Fatigue failure of osteocyte cellular processes: implications for the repair of bone.

The physical effects of fatigue failure caused by cyclic strain are important and for most materials well understood. However, nothing is known about this mode of failure in living cells. We developed a novel method that allowed us to apply controlled levels of cyclic displacement to networks of osteocytes in bone. We showed that under cyclic loading, fatigue failure takes place in the dendritic processes of osteocytes at cyclic strain levels as low as one tenth of the strain needed for instantaneous rupture. The number of cycles to failure was inversely correlated with the strain level. Further experiments demonstrated that these failures were not artefacts of our methods of sample preparation and testing, and that fatigue failure of cell processes also occurs in vivo. This work is significant as it is the first time it has been possible to conduct fatigue testing on cellular material of any kind. Many types of cells experience repetitive loading which may cause failure or damage requiring repair. It is clinically important to determine how cyclic strain affects cells and how they respond in order to gain a deeper understanding of the physiological processes stimulated in this manner. The more we understand about the natural repair process in bone the more targeted the intervention methods may become if disruption of the repair process occurred. Our results will help to understand how the osteocyte cell network is disrupted in the vicinity of matrix damage, a crucial step in bone remodelling.

The mechanical effects of extracorporeal irradiation on bone.

Extracorporeal irradiation of an excised tumour-bearing segment of bone followed by its re-implantation is a technique used in bone sarcoma surgery for limb salvage when the bone is of reasonable quality. There is no agreement among previous studies about the dose of irradiation to be given: up to 300 Gy have been used. We investigated the influence of extracorporeal irradiation on the elastic and viscoelastic properties of bone. Bone was harvested from mature cattle and subdivided into 13 groups: 12 were exposed to increasing levels of irradiation: one was not and was used as a control. The specimens, once irradiated, underwent mechanical testing in saline at 37°C. The mechanical properties of each group, including Young's modulus, storage modulus and loss modulus, were determined experimentally and compared with the control group. There were insignificant changes in all of these mechanical properties with an increasing level of irradiation. We conclude that the overall mechanical effect of high levels of extracorporeal irradiation (300 Gy) on bone is negligible. Consequently the dose can be maximised to reduce the risk of local tumour recurrence.