Cation Co-intercalation in Potassium Copper(II) Hexacyanoferrates.

The cation-insertion solid state electrochemistry of a potassium copper(II) hexacyanoferrate in contact with LiClO4 /DMSO, NaPF6 /DMSO, and KPF6 /DMSO electrolytes has been theoretically and experimentally studied using the voltammetry of immobilized particles methodology. Voltammetric data, combined with SEM/EDS analysis permit to determine a K0.876 CuII 1.328 FeIII 0.049 [FeIII 0.318 FeII 0.682 (CN)6 ] stoichiometry for the synthesized solid. Separation of electronic and ionic contributions to Gibbs energy changes can be made based on cyclic voltammetric and open circuit potential measurements. These parameters can be combined to measure values of the Gibbs energy of cation-independent electron transfer of 7.2±0.4 (K+ ), 7.1±0.5 (Na+ ) kJ mol-1 , in close agreement with the expected independence of this parameter on the electrolyte cation. The reduction Fe(III) centers bound to cyano groups exhibit a cation-dependent, essentially Nernstian character which can be described in terms of Na+ and K+ insertion/deinsertion while in the case of Li+ electrolytes there is significant co-cation diffusion. Chronoamperometric data provide estimates of the diffusion coefficients of Na+ , and K+ ions through the solid around 10-9  cm2 s-1 .

Experimental Global Warming Potential-Weighted Specific Stiffness Comparison among Different Natural and Synthetic Fibers in a Composite Component Manufactured by Tailored Fiber Placement.

This work aims to evaluate experimentally different fibers and resins in a topologically optimized composite component. The selected ones are made of carbon, glass, basalt, flax, hemp, and jute fibers. Tailored Fiber Placement (TFP) was used to manufacture the textile preforms, which were infused with two different epoxy resins: a partly biogenic and a fully petro-based one. The main objective is to evaluate and compare the absolute and specific mechanical performance of synthetic and natural fibers within a component framework as a base for improving assessments of sustainable endless-fiber reinforced composite material. Furthermore, manufacturing aspects regarding the different fibers are also considered in this work. In assessing the efficiency of the fiber-matrix systems, both the specific stiffness and the specific stiffness relative to carbon dioxide equivalents (CO2eq.) as measures for the global warming potential (GWP) are taken into account for comparison. The primary findings indicate that basalt and flax fibers outperform carbon fibers notably in terms of specific stiffness weighted by CO2eq.. Additionally, the selection of epoxy resin significantly influences the assessment of sustainable fiber-plastic composites.