots were observed on the Pt tracks for both passive and actively tested samples. Despite the delamination spots, the unbiased samples maintained high impedances until the end of the study. For the actively stressed samples, two different failure mechanisms were observed which were signal related. DC stressed samples showed severe parylene cracking mainly due to the electrolysis of the condensed water. Biphasically stressed samples showed gradual Pt dissolution and migration. These results contribute to a better understanding of the failure mechanisms of Pt tracks in active implants and suggest that new testing paradigms may be necessary to fully assess the long-term reliability of these devices.